Dissolution of TiO₂ and TiN inclusions in CaO–SiO₂–B₂O₃-based fluorine-free mold flux

Abstract

Mold flux serves the crucial metallurgical function of absorbing inclusions, directly impacting the smoothness of the casting process as well as the cast slab quality. In this study, the dissolution behavior and mechanism of TiO₂ and TiN inclusions in molten CaO–SiO_2–B₂O₃-based fluorine-free mold flux were explored by in situ single hot thermocouple technology combined with X-ray photoelectron spectroscopy. The results showed that TiO₂ inclusions are effectively dissolved by the molten slag within 76 s, during which the original octahedral [TiO₆]⁸⁻ structures are destroyed and convert to the networker tetrahedral [TiO₄]⁴⁻ structures. However, the dissolution rate is much lower for TiN inclusions than for TiO₂ inclusions. This can be attributed to the fact that the TiN particles need to be oxidized and then dissolved in the molten slag to form tetrahedral [TiO₄]⁴⁻ and octahedral [TiO₆]⁸⁻ structures during the TiN inclusion dissolution process, which is accompanied by the generation of a large amount of N₂ gas. Moreover, CaTiO₃ crystals tend to nucleate and grow on bubble surfaces with sufficient octahedral [TiO₆]⁸⁻ structures and Ca²⁺ ions, eventually resulting in the molten slag being in a solid–liquid mixed state.

Keywords

TiO₂ inclusion / TiN inclusion / mold flux / fluorine-free / continuous casting

References

[1] Yen HW, Chen CY, Wang TY, Huang CY, Yang JR. Orientation relationship transition of nanometre sized interphase precipitated TiC carbides in Ti bearing steel. Mater. Sci. Technol., 2010, 26(4): 421.

[2] L.D. Xing, J.L. Guo, X. Li, et al., Control of TiN precipitation behavior in titanium-containing micro-alloyed steel, Mater. Today Commun., 25(2020), art. No. 101292.

[3] Shen YF, Wang CM, Sun X. A micro-alloyed ferritic steel strengthened by nanoscale precipitates. Mater. Sci. Eng. A, 2011, 528(28): 8150.

[4] Z. Chen, M. Li, X.F. Wang, S.P. He, and Q. Wang, Mechanism of floater formation in the mold during continuous casting of Ti-stabilized austenitic stainless steels, Metals, 9(2019), No. 6, art. No. 635.

[5] T.F. Zhao, X. Zheng, D.J. Huang, Z.H. Zhu, and Z.H. Yin, Thermodynamic research on the precipitation of Ti₂O₃, TiN and TiC in continuous casting of titanium microalloyed steel, J. Phys.: Conf. Ser., 2076(2021), No. 1, art. No. 012077.

[6] Li JY, Cheng GG, Ruan Q, Pan JX, Chen XR. Characteristics of nozzle clogging and evolution of oxide inclusion for Al-killed Ti-stabilized 18Cr stainless steel. Metall. Mater. Teans. B, 2019, 50(6): 2769.

[7] Cheng LM, Zhang LF, Ren Y, Yang W. Clogging behavior of a submerged entry nozzle for the casting of Ca-treated Al-killed Ti-bearing steel. Metall. Mater. Trans. B, 2021, 52(3): 1186.

[8] Cui H, Bao YP, Wang M, Wu WS. Clogging behavior of submerged entry nozzles for Ti-bearing IF steel. Int. J. Miner. Metall. Mater., 2010, 17(2): 154.

[9] Basu S, Choudhary SK, Girase NU. Nozzle clogging behaviour of Ti-bearing Al-killed ultra low carbon steel. ISIJ Int., 2004, 44(10): 1653.

[10] Zhou LJ, Pan ZH, Wang WL, et al. Interfacial interactions between inclusions comprising TiO₂ or TiN and the mold flux during the casting of titanium-stabilized stainless steel. Metall. Mater. Trans. B, 2020, 51(1): 85.

[11] Pan ZH, Zhou LJ, Wang WL. Study on the interaction process between mold flux and TiN/TiO₂ by sessile drop method. TMS 2020 149th Annual Meeting & Exhibition Supplemental Peoceedings, 2020, Cham, Springer, 67.

