In-situ research on tensile deformation and microvoid formation in a nuclear pressure vessel steel

Zhifeng Zhang , Daming Tong , Xingyun Yang , Xiaofang Wang , Lizhan Han , Guanghua Yan , Chuanwei Li , Jianfeng Gu

International Journal of Minerals, Metallurgy, and Materials ›› 2025, Vol. 32 ›› Issue (8) : 1893 -1901.

PDF
International Journal of Minerals, Metallurgy, and Materials ›› 2025, Vol. 32 ›› Issue (8) : 1893 -1901. DOI: 10.1007/s12613-024-3043-0
Research Article
research-article

In-situ research on tensile deformation and microvoid formation in a nuclear pressure vessel steel

Author information +
History +
PDF

Abstract

Tensile deformation and microvoid formation of quenched and tempered SA508 Gr.3 steel were studied using an in-situ digital image correlation technique and in-situ electron backscatter diffraction (EBSD) measurements. The quenched steel with a mixture of upper bainite and granular bainite exhibited a high ultimate tensile strength (UTS) of ∼795 MPa and an elongation of ∼25%. After tempering, long-rod carbides and accumulated carbide particles were formed at the interface of bainite–ferrite subunits and prior austenite grain boundaries (PAGBs), respectively. The UTS of the tempered steel decreased to ∼607 MPa, whereas the total elongation increased to 33.0% with a local strain of 191.0% at the necked area. In-situ EBSD results showed that strain localization in the bainite–ferrite produced lattice rotation and dislocation pileup, thus leading to stress concentration at the discontinuities (e.g., martensite–austenite islands and carbides). Consequently, the decohesion of PAGBs dotted with martensite–austenite islands was the dominant microvoid initiation mechanism in the quenched steel, whereas microvoids primarily initiated through the fracturing of long-rod carbides and the decohesion of PAGBs with carbides aggregation in the tempered steel. The fracture surfaces for both the quenched and tempered specimens featured dimples, indicating the ductile failure mechanism caused by microvoid coalescence.

Keywords

nuclear pressure vessel steel / microvoid / mechanical properties / tensile deformation / microstructural evolution

Cite this article

Download citation ▾
Zhifeng Zhang, Daming Tong, Xingyun Yang, Xiaofang Wang, Lizhan Han, Guanghua Yan, Chuanwei Li, Jianfeng Gu. In-situ research on tensile deformation and microvoid formation in a nuclear pressure vessel steel. International Journal of Minerals, Metallurgy, and Materials, 2025, 32(8): 1893-1901 DOI:10.1007/s12613-024-3043-0

登录浏览全文

4963

注册一个新账户 忘记密码

References

[1]

LuSM, WanL, ZhengSJ, et al.. Effect of austenitizing temperature on martensitic transformation in SA508Gr.4N steel. J. Mater. Sci. Technol., 2024, 186244

[2]

WanL, LuSM, ZhengSJ, LiMN, DuanYH, XuZD. Elemental partitioning as a route to decrease HAZ hardness. J. Mater. Res. Technol., 2023, 23438

[3]

C.Y. Hsu, J. Stodolna, P. Todeschini, F. Delabrouille, and F. Christien, Effect of bainitic or martensitic microstructure of a pressure vessel steel on grain boundary segregation induced by step cooling simulating thermal aging, J. Nucl. Mater., 584(2023), art. No. 154554.

[4]

G.S. Rao, Y. Yagodzinskyy, Z. Que, P. Spätig, and H.P. Seifert, Study on hydrogen embrittlement and dynamic strain ageing on low-alloy reactor pressure vessel steels, J. Nucl. Mater., 556(2021), art. No. 153161.

[5]

LuCY, HeYM, YangJG, ZhengWJ, XieZG, GaoZL. An investigation of phase transition on the microstructural characteristic and creep behavior for the SA508 Gr.3 steel used for nuclear reactor pressure vessels. Mater. Sci. Eng. A, 2018, 711659

[6]

R. Ranjan and A. Meena, Influence of prior austenite grain size on martensite-austenite islands morphology and decomposition characteristics during two-step tempering in Mn–Ni–Mo steel, Mater. Today Commun., 39(2024), art. No. 108810.

[7]

YanGH, HanLZ, LiCW, LuoXM, GuJF. Characteristic of retained austenite decomposition during tempering and its effect on impact toughness in SA508 Gr.3 steel. J. Nucl. Mater., 2017, 483167

[8]

LiCW, HanLZ, LuoXM, LiuQD, GuJF. Effect of tempering temperature on the microstructure and mechanical properties of a reactor pressure vessel steel. J. Nucl. Mater., 2016, 477246

[9]

A. A. Benzerga and J.B. Leblond, Advances in Applied Mechanics, H. Aref and E. Giessen, eds., Elsevier, Amsterdam, 2010, p. 169.

[10]

BessonJ. Continuum models of ductile fracture: A review. Int. J. Damage Mech., 2010, 1913

[11]

W. Wciślik and R. Pała, Some microstructural aspects of ductile fracture of metals, Materials, 14(2021), No. 15, art. No. 4321.

[12]

PineauA, BenzergaA, PardoenT. Failure of metals I: Brittle and ductile fracture. Acta Mater., 2016, 107424

[13]

DasA. Stress/strain induced void?. Arch. Comput. Meth. Eng., 2021, 2831795

[14]

W. Wciślik and S. Lipiec, Void-induced ductile fracture of metals: Experimental observations, Materials, 15(2022), No. 18, art. No. 6473.

