Effect of FeO concentration in sinter iron ore on reduction behavior in a hydrogen-enriched blast furnace

Abstract

Japan started the national project “COURSE 50” for CO₂ reduction in the 2000s. This project aimed to establish novel technologies to reduce CO₂ emissions with partially utilization of hydrogen in blast furnace-based ironmaking by 30% by around 2030 and use it for practical applications by 2050. The idea is that instead of coke, hydrogen is used as the reducing agent, leading to lower fossil fuel consumption in the process. It has been reported that the reduction behavior of hematite, magnetite, calcium ferrite, and slag in the sinter is different, and it is also considerably influenced by the sinter morphology. This study aimed to investigate the reduction behavior of sinters in hydrogen enriched blast furnace with different mineral morphologies in CO—CO₂—H₂ mixed gas. As an experimental sample, two sinter samples with significantly different hematite and magnetite ratios were prepared to compare their reduction behaviors. The reduction of wustite to iron was carried out at 1000, 900, and 800°C in a CO—CO₂—H₂ atmosphere for the mineral morphology-controlled sinter, and the following findings were obtained. The reduction rate of smaller amount of FeO led to faster increase of the reduction rate curve at the initial stage of reduction. Macro-observations of reduced samples showed that the reaction proceeded from the outer periphery of the sample toward the inside, and a reaction interface was observed where reduced iron and wustite coexisted. Micro-observations revealed three layers, namely, wustite single phase in the center zone of the sample, iron single phase in the outer periphery zone of the sample, and iron oxide-derived wustite FeO and iron, or calcium ferrite-derived wustite ‘FeO’ and iron in the reaction interface zone. A two-interface unreacted core model was successfully applied for the kinetic analysis of the reduction reaction, and obtained temperature dependent expressions of the chemical reaction coefficients from each mineral phases.

Keywords

hydrogen / reduction / wustite / hematite / magnetite / calcium ferrite / two-interface unreacted core model / COURSE50

References

[1] Greenhouse Gas Inventory Office of JapanMinistry of the Environment, Japan. National Greenhouse Gas Inventory Report of JAPAN 2022, 2022, Japan, Center for Global Environmental Research, Earth System Division, National Institute for Environmental Studies

[2] Miwa T, Okuda H. CO₂ ultimate reduction in steelmaking process by innovative technology for cool earth 50 (COURSE50). J. Jpn. Inst. Eng., 2010, 89(1): 28

[3] Ban-Ya S, Iguchi Y, Nagasaka T. Rate of reduction of liquid wustite with hydrogen. Tetsu-to-Hagane, 1984, 70(14): 1689.

[4] Chen YB, Zuo HB. Review of hydrogen-rich ironmaking technology in blast furnace. Ironmaking Steelmaking, 2021, 48(6): 749.

[5] Ma KH, Deng JY, Wang G, Zhou Q, Xu J. Utilization and impacts of hydrogen in the ironmaking processes: A review from lab-scale basics to industrial practices. Int. J. Hydrogen Energy, 2021, 46(52): 26646.

[6] Steel Year Book, Japan Metal Daily, Tokyo, 2014, p. 84.

[7] Qie YN, Lyu Q, Li JP, Lan CC, Liu XJ. Effect of hydrogen addition on reduction kinetics of iron oxides in gas-injection BF. ISIJ Int., 2017, 57(3): 404.

[8] Murakami T, Wakabayashi H, Maruoka D, Kasai E. Effect of hydrogen concentration in reducing gas on the changes in mineral phases during reduction of iron ore sinter. ISIJ Int., 2020, 60(12): 2678.

[9] Higuchi K, Matsuzaki S, Saito K, Nomura S. Improvement in reduction behavior of sintered ores in a blast furnace through injection of reformed coke oven gas. ISIJ Int., 2020, 60(10): 2218.

[10] Yagi T, Ono Y. A method of analysis for reduction of iron oxide in mixed-control kinetics. ISIJ Int., 1968, 8(6): 377.

[11] Ishida M, Wen CY. Comparison of kinetic and diffusional models for solid-gas reactions. AIChE J., 1968, 14(2): 311.

[12] Murayama T, Ono Y. Method of determination of parameters included in ISHIDA-WEN’S model. Tetsu-to-Hagane, 1987, 73(10): 1323.

[13] Szekely J, Evans JW. A structural model for gas—Solid reactions with a moving boundary. Chem. Eng. Sci., 1970, 25(6): 1091.

[14] Szekely J, Evans JW. A structural model for gas-solid reactions with a moving boundary-II: The effect of grain size, porosity and temperature on the reaction of porous pellets. Chem. Eng. Sci., 1971, 26(11): 1901.

[15] Noguchi D, Ohno KI, Maeda T, Nishioka K, Shimizu M. Kinetics of reduction step of wustite to iron of hematite and quaternary calcium ferrite mixtures. Tetsu-to-Hagane, 2012, 98(2): 55.

[16] Spitzer RH, Manning FS, Philbrook WO. Generalized model for the gaseous, topochemical reduction of porous hematite spheres. Trans. Metall. Soc. AIME, 1966, 236, 1715

[17] Ranz WE, Marshall WR. Evaporation from drops, part I. Chem. Eng. Prog., 1952, 48(3): 141

[18] St. Clair HW. Rate of reduction of an oxide sphere in a stream of reducing gas. Trans. Metall. Soc. AIME, 1965, 233, 1145

[19] Usui T, Naito M, Murayama T, Morita ZI. Kinetic analysis on gaseous reduction of agglomerates, part 1, reaction models for gaseous reduction of agglomerates. Tetsu-to-Hagane, 1994, 80(6): 431.

[20] Maeda T, Ono Y. Kinetics of reduction step of wustite to iron in gaseous reduction of quaternary calcium ferrite. Tetsu-to-Hagane, 1991, 77(10): 1569.

[21] Murayama T, Ono Y, Kamijo C. Effect of the amount of gangue on rate parameters included in the unreacted-core model. CAMP-ISIJ, 1989, 2(4): 949