Optimizing microstructure of medium Ni-bearing steel to ensure high resistance to corrosion and corrosion-assisted mechanical degradation

Abstract

Through quenching and tempering (QT) and quenching and partitioning (Q&P) processes, this study aimed to investigate the effects of microstructural modifications on the corrosion behavior and corrosion-assisted mechanical degradation of medium Ni-bearing steel. The primary objective was the identification of strategies for the enhancement of the long-term lifespan and reliability of these alloys in neutral aqueous environments. Various electrochemical evaluations and microstructural characterizations were conducted to elucidate the relationship between heat treatment processes and corrosion behavior. The findings reveal that the conventional Q&P process formed partitioned austenite with a coarse size within the martensitic matrix, which led to an uneven distribution of Ni and high kernel average misorientation and resulted in an increased susceptibility to corrosion and corrosion-induced mechanical degradation. In addition, the corroded QT sample displayed preferential attacks around cementite clusters due to selective dissolution. By contrast, a slightly higher partitioning temperature, just above the martensite transformation start temperature, provided finely distributed austenite within bainite in the microstructure, which exhibited lower corrosion kinetics and reduced susceptibility to mechanical degradation in the corrosive environment. This study highlights the potential of microstructural optimization through the Q&P process with a high partitioning temperature as an effective technical strategy for achieving the superior durability and reliability of medium Ni-bearing steel alloys in neutral aqueous environments.

Keywords

Ni-bearing steel / quenching / partitioning / corrosion / mechanical degradation

References

[1] FultzB, KimJI, KimYH, MorrisJW. The chemical composition of precipitated austenite in 9Ni steel. Metall. Trans. A, 1986, 176967.

[2] Y.K. Kim, B.T. Oh, and J.H. Kim, Effects of crack tip constraint on the fracture toughness assessment of 9% Ni steel for cryogenic application in liquefied natural gas storage tanks, Materials, 13(2020), No. 22, art. No. 5250.

[3] TanakaM, MatsuoK, YoshimuraN, et al.. Effects of Ni and Mn on brittle-to-ductile transition in ultralow-carbon steels. Mater. Sci. Eng. A, 2017, 682370.

[4] F.Y. Niu, J.S. He, D.H. Liu, X.R. Zuo, and M.H. Cai, Effect of bending process on microstructure, mechanical properties and crack formation of 5% Ni steel, Metals, 12(2022), No. 7, art. No. 1188.

[5] M. Arribas, T. Gutiérrez, E.D. Molino, et al., Austenite reverse transformation in a Q&P route of Mn and Ni added steels, Metals, 10(2020), No. 7, art. No. 862.

[6] SaitohN, MuraokaH, YamabaR, SaekiO. Development of heavy 9% nickel steel plates with superior low-temperature toughness for LNG storage tanks. Nippon Steel Technical Report, 1993, 589

[7] ShinHS, LeeHM, KimMS. Impact tensile behaviors of 9% nickel steel at low temperature. Int. J. Impact Eng., 2000, 246–7571.

[8] WuSJ, SunGJ, MaQS, ShenQY, XuL. Influence of QLT treatment on microstructure and mechanical properties of a high nickel steel. J. Mater. Process. Technol., 2013, 2131120.

[9] J.S. Park, H.G. Seong, J. Hwang, and S.J. Kim, Adverse effects of Ni on the mechanical and corrosion-induced hydrogen embrittlement properties of ultra-strong giga steel used for automotive applications, Mater. Des., 193(2020), art. No. 108877.

[10] HwangEH, ParkJS, KimSO, SeongHG, KimSJ. Study on the controlling factors for the quenching crack sensitivity of ultra-strong automotive steel. J. Mater. Sci., 2020, 5583605.

[11] WanJQ, LouY, RuanHH. The partition coefficient of alloying elements and its influence on the pitting corrosion resistance of 15Cr–2Ni duplex stainless steel. Corros. Sci., 2018, 13913.

[12] SpeerJG, De MoorE, FindleyKO, MatlockDK, CoomanBCD, EdmondsDV. Analysis of microstructure evolution in quenching and partitioning automotive sheet steel. Metall. Mater. Trans. A, 2011, 42123591.

[13] EdmondsDV, HeK, RizzoFC, CoomanBCD, MatlockDK, SpeerJG. Quenching and partitioning martensite: A novel steel heat treatment. Mater. Sci. Eng. A, 2006, 43825.

[14] WangL, SpeerJG. Quenching and partitioning steel heat treatment. Metall. Microstruct. Anal., 2013, 24268.

[15] WagnerC, TraudW. The original formulation of the mixed potential concept and the basic theory of corrosion of a pure metal. Z. Elektrochem., 1938, 44391

[16] DevanathanMAV, StachurskiZ. The adsorption and diffusion of electrolytic hydrogen in palladium. Proc. R. Soc. Lond. A, 1962, 270134090.