[15]

FengH, WangHJ, LiHB, ZhuHC, ZhangSC, JiangZH. Parent austenite grain reconstruction in martensitic steel. J. Mater. Sci. Technol., 2025, 215244

[16]

LongXY, SunDY, WangK, et al.. Effect of carbon distribution range in mixed bainite/martensite/retained austenite micro-structure on mechanical properties. J. Mater. Res. Technol., 2022, 17898

[17]

ChenK, LiHB, JiangZH, et al.. Multiphase microstructure formation and its effect on fracture behavior of medium carbon high silicon high strength steel. J. Mater. Sci. Technol., 2021, 7281

[18]

H.C. Ma, J.B. Zhao, Y. Fan, et al., Comparative study on corrosion fatigue behaviour of high strength low alloy steel and simulated HAZ microstructures in a simulated marine atmosphere, Int. J. Fatigue, 137(2020), art. No. 105666.

[19]

MosallaeeM, SemiromiMT. Effect of nickel content on the microstructural, mechanical and corrosion behavior of E7018-G electrode weld metal. J. Mater. Eng. Perform., 2021, 30128901

[20]

LanLY, QiuCL, SongHY, ZhaoDW. Correlation of martensite-austenite constituent and cleavage crack initiation in welding heat affected zone of low carbon bainitic steel. Mater. Lett., 2014, 12586

[21]

L.S. Derevyagina, A.I. Gordienko, A.M. Orishich, A.G. Malikov, N.S. Surikova, and M.N. Volochaev, Microstructure of intercritical heat affected zone and toughness of microalloyed steel laser welds, Mater. Sci. Eng. A, 770(2020), art. No. 138522.

[22]

LeeSG, SohnSS, KimB, KimWG, UmKK, LeeS. Effects of martensite-austenite constituent on crack initiation and propagation in inter-critical heat-affected zone of high-strength low-alloy (HSLA) steel. Mater. Sci. Eng. A, 2018, 715332

[23]

LuJX, ChangL, WangJ, SangLJ, WuSK, ZhangYF. In-situ investigation of the anisotropic mechanical properties of laser direct metal deposition Ti6Al4V alloy. Mater. Sci. Eng. A, 2018, 712199

[24]

W.J. Gao, J.X. Lu, J.L. Zhou, et al., Effect of grain size on deformation and fracture of Inconel718: An in situ SEM-EBSD-DIC investigation, Mater. Sci. Eng. A, 861(2022), art. No. 144361.

[25]

LiSC, GuoCY, HaoLL, KangYL, AnYG. In-situ EBSD study of deformation behaviour of 600 MPa grade dual phase steel during uniaxial tensile tests. Mater. Sci. Eng. A, 2019, 759624

[26]

M.N. Gussev, D.A. McClintock, T.S. Byun, and T.G. Lach, Recent progress in analysis of strain-induced phenomena in irradiated metallic materials and advanced alloys using SEM–EBSD in situ tensile testing, Curr. Opin. Solid State Mater. Sci., 28(2024), art. No. 101132.

[27]

N. Bibhanshu, M.N. Gussev, C.P. Massey, and K.G. Field, Investigation of deformation mechanisms in an advanced FeCrAl alloy using in situ SEM-EBSD testing, Mater. Sci. Eng. A, 832(2022), art. No. 142373.

[28]

C. Zhang, R.H. Ya, M. Sun, et al., In-situ EBSD study of deformation behavior of nickel-based superalloys during uniaxial tensile tests, Mater. Today Commun., 35(2023), art. No. 105522.

[29]

Z.H. Jiang, Y.H. Li, Z.D. Yang, P. Wang, D.Z. Li, and Y.Y. Li, The tempering behavior of martensite/austenite islands on the mechanical properties of a low alloy Mn–Ni–Mo steel with granular bainite, Mater. Today Commun., 26(2021), art. No. 102166.

[30]

LiuDG, CaiMH, DingH, HanD. Control of inter/intragranular κ-carbides and its influence on overall mechanical properties of a Fe–11Mn–10Al–1.25C low density steel. Mater. Sci. Eng. A, 2018, 71525

[31]

MinKS, KimKJ, NamSW. Investigation of the effect of the types and densities of grain boundary carbides on grain boundary cavitation resistance of AISI 321 stainless steel under creep–fatigue interaction. J. Alloys Compd., 2004, 3701–2223

[32]

N.Y. Du, H.H. Liu, Y.F. Cao, et al., In situ investigation of the fracture of primary carbides and its mechanism in M50 steel, Mater. Charact., 186(2022), art. No. 111822.

[33]

XuS, WuXQ, HanEH, KeW. Effects of dynamic strain aging on mechanical properties of SA508 class 3 reactor pressure vessel steel. J. Mater. Sci., 2009, 44112882

[34]

DongYZ, RenYJ, JiangH, ZhangSW, ZhaoSD. Numerical and experimental investigation of Notch-induced highspeed precise shearing of 42CrMo bar. Proc. Inst. Mech. Eng. Part C: J. Mech. Eng. Sci., 2021, 235194204

[35]

M. Marteleur, J. Leclerc, M.S. Colla, V.D. Nguyen, L. Noels, and T. Pardoen, Ductile fracture of high strength steels with morphological anisotropy, Part I: Characterization, testing, and void nucleation law, Eng. Fract. Mech., 244(2021), art. No. 107569.

RIGHTS & PERMISSIONS

University of Science and Technology Beijing

AI Summary AI Mindmap
PDF

107

Accesses

0

Citation

Detail

Sections
Recommended

AI思维导图

/