In-situ observation of nonmetallic inclusions in steel using confocal scanning laser microscopy: A review

Abstract

The characteristics of nonmetallic inclusions formed during steel production have a significant influence on steel performance. In this paper, studies on inclusions using confocal scanning laser microscopy (CSLM) are reviewed and summarized, particularly the collision of various inclusions, dissolution of inclusions in liquid slag, and reactions between inclusions and steel. Solid inclusions exhibited a high collision tendency, whereas pure liquid inclusions exhibited minimal collisions because of the small attraction force induced by their <90° contact angle with molten steel. The collision of complex inclusions in molten steel was not included in the scope of this study and should be evaluated in future studies. Higher CaO/Al₂O₃ and CaO/SiO₂ ratios in liquid slag promoted the dissolution of Al₂O₃-based inclusions. The formation of solid phases in the slag should be prevented to improve dissolution of inclusions. To accurately simulate the dissolution of inclusions in liquid slag, in-situ observation of the dissolution of inclusions at the steel–slag interface is necessary. Using a combination of CSLM and scanning electron microscopy–energy dispersive spectroscopy, the composition and morphological evolution of the inclusions during their modification by the dissolved elements in steel were observed and analyzed. Although the in-situ observation of MnS and TiN precipitations has been widely studied, the in-situ observation of the evolution of oxide inclusions in steel during solidification and heating processes has rarely been reported. The effects of temperature, heating and cooling rates, and inclusion characteristics on the formation of acicular ferrites (AFs) have been widely studied. At a cooling rate of 3–5 K/s, the order of AF growth rate induced by different inclusions, as reported in literature, is Ti–O < Ti–Ca–Zr–Al–O < Mg–O < Ti–Zr–Al–O < Mn–Ti–Al–O < Ti–Al–O < Zr–Ti–Al–O. Further comprehensive experiments are required to investigate the quantitative relationship between the formation of AFs and inclusions.

Keywords

inclusion / steel / in-situ observation / confocal scanning laser microscopy

References

[1] KangY, ThunmanM, DuSC, MorohoshiT, MizukamiK, MoritaK. Aluminum deoxidation equilibrium of molten iron–aluminum alloy with wide aluminum composition range at 1 873 K. ISIJ Int., 2009, 49101483.

[2] PaekMK, JangJM, KangYB, PakJJ. Aluminum deoxidation equilibria in liquid iron: Part I. experimental. Metall. Mater. Trans. B, 2015, 4641826.

[3] PaekM, PakJ, KangY. Aluminum deoxidation equilibria in liquid iron: Part II. Thermodynamic modeling. Metall. Mater. Trans. B, 2015, 46: 2224.

[4] DuanHJ, RenY, ThomasBG, ZhangLF. Agglomeration of solid inclusions in molten steel. Metall. Mater. Trans. B, 2019, 50136.

[5] DuanHJ, RenY, ZhangLF. Effects of interphase forces on fluid flow in gas-stirred steel ladles using the eulerian–Lagrangian multiphase approach. JOM, 2018, 70102128.

[6] H.J. Duan, Y. Ren, and L.F. Zhang, Modeling of turbulent flow around bubbles in molten steel, Steel Res. Int., 90(2019), No. 6, art. No. 1800576.

[7] RenCY, ZhangLF, ZhangJ, WuSJ, ZhuP, RenY. In situ observation of the dissolution of Al₂O₃ particles in CaO–Al₂O₃–SiO₂ slags. Metall. Mater. Trans. B, 2021, 5253288.

[8] GuYD, RenY, ZhangLF. In-situ observation on dissolution of CaO–SiO₂–Al₂O₃ complex inclusions in refining slag. J. Iron Steel Res. Int., 2025, 32: 376.

[9] ValdezM, ShannonGS, SridharS. The ability of slags to absorb solid oxide inclusions. ISIJ Int., 2006, 463450.

[10] VermaN, PistoriusP, FruehanR, PotterM, LindM, StoryS. Transient Inclusion evolution during modification of alumina inclusions by calcium in liquid steel: Part II. Results and discussion. Metall. Mater. Trans. B, 2011, 42: 720.

[11] VermaN, PistoriusPC, FruehanRJ, PotterM, LindM, StoryS. Transient inclusion evolution during modification of alumina inclusions by calcium in liquid steel: Part I. background, experimental techniques and analysis methods. Metall. Mater. Trans. B, 2011, 424711.