[12] W.L. Wang, D.X. Cai, L. Zhang, and I. Sohn, Effect of TiO₂ and TiN on the viscosity, fluidity, and crystallization of fluorine-free mold fluxes for casting Ti-bearing steels, Steel Res. Int., 92(2021), No. 2, art. No. 2000314.

[13] Mills KC, Fox AB, Li Z, Thackray RP. Performance and properties of mould fluxes. Ironmaking Steelmaking, 2005, 32(1): 26.

[14] Wang WL, Cai DX, Zhang L. A review of fluorine-free mold flux development. ISIJ Int., 2018, 58(11): 1957.

[15] Ozturk B. Solubility of TiN in continuous casting powders. Metall. Teans. B, 1992, 23(4): 523.

[16] Pretorius EB, Nunnington RC. Stainless steel slag fundamentals: From furnace to tundish. Ironmaking Steelmaking, 2002, 29(2): 133.

[17] Ren ZS, Hu XJ, Hou XM, Xue XX, Chou KC. Dissolution and diffusion of TiO₂ in the CaO–Al₂O_3–SiO₂ slag. Int. J. Miner. Metall. Mater., 2014, 21(4): 345.

[18] Park H, Park JY, Kim GH, Sohn I. Effect of TiO₂ on the viscosity and slag structure in blast furnace type slags. Steel Res. Int., 2012, 83(2): 150.

[19] Sun LF, Wang HP, Jiang MF, Lin QZ, Liu CL, Zou Y. Effects of TiO₂ on the viscocity and solidification temperature of mold fluxes for the stainless steel. Adv. Mater. Res., 2011, 189–193, 107.

[20] R.C. Nunnington and N. Sutcliffe, The steelmaking and casting of Ti stabilized stainless steels, [in] 59th Electric Furnace Conference and 19th Process Technology Conference, Arizona, 2001, p. 361.

[21] Hasegawa M, Maruhashi S, Muranaka Y, Hoshi F. Mechanism of formation of surface defects in continuously cast stainless steel slabs containing titanium. Tetsu-to-Hagane, 1987, 73(3): 505.

[22] B.Y. Li, X. Geng, Z.H. Jiang, Y. Hou, and W. Gong, Effects of BaO and B₂O₃ on the absorption of Ti inclusions for high titanium steel, Metals, 11(2021), No. 1, art. No. 165.

[23] Z.S. Bi, K.J. Li, C.H. Jiang, et al., Effects of B₂O₃ on the structure and properties of blast furnace slag by molecular dynamics simulation, J. Non-Cryst. Solids, 551(2021), art. No. 120412.

[24] Lai FF, Yao W, Li JL. Effect of B₂O₃ on structure of CaO–Al₂O_3–SiO_2–TiO_2–B₂O₃ glassy systems. ISIJ Int., 2020, 60(8): 1596.

[25] L.T. Bian and Y.H. Gao, Influence of B₂O₃ and basicity on viscosity and structure of medium titanium bearing blast furnace slag, J. Chem., 2016(2016), art. No. 6754593

[26] Sun YQ, Liao JL, Zheng K, Wang XD, Zhang ZT. Effect of B₂O₃ on the structure and viscous behavior of Ti-bearing blast furnace slags. JOM, 2014, 66(10): 2168.

[27] Zhang L, Wang WL. Growth mechanism and structure evolution during nucleation of calcium borosilicate crystal in CaO–SiO_2–B₂O₃ based fluorine-free mold flux. ISIJ Int., 2019, 59(6): 1041.

[28] Zhang L, Wang WL, Sohn I. Crystallization behavior and structure analysis for molten CaO–SiO_2–B₂O₃ based fluorine-free mold fluxes. J. Non-Cryst. Solids, 2019, 511, 41.

[29] Zhang L, Wang WL, Zhai BY, Sohn I. The evolution of the mold flux melt structure during the process of fluorine replacement by B₂O₃. J. Am. Ceram. Soc., 2020, 103(1): 112.

[30] Zhang JJ, Zhai BY, Zhang L, Wang WL. A comparison study on interfacial properties of fluorine-bearing and fluorine-free mold flux for casting advanced high-strength steels. J. Iron Steel Res. Int., 2022, 29(10): 1613.

