Effect of quenching-partitioning treatment on the microstructure, mechanical and abrasive properties of high carbon steel

Abstract

The present work employed the X-ray diffraction, scanning electron microscopy, electron backscattered diffraction, and electron probe microanalysis techniques to identify the microstructural evolution and mechanical and abrasive behavior of high carbon steel during quenching-partitioning treatment with an aim to enhance the toughness and wear resistance of high carbon steel. Results showed that, with the increase in partitioning temperature from 250 to 400°C, the amount of retained austenite (RA) decreased resulting from the carbide precipitation effect after longer partitioning times. Moreover, the stability of RA generally increased because of the enhanced degree of carbon enrichment in RA. Given the factors affecting the toughness of high carbon steel, the stability of RA associated with size, carbon content, and morphology plays a significant role in determining the toughness of high carbon steel. The analysis of the wear resistance of samples with different mechanical properties shows that hardness is the primary factor affecting the wear resistance of high carbon steel, and the toughness is the secondary one.

Keywords

high carbon steel / quenching and partitioning / microstructural evolution / retained austenite

References

[1] Hossain R, Pahlevani F, Sahajwalla V. Surface modification of high carbon steel through microstructural engineering. Mater. Charact., 2019, 148, 116.

[2] Hossain R, Pahlevani F, Sahajwalla V. Stability of retained austenite in high carbon steel — Effect of post-tempering heat treatment. Mater. Charact., 2019, 149, 239.

[3] Bhadeshia HKDH. High performance bainitic steels. Mater. Sci. Forum, 2005, 500–501, 63.

[4] Hossain R, Pahlevani F, Sahajwalla V. Effect of small addition of Cr on stability of retained austenite in high carbon steel. Mater. Charact., 2017, 125, 114.

[5] Zhang S, Findley KO. Quantitative assessment of the effects of microstructure on the stability of retained austenite in TRIP steels. Acta Mater., 2013, 61(6): 1895.

[6] Gao GH, Zhang H, Gui XL, Tan ZL, Bai BZ, Weng YQ. Enhanced strain hardening capacity in a lean alloy steel treated by a “disturbed” bainitic austempering process. Acta Mater., 2015, 101, 31.

[7] Malinov LS, Malinov VL, Burova DV, Anichenkov VV. Increasing the abrasive wear resistance of low-alloy steel by obtaining residual metastable austenite in the structure. J. Frict. Wear, 2015, 36(3): 237.

[8] Long XY, Zhang FC, Kang J, Yang ZN, Wu DD, Wu KM, Zhang GH. Study on carbide-bearing and carbide-free bainitic steels and their wear resistance. Mater. Sci. Technol., 2017, 33(5): 615.

[9] Guo H, Zhao A, Zhi C, Ding R, Wang J. Two-body abrasion wear mechanism of super bainitic steel. Mater. Sci. Technol., 2017, 33(7): 893.

[10] Gao GH, Zhang H, Gui XL, Luo P, Tan ZL, Bai BZ. Enhanced ductility and toughness in an ultrahigh-strength Mn-Si-Cr-C steel: The great potential of ultrafine filmy retained austenite. Acta Mater., 2014, 76, 425.

[11] Wang XD, Guo ZH, Rong YH. Mechanism exploration of an ultrahigh strength steel by quenching-partitioning-tempering process. Mater. Sci. Eng. A, 2011, 529, 35.

[12] Speer J, Matlock DK, De Cooman BC, Schroth JG. Carbon partitioning into austenite after martensite transformation. Acta Mater., 2003, 51(9): 2611.

[13] Guo HR, Gao GH, Gui XL, Misra RDK, Bai BZ. Structure-property relation in a quenched-partitioned low alloy steel involving bainite transformation. Mater. Sci. Eng. A, 2016, 667, 224.

[14] Dong J, Zhou XS, Liu YC, Li C, Liu CX, Li HJ. Effects of quenching-partitioning-tempering treatment on microstructure and mechanical performance of Nb-V-Ti micoalloyed ultra-high strength steel. Mater. Sci. Eng. A, 2017, 690, 283.

[15] Yan S, Liu XH, Liu WJ, Lan HF, Wu HY. Microstructural evolution and mechanical properties of low-carbon steel treated by a two-step quenching and partitioning process. Mater. Sci. Eng. A, 2015, 640, 137.

[16] Santofimia MJ, Zhao L, Petrov R, Kwakernaak C, Sloof WG, Sietsma J. Microstructural development during the quenching and partitioning process in a newly designed low-carbon steel. Acta Mater., 2011, 59(15): 6059.

[17] Tan XD, Xu YB, Yang XL, Liu ZQ, Wu D. Effect of partitioning procedure on microstructure and mechanical properties of a hot-rolled directly quenched and partitioned steel. Mater. Sci. Eng. A, 2014, 594, 149.

[18] Tsuchiyama T, Tobata J, Tao T, Nakada N, Takaki S. Quenching and partitioning treatment of a low-carbon martensitic stainless steel. Mater. Sci. Eng. A, 2012, 532, 585.

[19] Yi HL, Chen P, Hou ZY, Hong N, Cai HL, Xu YB, Wu D, Wang GD. A novel design: Partitioning achieved by quenching and tempering (Q-T & P) in an aluminium-added low-density steel. Scripta Mater., 2013, 68(6): 370.

[20] Zhang J, Ding H, Misra RDK, Wang C. Microstructural evolution and consequent strengthening through niobium-microalloying in a low carbon quenched and partitioned steel. Mater. Sci. Eng. A, 2015, 641, 242.