[12] VermaN, PistoriusPC, FruehanRJ, PotterMS, OltmannHG, PretoriusEB. Calcium modification of spinel inclusions in aluminum-killed steel: Reaction steps. Metall. Mater. Trans. B, 2012, 434830.

[13] RenY, ZhangLF, LiSS. Transient evolution of inclusions during calcium modification in linepipe steels. ISIJ Int., 2014, 54122772.

[14] YanPC, HuangSG, PandelaersL, Van DyckJ, GuoMX, BlanpainB. Effect of the CaO–Al₂O₃-based top slag on the cleanliness of stainless steel during secondary metallurgy. Metall. Mater. Trans. B, 2013, 4451105.

[15] RenY, ZhangLF, FangW, ShaoSJ, YangJ, MaoWD. Effect of slag composition on inclusions in Si-deoxidized 18Cr–8Ni stainless steels. Metall. Mater. Trans. B, 2016, 4721024.

[16] RenY, ZhangLF. Thermodynamic model for prediction of slag–steel–inclusion reactions of 304 stainless steels. ISIJ Int., 2017, 57168.

[17] ColettiB, GommersB, VercruyssenC, BlanpainB, WollantsP, HaersF. Reoxidation during ladle treatment. Ironmaking Steelmaking, 2003, 302101.

[18] GotoH, MiyazawaKI. Reoxidation behavior of molten steel in non-killed and Al-killed steels. ISIJ Int., 1998, 383256.

[19] HiguchiY, TagoY, FukagawaS, KanaiT, MutohA. Reoxidation behavior in Al killed steel during casting. Tetsuto-Hagane, 1999, 855375.

[20] WuMH, RenCY, RenY, ZhangLF. In situ observation of the agglomeration of MgO–Al₂O₃ inclusions on the surface of a molten GCr15-bearing steel. Metall. Mater. Trans. B, 2023, 5431159.

[21] YuSF, LeiY, XieML, HuangAG, LiZY. Nucleation mechanisms of intragranular ferrite (IGF). J. Iron Steel Res., 2005, 17147

[22] AraiY, EmiT, FredrikssonH, ShibataH. In-situ observed dynamics of peritectic solidification and δ/γ transformation of Fe–3 to 5 At. pct Ni alloys. Metall. Mater. Trans. A, 2005, 36113065.

[23] ShibataH, AraiY, SuzukiM, EmiT. Kinetics of peritectic reaction and transformation in Fe–C alloys. Metall. Mater. Trans. B, 2000, 315981.

[24] YukiN, ShibataH, EmiT. Solubility of MnS in Fe-Ni alloys as determined by in situ observation of precipitation of MnS with a confocal scanning laser microscope. ISIJ Int., 1998, 384317.

[25] MisraP, SridharS, CrambAW. In-situ observation of TiN precipitates at stainless steel/CaO–Al₂O₃–MgO–SiO₂ interface. Metall. Mater. Trans. B, 2001, 325963.

[26] MinskyM. Memoir on inventing the confocal scanning microscope. Scanning, 1988, 104128.

[27] ChikamaH, ShibataH, EmiT, SuzukiM. “In-situ” real time observation of planar to cellular and cellular to dendritic transition of crystals growing in Fe–C alloy melts. Mater. Trans. JIM, 1996, 374620.

[28] YinHB, ShibataH, EmiT, SuzukiM. “In-situ” observation of collision, agglomeration and cluster formation of alumina inclusion particles on steel melts. ISIJ Int., 1997, 3710936.

[29] ShibataH, YinH, EmiT. The capillary effect promoting collision and agglomeration of inclusion particles at the inert gas–steel interface. Philos. Trans. R. Soc. Lond. Ser. A: Math. Phys. Eng. Sci., 1998, 3561739957.

[30] ShibataH, YinHB, YoshinagaS, EmiT, SuzukiM. In-situ observation of engulfment and pushing of nonmetallic inclusions in steel melt by advancing melt/solid interface. ISIJ Int., 1998, 382149.

[31] HanamuraT, ShibataH, WasedaY, et al. . In-situ observation of intragranular ferrite nucleation at oxide particles. ISIJ Int., 1999, 39111188.

[32] SridharS, CrambAW. Kinetics of Al₂O₃ dissolution in CaO–MgO–SiO₂–Al₂O₃ slags: in situ observations and analysis. Metall. Mater. Trans. B, 2000, 312406.

[33] KhuranaB, SpoonerS, RaoMBV, RoyGG, SrirangamP. In situ observation of calcium oxide treatment of inclusions in molten steel by confocal microscopy. Metall. Mater. Trans. B, 2017, 4831409.