[31] T.M. Yeo, J.W. Cho, M. Alloni, S. Casagrande, and R. Carli, Structure and its effect on viscosity of fluorine-free mold flux: Substituting CaF₂ with B₂O₃ and Na₂O, J. Non-Cryst. Solids, 529(2020), art. No. 119756.

[32] The Materials Project. Materials Data Materials Project for TiO ₂ (mp-2657) from Database Version v2021 [2022-10-28]. https://doi.org/10.17188/1184648

[33] The Materials Project. Materials Data Materials Project for TiN (mp-492) from Database Version v2021 [2022-10-28]. https://doi.org/10.17188/1208488

[34] Wu X, Zhao SX, Wei L, Zhao EL, Li JW, Nan CW. Improved structural reversibility and cycling stability of Li₂MnSiO₄ cathode material by the pillar effect of [TiO_x] polyanions. ChemistrySelect, 2018, 3(15): 4047.

[35] Jin SQ, Wang ZD, Tao GJ, et al. UV resonance Raman spectroscopic insight into titanium species and structure-performance relationship in boron-free Ti-MWW zeolite. J. Catal., 2017, 353, 305.

[36] Wang Z, Shu QF, Chou K. Structure of CaO-B₂O₃-SiO₂-TiO₂ glasses: A Raman spectral study. ISIJ Int., 2011, 51(7): 1021.

[37] Wang Z, Shu QF, Chou K. Study on structure characteristics of B₂O₃ and TiO₂-bearing F-free mold flux by Raman spectroscopy. High Temp. Mater. Processes, 2013, 32(3): 265.

[38] X.H. Zhang, Z. Du, H.T. Wu, and Y.L. Yue, Effect of TiO₂ on structure and dielectric properties of RO-Al₂O₃-B₂O₃-SiO₂ (R = Ca, Mg) glasses, Surf. Rev. Lett., 20(2013), No. 03n04, art. No. 1350030.

[39] Kleebusch E, Patzig C, Hoeche T, Russel C. The evidence of phase separation droplets in the crystallization process of a Li₂O–Al₂O_3–SiO₂ glass with TiO₂ as nucleating agent - An X-ray diffraction and (S)TEM-study supported by EDX-analysis. Ceram. Int., 2018, 44(3): 2919.

[40] Back GS, Yoon MJ, Jung WG. Effect of the Cr₂O₃ and TiO₂ as nucleating agents in SiO_2–Al₂O_3–CaO–MgO glass-ceramic system. Met. Mater. Int., 2017, 23(4): 798.

[41] Wang Q, Lu YJ, He SP, Mills KC, Li ZS. Formation of TiN and Ti(C,N) in TiO₂ containing, fluoride free, mould fluxes at high temperature. Ironmaking Steelmaking, 2011, 38(4): 297.

[42] Y.H. Hua and B.J. Zhao, Phase equilibria in the system Al₂O_3–MnO–SiO₂: Thermodynamic and application, [in] 11th International Symposium on High-Temperature Metallurgical Processing, California, 2020, p. 183.

[43] Wittmer M, Noser J, Melchior H. Oxidation kinetics of TiN thin films. J. Appl. Phys., 1981, 52(11): 6659.

[44] Kusabiraki K. Infrared spectra of vitreous silica and sodium silicates containing titanium. J. Non-Cryst. Solids, 1986, 79(1–2): 208.

[45] Yang D, Zhou HH, Wang J, et al. Influence of TiO₂ on viscosity, phase composition and structure of chromium-containing high-titanium blast furnace slag. J. Mater. Res. Technol., 2021, 12, 1615.

[46] Yan K, Che DF. A coupled model for simulation of the gas–liquid two-phase flow with complex flow patterns. Int. J. Multiphase Flow, 2010, 36(4): 333.

[47] S.P. Gu, G.H. Wen, Z.Q. Ding, J.L. Guo, P. Tang, and Q. Liu, Effect of bubbles on crystallization behavior of CaO–SiO₂ based slags, Metals, 9(2019), No. 2, art. No. 193.