[21] J.P. Lai, L.P. Zhang, W. Gong, X. Xu, and C.A. Xiao, Two-body abrasion resistance of high carbon steel treated by quenching-partitioning-tempering process, Wear, 440–441(2019), art. No. 203096.

[22] Song YY, Cui JP, Rong LJ. Microstructure and mechanical properties of 06Cr13Ni4Mo steel treated by quenching-tempering-partitioning process. J. Mater. Sci. Technol., 2016, 32(2): 189.

[23] Behera AK, Olson GB. Nonequilibrium thermodynamic modeling of carbon partitioning in quench and partition (Q&P) steel. Scripta Mater., 2018, 147, 6.

[24] Li HY, Lu XW, Wu XC, Min YA, Jin XJ. Bainitic transformation during the two-step quenching and partitioning process in a medium carbon steel containing silicon. Mater. Sci. Eng. A, 2010, 527(23): 6255.

[25] Santofimia MJ, Speer JG, Clarke AJ, Zhao L, Sietsma J. Influence of interface mobility on the evolution of austenite-martensite grain assemblies during annealing. Acta Mater., 2009, 57(15): 4548.

[26] Maheswari N, Chowdhury SG, Kumar KCH, Sankaran S. Influence of alloying elements on the microstructure evolution and mechanical properties in quenched and partitioned steels. Mater. Sci. Eng. A, 2014, 600, 12.

[27] Jacques P J, Delannay F, Ladrière J. On the influence of interactions between phases on the mechanical stability of retained austenite in transformation-induced plasticity multiphase steels. Metall. Mater. Trans. A, 2001, 32(11): 2759.

[28] Timokhina IB, Hodgson PD, Pereloma EV. Effect of microstructure on the stability of retained austenite in transformation-induced-plasticity steels. Metall. Mater. Trans. A, 2004, 35(8): 2331.

[29] De Knijf D, Petrov R, Föjer C, Kestens LAI. Effect of fresh martensite on the stability of retained austenite in quenching and partitioning steel. Mater. Sci. Eng. A, 2014, 615, 107.

[30] Blondé R, Jimenez-Melero E, Zhao L, Wright JP, Brück E, van der Zwaag S, van Dijk NH. High-energy X-ray diffraction study on the temperature-dependent mechanical stability of retained austenite in low-alloyed TRIP steels. Acta Mater., 2012, 60(2): 565.

[31] van Dijk NH, Butt AM, Zhao L, Sietsma J, Offerman SE, Wright JP, van der Zwaag S. Thermal stability of retained austenite in TRIP steels studied by synchrotron X-ray diffraction during cooling. Acta Mater., 2005, 53(20): 5439.

[32] Jimenez-Melero E, van Dijk NH, Zhao L, Sietsma J, Offerman SE, Wright JP, van der Zwaag S. Characterization of individual retained austenite grains and their stability in low-alloyed TRIP steels. Acta Mater., 2007, 55(20): 6713.

[33] Xiong XC, Chen B, Huang MX, Wang JF, Wang L. The effect of morphology on the stability of retained austenite in a quenched and partitioned steel. Scripta Mater., 2013, 68(5): 321.

[34] Zhao HS, Li W, Zhu X, Lu XH, Wang L, Zhou S, Jin XJ. Analysis of the relationship between retained austenite locations and the deformation behavior of quenching and partitioning treated steels. Mater. Sci. Eng. A, 2016, 649, 18.

[35] Narayanaswamy B, Hodgson P, Timokhina I, Beladi H. The impact of retained austenite characteristics on the two-body abrasive wear behavior of ultrahigh strength bainitic steels. Metall. Mater. Trans. A, 2016, 47(10): 4883.

[36] de Diego-Calderón I, Sabirov I, Molina-Aldareguia JM, Föjer C, Thiessen R, Petrov RH. Microstructural design in quenched and partitioned (Q&P) steels to improve their fracture properties. Mater. Sci. Eng. A, 2016, 657, 136.

[37] Ding R, Tang D, Zhao AM. A novel design to enhance the amount of retained austenite and mechanical properties in low-alloyed steel. Scripta Mater., 2014, 88, 21.

[38] Yan S, Liu XH, Liu WJ, Lan HF, Wu HY. Comparison on mechanical properties and microstructure of a C-Mn-Si steel treated by quenching and partitioning (Q&P) and quenching and tempering (Q&T) processes. Mater. Sci. Eng. A, 2015, 620, 58.

[39] Efremenko VG, Hesse O, Friedrich TH, Kunert M, Brykov MN, Shimizu K, Zurnadzhy VI, Suchmann P. Two-body abrasion resistance of high-carbon high-silicon steel: Metastable austenite vs nanostructured bainite. Wear, 2019, 418–419, 24.

[40] Yang J, Wang TS, Zhang B, Zhang FC. Sliding wear resistance and worn surface microstructure of nanostructured bainitic steel. Wear, 2012, 282–283, 81.

[41] Hu F, Wu KM, Hodgson PD. Effect of retained austenite on wear resistance of nanostructured dual phase steels. Mater. Sci. Technol., 2016, 32(1): 40.

[42] Koval’ AD, Efremenko VG, Brykov MN, Andrushchenko MI, Kulikovskii RA, Efremenko AV. Principles for developing grinding media with increased wear resistance. Part 1. Abrasive wear resistance of iron-based alloys. J. Frict. Wear, 2012, 33(1): 39.