[34] YinHB, ShibataH, EmiT, SuzukiM. Characteristics of agglomeration of various inclusion particles on molten steel surface. ISIJ Int., 1997, 3710946.

[35] LiangGF, WangCQ, FangY. In situ observation on movement and agglomeration of inclusion in solidliquid mush zone during melting of stainless steel aisi304. Acta Metall. Sin., 2006, 427708

[36] KimuraS, NakajimaK, MizoguchiS. Behavior of alumina-magnesia complex inclusions and magnesia inclusions on the surface of molten low-carbon steels. Metall. Mater. Trans. B, 2001, 32179.

[37] KimuraS, NabeshimaY, NakajimaK, MizoguchiS. Behavior of nonmetallic inclusions in front of the solid-liquid interface in low-carbon steels. Metall. Mater. Trans. B, 2000, 3151013.

[38] NakajimaK, MizoguchiS. Capillary interaction between inclusion particles on the 16Cr stainless steel melt surface. Metall. Mater. Trans. B, 2001, 324629.

[39] WikströmJ, NakajimaK, ShibataH, TillianderA, JönssonP. In situ studies of the agglomeration phenomena for calcium–alumina inclusions at liquid steel–liquid slag interface and in the slag. Mater. Sci. Eng. A, 2008, 4951–2316.

[40] WikströmJ, NakajimaK, ShibataH, TillianderA, JönssonP. In situ studies of agglomeration between Al₂O₃–CaO inclusions at metal/gas, metal/slag interfaces and in slag. Ironmaking Steelmaking, 2008, 358589.

[41] LeeSH, TseC, YiKW, et al. . Separation and dissolution of Al₂O₃ inclusions at slag/metal interfaces. J. Non Cryst. Solids, 2001, 282141.

[42] ColettiB, BlanpainB, VantiltS, SridharS. Observation of calcium aluminate inclusions at interfaces between Catreated, Al-killed steels and slags. Metall. Mater. Trans. B, 2003, 345533.

[43] AppelbergJ, NakajimaK, ShibataH, TillianderA, JönssonP. In situ studies of misch-metal particle behavior on a molten stainless steel surface. Mater. Sci. Eng. A, 2008, 4951–2330.

[44] WangYG, LiuCJ. Agglomeration characteristics of various inclusions in Al-killed molten steel containing rare earth element. Metall. Mater. Trans. B, 2020, 5162585.

[45] WenB, SongB. In situ observation of the evolution of intragranular acicular ferrite at Ce-containing inclusions in 16Mn steel. Steel Res. Int., 2012, 835487.

[46] WangYG, LiuCJ. Agglomeration characteristics of various oxide inclusions in molten steel containing rare earth element under different deoxidation conditions. ISIJ Int., 2021, 6151396.

[47] HasegawaH, NakajimaK, MizoguchiS. “In-situ” observation of phase transformation and MnS precipitation in Fe–Si alloys. Tetsu-to-Hagane, 2001, 876433.

[48] YanPC, GuoMX, BlanpainB. In situ observation of the formation and interaction behavior of the oxide/oxysulfide inclusions on a liquid iron surface. Metall. Mater. Trans. B, 2014, 453903.

[49] AnezirisCG, SchroederC, EmmelM, SchmidtG, HellerHP, BerekH. In situ observation of collision between exogenous and endogenous inclusions on steel melts for active steel filtration. Metall. Mater. Trans. B, 2013, 444954.

[50] MuWZ, DoganN, ColeyKS. In situ observations of agglomeration of non-metallic inclusions at steel/Ar and steel/slag interfaces by high-temperature confocal laser scanning microscope: A review. JOM, 2018, 7071199.

[51] VantiltS, ColettiB, BlanpainB, FransaerJ, WollantsP, SridharS. Observation of inclusions in manganese-silicon killed steels at steel–gas and steel–slag interfaces. ISIJ Int., 2004, 4411.

[52] MuWZ, DoganN, ColeyKS. Agglomeration of non-metallic inclusions at steel/Ar interface: In situ observation experiments and model validation. Metall. Mater. Trans. B, 2017, 4852379.

[53] MuWZ, DoganN, ColeyKS. Agglomeration of non-metallic inclusions at the steel/Ar interface: Model application. Metall. Mater. Trans. B, 2017, 4842092.

[54] MuWZ, DoganN, ColeyKS. In situ observation of deformation behavior of chain aggregate inclusions: A case study for Al₂O₃ at a liquid steel/argon interface. J. Mater. Sci., 2018, 531813203.

