Fine structure characterization of an explosively-welded GH3535/316H bimetallic plate interface

Abstract

An explosion-welded technology was induced to manufacture the GH3535/316H bimetallic plates to provide a more cost-effective structural material for ultrahigh temperature, molten salt thermal storage systems. The microstructure of the bonding interfaces were extensively investigated by scanning electron microscopy, energy dispersive spectrometry, and an electron probe microanalyzer. The bonding interface possessed a periodic, wavy morphology and was adorned by peninsula- or island-like transition zones. At higher magnification, a matrix recrystallization region, fine grain region, columnar grain region, equiaxed grain region, and shrinkage porosity were observed in the transition zones and surrounding area. Electron backscattered diffraction demonstrated that the strain in the recrystallization region of the GH3535 matrix and transition zone was less than the substrate. Strain concentration occurred at the interface and the solidification defects in the transition zone. The dislocation substructure in 316H near the interface was characterized by electron channeling contrast imaging. A dislocation network was formed in the grains of 316H. The microhardness decreased as the distance from the welding interface increased and the lowest hardness was inside the transition zone.

Keywords

GH3535/316H bimetallic plate / ultrahigh temperature molten salt / explosive welding / interface structure / dislocation substructure

References

[1] Xu HX, Lin J, Zhong YJ, Zhu ZY, Chen Y, Liu JD, Ye BJ. Characterization of molten 2LiF-BeF₂ salt impregnated into graphite matrix of fuel elements for thorium molten salt reactor. Nucl. Sci. Tech., 2019, 30(5): 74.

[2] Han FF, Zhou BM, Huang HF, Leng B, Lu YL, Li ZJ, Zhou XT. Effect of long-term thermal exposure on the hot ductility behavior of GH3535 alloy. Mater. Sci. Eng. A, 2016, 673, 299.

[3] Jiang L, Ye XX, Wang DJ, Li ZJ. Synchrotron radiation-based materials characterization techniques shed light on molten salt reactor alloys. Nucl. Sci. Tech., 2020, 31(1): 6.

[4] Han FF, Zhou BM, Huang HF, Leng B, Lu YL, Dong JS, Li ZJ, Zhou XT. The tensile behavior of GH3535 superalloy at elevated temperature. Mater. Chem. Phys., 2016, 182, 22.

[5] Liu T, Dong JS, Wang L, Li ZJ, Zhou XT, Lou LH, Zhang J. Effect of long-term thermal exposure on microstructure and stress rupture properties of GH3535 superalloy. J. Mater. Sci. Technol., 2015, 31(3): 269.

[6] Liu BX, Wang S, Fang W, Yin FX, Chen CX. Meso and microscale clad interface characteristics of hot-rolled stainless steel clad plate. Mater. Charact., 2019, 148, 17.

[7] Groschopp J, Heyne V, Hofmann B. Explosively clad titanium steel composite. Weld. Int., 1987, 1(9): 879.

[8] Malyutina YN, Skorohod KA, Shevtsova KE, Chesnokova AV. Multilayered titanium-steel composite produced by explosive welding. AIP Conf. Proc., 2015, 1683(1): 020142.

[9] Xie MX, Shang XT, Zhang LJ, Bai QL, Xu TT. Interface characteristic of explosive-welded and hot-rolled TA1/X65 bimetallic plate. Metals, 2018, 8(3): 159.

[10] Gulenc B. Investigation of interface properties and weldability of aluminum and copper plates by explosive welding method. Mater. Des., 2008, 29(1): 275.

[11] Loureiro A, Mendes R, Ribeiro JB, Leal RM. Effect of explosive ratio on explosive welding quality of copper to aluminium. Cienc. Tecnol. Mater., 2017, 29(1): e46.

[12] Kacar R, Acarer M. An investigation on the explosive cladding of 316L stainless steel-din-P355GH steel. J. Mater. Process. Technol., 2004, 152(1): 91.

[13] Gladkovsky SV, Kuteneva SV, Sergeev SN. Microstructure and mechanical properties of sandwich copper/steel composites produced by explosive welding. Mater. Charact., 2019, 154, 294.

[14] Prasanthi TN, Sudha RC, Saroja S. Explosive cladding and post-weld heat treatment of mild steel and titanium. Mater. Des., 2016, 93, 180.

[15] Carvalho GHSFL, Galvão I, Mendes R, Leal RM, Loureiro A. Formation of intermetallic structures at the interface of steel-to-aluminium explosive welds. Mater. Charact., 2018, 142, 432.

[16] Szachogluchowicz I, Sniezek L, Hutsaylyuk V. Low cycle fatigue properties of AA2519-Ti6Al4V laminate bonded by explosion welding. Eng. Fail. Anal., 2016, 69, 77.

[17] Ashani JZ, Bagheri SM. Explosive scarf welding of aluminum to copper plates and their interface properties. Materialwiss. Werkstofftech., 2009, 40(9): 690.

[18] Bataev IA, Ogneva TS, Bataev AA, Mali VI, Esikov MA, Lazurenko DV, Guo Y, Jorge Junior AM. Explosively welded multilayer Ni-Al composites. Mater. Des., 2015, 88, 1082.

[19] Zhang LJ, Pei Q, Zhang JX, Bi ZY, Li PC. Study on the microstructure and mechanical properties of explosive welded 2205/X65 bimetallic sheet. Mater. Des., 2014, 64, 462.

[20] Kaya Y, Kahraman N, Durgutlu A, Gülenç B. Investigation of the microstructural. mechanical and corrosion properties of grade A ship steel-duplex stainless steel composites produced via explosive welding, 2017, Metall.Mater.Trans.A48(8): 3721.

[21] Akbari Mousavi SAA, Farhadi Sartangi P. Experimental investigation of explosive welding of cp-titanium/AISI 304 stainless steel. Mater. Des., 2009, 30(3): 459.

[22] Acarer M, Gülenç B, Findik F. Investigation of explosive welding parameters and their effects on microhardness and shear strength. Mater. Des., 2003, 24(8): 659.

[23] Prazmowski M, Rozumek D, Paul H. Static and fatigue tests of bimetal Zr-steel made by explosive welding. Eng. Fail. Anal., 2017, 75, 71.

[24] Rozumek D, Marciniak Z. Fatigue tests of bimetal zirconium- steel made by explosive welding. Procedia Eng., 2016, 160, 137.

[25] Rozumek D, Kwiatkowski G. The influence of heat treatment parameters on the cracks growth under cyclic bending in st-Ti clad obtained by explosive welding. Metals, 2019, 9(3): 338.

[26] Ruggles TJ, Fullwood DT, Kysar JW. Resolving geometrically necessary dislocation density onto individual dislocation types using EBSD-based continuum dislocation microscopy. Int. J. Plast., 2016, 76, 231.

[27] Pandey A, Kabirian F, Hwang JH, Choi SH, Khan AS. Mechanical responses and deformation mechanisms of an AZ31 Mg alloy sheet under dynamic and simple shear deformations. Int. J. Plast., 2015, 68, 111.

[28] Farooq MU, Klement U, Nolze G. The role of α- to ɛ-Co phase transformation on strain hardening of a Co-Cr-Mo laser clad. Mater. Sci. Eng. A, 2007, 445-446, 40.

[29] Gutierrez-Urrutia I, Raabe D. Dislocation and twin substructure evolution during strain hardening of an Fe-22 wt.% Mn-0.6 wt.% C TWIP steel observed by electron channeling contrast imaging. Acta Mater., 2011, 59(16): 6449.

[30] Findik F. Recent developments in explosive welding. Mater. Des., 2011, 32(3): 1081.