Effects of BN content on the mechanical properties of nanocrystalline 3Y-TZP/Al₂O₃/BN dental ceramics

Abstract

3Y-TZP/3wt% Al₂O₃ powder was coated with varying amounts of BN using the urea and borate reaction sintering method, and then multiphase ceramics were prepared by hot pressing sintering. The micro-topography and the compositional analysis of synthesized ceramics were conducted through scanning electron microscopy, transmission electron microscopy and X-ray diffraction. A mechanical tester was used to analyze the Vickers hardness, fracture toughness, and bending strength of the synthesized ceramics. The results showed that the ceramic with a BN content of 12wt% showed the best processability, but had diminished mechanical properties (such as fracture toughness and bending strength). The ceramic with a BN content of 9wt% showed better processability than those with 3wt% and 6wt% BN. However, the fracture toughness was affected by the addition of 9wt% BN, making this ceramic only usable as a base material for a three-unit fixed bridge. In contrast, the ceramics with a BN content of 3wt% or 6wt% fulfilled the criteria for use in multi-unit restoration, but their low processability made them unsuitable for milling after sintering.

Keywords

multiphase ceramic / boron nitride / mechanical properties / reaction sintering method

References

[1] Ramesh TR, Makam G, Harish PV, Krishnakumar U, Nandakishore B. Zirconia ceramics as a dental biomaterial - An over view. Trends Biomater. Artif. Organs, 2012, 26(3): 154

[2] Yildiz BK, Yilmaz H, Tür YK. Influence of nickel addition on the microstructure and mechanical properties of Al₂O₃-5vol% ZrO₂ ceramic composites prepared via precipitation method. Int. J. Miner. Metall. Mater., 2019, 26(7): 908.

[3] Caglar I, Ates SM, Yesil Duymus Z. The effect of various polishing systems on surface roughness and phase transformation of monolithic zirconia. J. Adv. Prosthodont., 2018, 10(2): 132.

[4] Zambrano DF, Barrios A, Tobón LE, Serna C, Gómez P, Osorio JD, Toro A. Thermal properties and phase stability of yttria-stabilized zirconia (YSZ) coating deposited by air plasma spray onto a Ni-base superalloy. Ceram. Int., 2018, 44(4): 3625.

[5] Camposilvan E, Leone R, Gremillard L, Sorrentino R, Zarone F, Ferrari M, Chevalier J. Aging resistance. mechanical properties and translucency of different yttria-stabilized zirconia ceramics for monolithic dental crown applications, 2018, Dent.Mater.34(6): 879

[6] Li WY, Sun J. Effects of ceramic density and sintering temperature on the mechanical properties of a novel polymerinfiltrated ceramic-network zirconia dental restorative (filling) material. Med. Sci. Monit., 2018, 24, 3068.

[7] Ramola RC, Rawat M, Joshi K, Das A, Gautam SK, Singh F. Study of phase transformation induced by electronic excitation in pure and yttrium doped ZrO2 thin films. Mater. Res. Express, 2017, 4(9): 096401.

[8] Gonzaga CC, Okada CY, Cesar PF, Miranda WG Jr, Yoshimura HN Jr. Effect of processing induced particle alignment on the fracture toughness and fracture behavior of multiphase dental ceramics. Dent. Mater., 2009, 25(11): 1293.

[9] Wang SJ, Jia DC, Yang ZH, Duan XM, Tian Z, Zhou Y. Effect of BN content on microstructures, mechanical and dielectric properties of porous BN/Si₃N₄ composite ceramics prepared by gel casting. Ceram. Int., 2013, 39(4): 4231.

[10] Shi ZQ, Wang JP, Qiao GJ, Jin ZH. Effects of weak boundary phases (WBP) on the microstructure and mechanical properties of pressureless sintered Al2O₃/h-BN machinable composites. Mater. Sci. Eng. A, 2008, 492(1-2): 29.

[11] Wu JS, Zhou L, Xing HL, Wang Z, Dong CF, Yang SF. Preparation processes of 3% yttria-stabilized tetragonal zirconia polycrystalline ceramic composite powders coated with nano-sized Al₂O₃-boron nitride. West Chin. J. Stomatol., 2017, 35(5): 461

[12] Gali S, Ravikumar K, Murthy BVS, Basu B. Zirconia toughened mica glass ceramics for dental restorations. Dent. Mater., 2018, 34(3): e36.

[13] ISO International, ISO Standard 6872: Dentistry-Ceramic Materials, Switzerland, 2015.

[14] Zhong B, Zhao GL, Huang XX, Xia L, Tang XH, Zhang SC, Wen GW. Microstructure and mechanical properties of ZTA/BN machinable ceramics fabricated by reactive hot pressing. J. Eur. Ceram. Soc., 2015, 35(2): 641.

[15] Phillipps AJ, Clegg WJ, Clyne TW. Fracture behaviour of ceramic laminates in bending-I. Modelling of crack propagation. Acta Metall. Mater., 1993, 41(3): 805.

[16] Sakoda S, Nakao N, Watanabe I. The effect of abrading and cutting instruments on machinability of dental ceramics. J. Mater. Sci. Mater. Med., 2018, 29(3): 34.

[17] Guilardi LF, Pereira GKR, Gündel A, Rippe MP, Valandro LF. Surface micro-morphology. phase transformation, 2017, andmechanicalreliabilityofgroundandagedmolithiczirconiaceramicJ.Mech.Behav.Biomed.Mater.65, 849

[18] Chen ZY, Wang LJ, Du XJ, Sun ZH, Li FS, Chou KC. Carbon deposition in porous nickel/yttria-stabilized zirconia anode under methane atmosphere. Int. J. Miner. Metall. Mater., 2019, 26(3): 350.

[19] Falin A, Cai QR, Santos EJG, Scullion D, Qian D, Zhang R, Yang Z, Huang SM, Watanabe K, Taniguchi T, Barnett MR, Chen Y, Ruoff RS, Li LH. Mechanical properties of atomically thin boron nitride and the role of interlayer interactions. Nat. Commun., 2017, 8, 15815.

[20] Yang SF, Yang LQ, Jin ZH, Guo TW, Wang L, Liu HC. New nano-sized Al₂O₃-BN coating 3Y-TZP ceramic composites for CAD/CAM-produced all-ceramic dental restorations. Part I. Fabrication of powders. Nanomed. Nanotechnol. Biol. Med., 2009, 5(2): 232.

[21] Zafar MS. Wear behavior of various dental restorative materials. Mater. Technol., 2019, 34(1): 25.

[22] Rupawala A, Musani SI, Madanshetty P, Dugal R, Shah UD, Sheth EJ. A study on the wear of enamel caused by monolithic zirconia and the subsequent phase transformation compared to two other ceramic systems. J. Indian Prosthodont. Soc., 2017, 17(1): 8