[55] ChenR, ChenZP, XuYT, ZhouCD, ShuD. In-situ observation of behaviors of inclusions in bearing steel. J. Iron. Steel Res. Int., 2015, 271248.

[56] JiangM, WangXH, PakJJ, YuanP. In situ observation on behaviors of CaO–MgO–Al₂O₃–SiO₂ complex inclusions at solid–liquid interface of low-oxygen special steel. Metall. Mater. Trans. B, 2014, 4551656.

[57] KangY, SahebkarB, SchellerPR, MoritaK, DuSC. Observation on physical growth of nonmetallic inclusion in liquid steel during ladle treatment. Metall. Mater. Trans. B, 2011, 423522.

[58] TianQR, WangGC, ShangDL, et al. . In situ observation of the precipitation, aggregation, and dissolution behaviors of TiN inclusion on the surface of liquid GCr15 bearing steel. Metall. Mater. Trans. B, 2018, 4963137.

[59] MuWZ, XuanCJ. Agglomeration mechanism of complex Ti–Al oxides in liquid ferrous alloys considering high-temperature interfacial phenomenon. Metall. Mater. Trans. B, 2019, 5062694.

[60] WuMH, RenY, ZhangLF. In-situ observation of collision and agglomeration of La₂O₃–La₂S₃ inclusions on surface of molten 304 stainless steels. Metall. Mater. Trans. B, 2024, 5542324.

[61] MuHY, ZhangTS, YangL, XavierRR, FruehanRJ, WeblerBA. In situ observation of MgO inclusions in liquid iron-aluminum alloys. Metall. Mater. Trans. B, 2016, 4763375.

[62] MisraP, ChevrierV, SridharS, CrambAW. In situ observations of inclusions at the (Mn, Si)-killed steel/CaO–Al₂O₃ interface. Metall. Mater. Trans. B, 2000, 3151135.

[63] S.K. Michelic, U. Dieguez Salgado, and C. Bernhard, In-situ observation of the behaviour of non-metallic inclusions at different interfaces in the system steel–slag–refractory, IOP Conf. Ser. Mater. Sci. Eng., 143(2016), art. No. 012010.

[64] YueQ, ChenHH, YaoCH, LuD, ZhangJF, HuangF. Review of collision and growth on non-metallic inclusion in steel. J. Iron Steel Res., 2012, 2491

[65] ChengLM, ZhangLF, ShenP. Fundamentals of interfacial wettability in ironmaking and steelmaking. Chin. J. Eng., 2018, 40121434

[66] ValdezM, PrapakornK, CrambAW, SridharS. Dissolution of alumina particles in CaO–Al₂O₃–SiO₂–MgO slags. Ironmaking Steelmaking, 2002, 29147.

[67] YiKW, TseC, ParkJH, ValdezM, CrambAW, SridharS. Determination of dissolution time of Al₂O₃ and MgO inclusions in synthetic Al₂O₃–CaO–MgO slags. Scand. J. Metall., 2003, 324177.

[68] MonaghanBJ, ChenL, SorbeJ. Comparative study of oxide inclusion dissolution in CaO–SiO₂–Al₂O₃ slag. Ironmaking Steelmaking, 2005, 323258.

[69] ParkJH, JungIH, LeeHG. Dissolution behavior of Al₂O₃ and MgO inclusions in the CaO–Al₂O₃–SiO₂ slags: Formation of ring-like structure of MgAl₂O₄ and Ca₂SiO₄ around MgO inclusions. ISIJ Int., 2006, 46111626.

[70] LiuJ, GuoM, JonesPT, VerhaegheF, BlanpainB, WollantsP. In situ observation of the direct and indirect dissolution of MgO particles in CaO–Al₂O₃–SiO₂-based slags. J. Eur. Ceram. Soc., 2007, 2741961.

[71] LiuJH, VerhaegheF, GuoMX, BlanpainB, WollantsP. In situ observation of the dissolution of spherical alumina particles in CaO–Al₂O₃–SiO₂ melts. J. Am. Ceram. Soc., 2007, 90123818.

[72] FeichtingerS, MichelicSK, KangYB, BernhardC. In situ observation of the dissolution of SiO₂ particles in CaO–Al₂O₃–SiO₂ slags and mathematical analysis of its dissolution pattern. J. Am. Ceram. Soc., 2014, 971316.

[73] MichelicS, GoriuppJ, FeichtingerS, KangYB, BernhardC, SchenkJ. Study on oxide inclusion dissolution in secondary steelmaking slags using high temperature confocal scanning laser microscopy. Steel Res. Int., 2016, 87157.