[17] KimSJ, KimKY. Electrochemical hydrogen permeation measurement through high-strength steel under uniaxial tensile stress in plastic range. Scripta Mater., 2012, 66121069.

[18] LuuWC, WuJK. The influence of microstructure on hydrogen transport in carbon steels. Corros. Sci., 1996, 382239.

[19] International Organization for Standardization (ISO)ISO 17081: Method of Measurement of Hydrogen Permeation and Determination of Hydrogen Uptake and Transport in Metals by an Electrochemical Technique, 2014

[20] ParkGT, KohSU, JungHG, KimKY. Effect of microstructure on the hydrogen trapping efficiency and hydrogen induced cracking of linepipe steel. Corros. Sci., 2008, 5071865.

[21] SternM, GearyAL. Electrochemical polarization: I. A theoretical analysis of the shape of polarization curves. J. Electrochem. Soc., 1957, 104156.

[22] HanJN, PyunS, YangTH. Roles of thiourea as an inhibitor in hydrogen absorption into palladium electrode. J. Electrochem. Soc., 1997, 144124266.

[23] H.R. Bang, J.S. Park, and S.J. Kim, Effects of Ni-flash coating on hydrogen evolution, ad/absorption, and permeation behaviors of advanced high-strength steel during electro-Zn plating, J. Electroanal. Chem., 944(2023), art. No. 117653.

[24] ZhangJM, LiH, YangF, ChiQ, JiLK, FengYR. Effect of heat treatment process on mechanical properties and microstructure of a 9% Ni steel for large LNG storage tanks. J. Mater. Eng. Perform., 2013, 22123867.

[25] BhadeshiaHKDH. Prevention of hydrogen embrittlement in steels. ISIJ Int., 2016, 56124.

[26] AndrewsKW. Empirical formulae for the calculation of some transformation temperatures. J. Iron Steel Inst., 1965, 2037721

[27] TrasattiS. Work function, electronegativity, and electrochemical behaviour of metals. J. Electroanal. Chem. Interfacial Electrochem., 1972, 391163.

[28] R. Hossain, F. Pahlevani, M.Z. Quadir, and V. Sahajwalla, Stability of retained austenite in high carbon steel under compressive stress: An investigation from macro to nano scale, Sci. Rep., 6(2016), art. No. 34958.

[29] SakakibaraY, KubushiroK. Stress evaluation at the maximum strained state by EBSD and several residual stress measurements for plastic deformed austenitic stainless steel. World J. Mech., 2017, 78195..

[30] GussevMN, LeonardKJ. In situ SEM-EBSD analysis of plastic deformation mechanisms in neutron-irradiated austenitic steel. J. Nucl. Mater., 2019, 51745.

[31] I. Zurutuza, N. Isasti, E. Detemple, V. Schwinn, H. Mohrbacher, and P. Uranga, Effect of Nb and Mo additions in the microstructure/tensile property relationship in high strength quenched and quenched and tempered boron steels, Metals, 11(2021), No. 1, art. No. 29.

[32] R. Mishnev, Y. Borisova, S. Gaidar, T. Kniaziuk, O. Vagina, and R. Kaibyshev, Q&P response of a medium carbon low alloy steel, Metals, 13(2023), No. 4, art. No. 689.

[33] ParkJS, JungSP, KimSJ. Mitigating hydrogen embrittlement of advanced high-strength steel by controlling carbides (cementite and alloy carbides) and microstructural modification. J. Mater. Res. Technol., 2024, 284703.

[34] CabotA, PuntesVF, ShevchenkoE, et al.. Vacancy coalescence during oxidation of iron nanoparticles. J. Am. Chem. Soc., 2007, 1293410358.

[35] Y.J. Jeong, S.O. Kim, J.S. Park, et al., Strong and ductile Fe–24Mn–3Cr alloy resistant against erosion–corrosion, npj Mater. Degrad., 5(2021), art. No. 47.

[36] S. Riaz, M. Bashir, and S. Naseem, Iron oxide nanoparticles prepared by modified co-precipitation method, IEEE Trans. Magn., 50(2014), No. 1, art. No. 4003304.

[37] PouretedalHR, MomenzadehF. Synthesis, characterization and study of photocatalytic activity of nanocomposites of oxides and sulfides of Ni(II) and Ni(III). Bulg. Chem. Commun., 2015, 47159

[38] FarelasF, GaliciaM, BrownB, NesicS, CastanedaH. Evolution of dissolution processes at the interface of carbon steel corroding in a CO₂ environment studied by EIS. Corros. Sci., 2010, 522509.

[39] WeiJ, DongJH, ZhouYT, HeXY, WangCG, KeW. Influence of the secondary phase on micro galvanic corrosion of low carbon bainitic steel in NaCl solution. Mater. Charact., 2018, 139401.

RIGHTS & PERMISSIONS

University of Science and Technology Beijing