[74] TianTL, ZhangYZ, ZhangHH, ZhangKX, LiJ, WangH. Dissolution behavior of SiO₂ in the molten blast furnace slags. Int. J. Appl. Ceram. Technol., 2019, 1631078.

[75] GuoX, SunZHI, Van DyckJ, GuoM, BlanpainB. In Situ Observation on lime dissolution in molten metallurgical slags–kinetic aspects. Ind. Eng. Chem. Res., 2014, 53156325.

[76] MonaghanBJ, ChenL. Dissolution behavior of alumina micro-particles in CaO–SiO₂–Al₂O₃ liquid oxide. J. Non Cryst. Solids, 2004, 3471–3254.

[77] MonaghanBJ, ChenL. Effect of changing slag composition on spinel inclusion dissolution. Ironmaking Steelmaking, 2006, 334323.

[78] MiaoKY, HaasA, SharmaM, MuWZ, DoganN. In situ observation of calcium aluminate inclusions dissolution into steelmaking slag. Metall. Mater. Trans. B, 2018, 4941612.

[79] SharmaM, MuWZ, DoganN. In situ observation of dissolution of oxide inclusions in steelmaking slags. JOM, 2018, 7071220.

[80] RenY, ZhuP, RenCY, LiuN, ZhangLF. Dissolution of SiO₂ inclusions in CaO–SiO₂-based slags in situ observed using high-temperature confocal scanning laser microscopy. Metall. Mater. Trans. B, 2022, 532682.

[81] FoxAB, ValdezME, GisbyJ, AtwoodRC, LeePD, SridharS. Dissolution of ZrO₂, Al₂O₃, MgO and MgAl₂O₄ particles in a B₂O₃ containing commercial fluoride-free mould slag. ISIJ Int., 2004, 445836.

[82] MonaghanBJ, NightingaleSA, ChenL, BrooksG. The dissolution behavior of selected oxides in CaO–SiO₂–Al₂O₃ slags. Conf. Molten Slag Fluxes and Salts-The South African Institute of Mining and Metallurgy, 2004585

[83] F. Verhaeghe, J. Liu, M. Guo, S. Arnout, B. Blanpain, and P. Wollants, Dissolution and diffusion behavior of Al₂O₃ in a CaO–Al₂O₃–SiO₂ liquid: An experimental-numerical approach, Appl. Phys. Lett., 91(2007), No. 12, art. No. 124104.

[84] ParkJH, ParkJG, MinDJ, LeeYE, KangYB. In situ observation of the dissolution phenomena of SiC particle in CaO–SiO₂–MnO slag. J. Eur. Ceram. Soc., 2010, 30153181.

[85] SunZHI, GuoXL, Van DyckJ, GuoMX, BlanpainB. Phase evolution and nature of oxide dissolution in metallurgical slags. AlChE. J., 2013, 5982907.

[86] LeeYM, YangJK, MinDJ, ParkJH. Mechanism of MgO dissolution in MgF₂–CaF₂–MF (M=Li or Na) melts: Kinetic analysis via in situ high temperature confocal scanning laser microscopy (HT-CSLM). Ceram. Int., 2019, 451620251.

[87] SharmaM, DoganN. Dissolution behavior of aluminum titanate inclusions in steelmaking slags. Metall. Mater. Trans. B, 2020, 512570.

[88] ParkYJ, ChoYM, ChaWY, KangYB. Dissolution kinetics of alumina in molten CaO–Al₂O₃–FetO–MgO–SiO₂ oxide representing the RH slag in steelmaking process. J. Am. Ceram. Soc., 2020, 10332210.

[89] RenCY, HuangCD, ZhangLF, RenY. In situ observation of the dissolution kinetics of Al₂O₃ particles in CaO–Al₂O₃–SiO₂ slags using laser confocal scanning microscopy. Int. J. Miner. Metall. Mater., 2023, 302345.

[90] GouL, LiuH, RenY, ZhangLF. Concept of inclusion capacity of slag and its application on the dissolution of Al₂O₃, ZrO₂ and SiO₂ inclusions in CaO–Al₂O₃–SiO₂ slag. Metall. Mater. Trans. B, 2023, 5431314.

[91] ZhangLF, RenY. Concept of inclusion capacity of slag and its application. Iron Steel, 2023, 58247

[92] WangYG, LiuCJ. In situ observation of transient evolution of inclusions by Ca treatment in molten steel. Metall. Mater. Trans. B, 2022, 5352768.

[93] ChenGJ, RenY, WuMH, WangWJ, ZhangLF. In-situ observation of the modification behavior of alumina inclusions in a calcium-treated steel. ISIJ Int., 2024, 6481263.

[94] WangY, SridharS, ValdezM. Formation of CaS on Al₂O₃–CaO inclusions during solidification of steels. Metall. Mater. Trans. B, 2002, 334625.

[95] ValdezME, WangY, SridharS. MnS precipitation behavior in re-sulfurized steels with intermediate levels of sulfur. Steel Res. Int., 2005, 764306.

[96] NakamaK, HarunaY, NakanoJ, SridharS. The effect of alloy solidification path on sulfide formation in Fe–Cr–Ni alloys. ISIJ Int., 2009, 493355.

[97] LuoYZ, ZhangJM, LiuZM, XiaoC. In situ observation and thermodynamic calculation of MnS in 49MnVS3 non-quenched and tempered steel. Acta Metall. Sin. Engl. Lett., 2011, 244326

[98] HuDL, LiuH, XieJB, ChengJ, LiJ, FuJX. Analysis of precipitation behavior of MnS in sulfur-bearing steel system with finite-difference segregation model. J. Iron Steel Res. Int., 2018, 258803.

[99] Q.R. Tian, G.C. Wang, X.H. Yuan, Q. Wang, and S. Sridhar, Complex precipitates of TiN–MC_x in GCr15 bearing steel, Metals, 9(2019), No. 6, art. No. 641.

[100] Y. Tanaka, F. Pahlevani, S.C. Moon, R. Dippenaar, and V. Sahajwalla, In situ characterisation of MnS precipitation in high carbon steel, Sci. Rep., 9(2019), No. 1, art. No. 10096.

[101] ZengJ, ZhuCY, WangWL, LiX. In situ observation of the MnS precipitation behavior in high-sulfur microalloyed steel under different cooling rates. Metall. Mater. Trans. B, 2020, 5162522.

[102] P. Shen, H. Zhang, X.Y. Xu, Q.K. Yang, and J.X. Fu, Study on the high-temperature evolution and formation mechanism of inclusions in Te-treated resulfurized special steel, Steel Res. Int., 92(2021), No. 11, art. No. 2100235.

[103] J.H. Chu, L.Q. Zhang, J. Yang, Y.P. Bao, N. Ali, and C.J. Zhang, Characterization of precipitation, evolution, and growth of MnS inclusions in medium/high manganese steel during solidification process, Mater. Charact., 194(2022), art. No. 112367.

[104] CaoL, WangGC, XiaoYY, YangRG. Effect of Mg addition on TiN inclusions in GCr15 bearing steel. J. Iron Steel Res. Int., 2022, 296925.

[105] LiuH, LiWF, RenCY, ZhangLF, RenY. Inclusion evolution in Al-killed Ca-treated steels at heat treatment temperature in situ observed using confocal scanning laser microscope. Metall. Mater. Trans. B, 2022, 5331323.

[106] X.L. Zhu, J. Yang, S. Wang, et al., The investigation of precipitation behavior of titanium compounds for high titanium steel based on in situ observation, PLoS One, 18(2023), No. 4, art. No. e0275049.

[107] CaoL, WangGC, XiaoYY, ZhaoZ, LiJG. In situ observation of the evolution behavior of MnS inclusions in high-Al medium-Mn steel. Metall. Mater. Trans. B, 2024, 552660.

[108] ShaoXJ, WangXH, JiangM, WangWJ, HuangFX. Effect of heat treatment conditions on shape control of large-sized elongated MnS inclusions in resulfurized free-cutting steels. ISIJ Int., 2011, 51121995.

[109] ShaoXJ, WangXH, JiangM, WangWJ, HuangFX, JiYQ. In situ observation of MnS inclusion behavior in resul-furized free-cutting steel during heating. Acta Metall. Sin., 2011, 4791210

[110] WangQY, ZouXD, MatsuuraH, WangC. Evolution of inclusions during the 1473 K (1200°C) heating process of EH36 shipbuilding steel. Metall. Mater. Trans. B, 2018, 49118.

[111] WangQY, ZouXD, MatsuuraH, WangC. Evolution of inclusions during 1473 K heating process in EH36 shipbuilding steel with Mg addition. JOM, 2018, 704521.

[112] WangHP, BaiB, JiangSL, SunLF, WangY. An in situ study of the formation of rare earth inclusions in arsenic high carbon steels. ISIJ Int., 2019, 5971259.

[113] P.S. Song, Y.Q. Li, T.H. Zhu, and L.F. Zhang, In situ observation on the heterogeneous nucleation of MnS in heavy rail steels with varied aluminum content, Steel Res. Int., 94(2023), No. 5, art. No. 2200684.

[114] HasegawaH, NakajimaK, MizoguchiS. Effects of MnS on the heterogeneous nucleation of Cu precipitates in Fe–10 and −5mass% Cu alloys. ISIJ Int., 2003, 4371021.

[115] YamamotoKI, ShibataH, NakajimaK, MizoguchiS. Precipitation behavior of Cu and MnS at high temperature in Fe–10mass%Cu alloys. Tetsu-to-Hagane, 2004, 9010781.

[116] YinHB, EmiT. Marangoni flow at the gas/melt interface of steel. Metall. Mater. Trans. B, 2003, 345483.

[117] ChenSY, YueXD, JinGC, LiQC, ChangGW. Behavior of inclusions in process of solid growth during solidification of Fe–0.15C–0.8Mn steel. J. Iron Steel Res. Int., 2012, 19517.

[118] C.L. Yan, F.M. Wang, W.L. Mo, P.C. Xiao, and Q.J. Zhang, Migration behavior of inclusions at the solidification front in oxide metallurgy, Materials, 16(2023), No. 12, art. No. 4486.

[119] ShaoXJ, WangXH, JiCX, LiHB, CuiY, ZhuGS. Morphology, size and distribution of MnS inclusions in non-quenched and tempered steel during heat treatment. Int. J. Miner. Metall. Mater., 2015, 225483.

[120] J. Yang, K. Zhu and G. wang, Progress in the technological development of oxide metallurgy for manufacturing steel plates with excellent HAZ toughness, Baosteel Tech. Res., 2008, No. 2, p. 43.

[121] KitaniY, IkedaR, YasudaK, OiK, IchimiyaK. Improvement of HAZ toughness for high heat input welding by using boron diffusion from weld metal. Weld. World, 2007, 51131.

[122] DuanH, ShanYY, YangK, ShiXB, YanW, RenY. Experimental on process, microstructure and mechanical properties of X80 high strength pipeline steel for low temperature. Iron Steel, 2020, 552103

[123] ZouZY, HanST, LiYX, WangC. Analysis of internal mechanism of impact toughness of CGHAZ for high heat input welding steels. China Metall., 2019, 29118

[124] WangBX, ZhuFX, WangC, LouHN, WangZD, WangGD. Application of oxide metallurgy in high heat input welding steels. Iron Steel, 2019, 54912

[125] WangBX, WuZZ, LouHN, WangC, WangZD, WangGD. Effect of oxide metallurgy on microstructure and properties of HAZ in EH36 steel. J. Iron Steel Res., 2019, 312239

[126] MuWZ, HedströmP, ShibataH, JönssonPG, NakajimaK. High-temperature confocal laser scanning microscopy studies of ferrite formation in inclusion-engineered steels: A review. JOM, 2018, 70102283.

[127] TerasakiH, YamadaT, KomizoYI. In-situ observation of nucleation and growth of acicular ferrite in weld metal. Tetsu-to-Hagane, 2007, 93127.

[128] ZhangD, TerasakiH, KomizoYI. In situ observation of the formation of intragranular acicular ferrite at non-metallic inclusions in C–Mn steel. Acta Mater., 2010, 5841369.

[129] HuZY, YangCW, JiangM, YangGW, WangWJ, WangXH. In situ observation of intragranular acicular ferrite nucleated on complex titanium containing inclusions in titanium deoxidized steel. Acta Metall. Sin., 2011, 478971

[130] WanXL, WuKM, HuangG, WeiR. In situ observations of the formation of fine-grained mixed microstructures of acicular ferrite and bainite in the simulated coarse-grained heated-affected zone. Steel Res. Int., 2014, 852243.

[131] WanXL, WeiR, ChengL, EnomotoM, AdachiY. Lengthening kinetics of ferrite plates in high-strength low-carbon low alloy steel. J. Mater. Sci., 2013, 48124345.

[132] MuWZ, JönssonPG, NakajimaK. Effect of sulfur content on inclusion and microstructure characteristics in steels with Ti₂O₃ and TiO₂ additions. ISIJ Int., 2014, 54122907.

[133] JiangM, WangXH, HuZY, WangKP, YangCW, LiSR. Microstructure refinement and mechanical properties improvement by developing IAF on inclusions in Ti–Al complex deoxidized HSLA steel. Mater. Charact., 2015, 108: 58.

[134] WanXL, WuKM, ChengL, WeiR. In-situ observations of acicular ferrite growth behavior in the simulated coarse-grained heat-affected zone of high-strength low-alloy steels. ISIJ Int., 2015, 553679.

[135] WuZH, ZhengW, LiGQ, MatsuuraH, TsukihashiF. Effect of inclusions’ behavior on the microstructure in Al–Ti deoxidized and magnesium-treated steel with different aluminum contents. Metall. Mater. Trans. B, 2015, 4631226.

[136] MuWZ, ShibataH, HedströmP, JönssonPG, NakajimaK. Ferrite formation dynamics and microstructure due to inclusion engineering in low-alloy steels by Ti₂O₃ and TiN addition. Metall. Mater. Trans. B, 2016, 4742133.

[137] LinCK, PanYC, HwangWS, et al. . In situ observation of growth behaviour of acicular ferrite in low-carbon steel containing 13 ppm magnesium. Ironmaking Steelmaking, 2019, 462176.

[138] LoderD, MichelicSK. Systematic investigation of acicular ferrite formation on laboratory scale. Mater. Sci. Technol., 2017, 332162.

[139] YangYK, ZhanDP, LeiH, et al. . In situ observation of acicular ferrite nucleation and growth at different cooling rate in Ti–Zr deoxidized steel. Metall. Mater. Trans. B, 2019, 5062536.

[140] X. Wang, C. Wang, J. Kang, G. Yuan, R.D.K. Misra, and G.D. Wang, An in situ microscopy study on nucleation and growth of acicular ferrite in Ti–Ca–Zr deoxidized low-carbon steel, Mater. Charact., 165(2020), art. No. 110381.

[141] WangTT, YangSF, LiJS, GuoH, ChenZY. Effect of in situ observation of cooling rates on acicular ferrite nucleation. High Temp. Mater. Process., 2022, 411181.

[142] LiuDK, YangJ, ZhangYH. In-situ observation of bainite transformation in CGHAZ of 420 MPa grade offshore engineering steel with different Mo contents. ISIJ Int., 2022, 624714.

[143] YaoH, RenQ, YangW, ZhangLF. In situ observation and prediction of the transformation of acicular ferrites in Ti-containing HLSA steel. Metall. Mater. Trans. B, 2022, 5331827.

[144] XieX, ZhongM, ZhaoPF, YuH, WangC. In situ observation of phase transformations in the weld metal of EH420 shipbuilding steel subjected to varied heat inputs. Metall. Mater. Trans. A, 2023, 5472532.

[145] LiYS, DongYW, JiangZH, TangQF, DuSY, HouZW. Influence of rare earth Ce on hot deformation behavior of as-cast Mn₁₈Cr18N high nitrogen austenitic stainless steel. Int. J. Miner. Metall. Mater., 2023, 302324.

[146] ShiWN, YangSF, LiJS. Effect of nonmetallic inclusions on localized corrosion of spring steel. Int. J. Miner. Metall. Mater., 2021, 283390.

[147] YangQK, ShenP, ZhangD, WuYX, FuJX. Analysis on composition and inclusions of ballpoint pen tip steel. Int. J. Miner. Metall. Mater., 2018, 254420.

[148] LinL, LiBS, ZhuGM, KangYL, LiuRD. Effects of Nb on the microstructure and mechanical properties of 38MnB5 steel. Int. J. Miner. Metall. Mater., 2018, 25101181.

[149] LiHB, JiangZH, FengH, ZhuHC, SunBH, LiZ. Corrosion behavior of ferritic stainless steel with 15wt% chromium for the automobile exhaust system. Int. J. Miner. Metall. Mater., 2013, 209850.

[150] ZengYP, FanHM, XieXS. Effects of the shape and size of rectangular inclusions on the fatigue cracking behavior of ultra-high strength steels. Int. J. Miner. Metall. Mater., 2013, 204360.

[151] GuC, LiuWQ, LianJH, BaoYP. In-depth analysis of the fatigue mechanism induced by inclusions for high-strength bearing steels. Int. J. Miner. Metall. Mater., 2021, 285826.

[152] ZhouMW, YuH. Effects of precipitates and inclusions on the fracture toughness of hot rolling X70 pipeline steel plates. Int. J. Miner. Metall. Mater., 2012, 199805.

RIGHTS & PERMISSIONS

University of Science and Technology Beijing