Improvement of the microstructural features and mechanical properties of advanced high-strength steel DP590 welds

Abstract

The effects of the welding current mode in resistance spot welding on the microstructure and mechanical properties of advanced high-strength steel dual-phase 590 (DP590) sheets were investigated. Results showed that a rough martensitic structure was formed in the weld zone of the sample welded via the single-pulsed mode, whereas the microstructure in the heat-affected zone consisted of a very rough martensitic microstructure and rough ferrite. However, using the secondary pulse mode led to the formation of tempered martensite in the weld zone. The maximum load and the energy absorption to failure of the samples with the secondary pulsed cycle were higher than those of the samples with the single-pulsed mode. Tensile shear results indicated that the secondary pulsed mode could significantly change the mode of failure upon shear tension testing. Therefore, the obtained results suggest that the use of secondary pulsed mode can improve the microstructural feature and mechanical properties of advanced high-strength steel DP590 welds.

Keywords

advanced high-strength steel / resistance spot welding / microstructure / mechanical properties

References

[1] Yuan XJ, Li C, Chen JB, Li XY, Liang XB, Pan XY. Resistance spot welding of dissimilar DP600 and DC54D steels. J. Mater. Process. Technol., 2017, 239, 31.

[2] Wang B, Hua L, Wang XK, Li JJ. Effects of multi-pulse tempering on resistance spot welding of DP590 steel. Int. J. Adv. Manuf. Technol., 2016, 86(9–12): 2927.

[3] Li YB, Li DL, Lin ZQ, David SA, Feng Z, Tang W. Review: Magnetically assisted resistance spot welding. Sci. Technol. Weld. Joining, 2016, 21(1): 59.

[4] Chen RM, Lou M, Li YB, Carlson BE. Improving weldability of Al-Si coated press hardened steel using stepped current pulse schedule. J. Manuf. Process., 2019, 48, 31.

[5] Wang B, Hua L, Wang XK, Song YK, Liu YL. Effects of electrode tip morphology on resistance spot welding quality of DP590 dual-phase steel. Int. J. Adv. Manuf. Technol., 2016, 83(9–12): 1917.

[6] Long HQ, Hu YM, Jin XQ, Shao JH, Zhu H. Effect of holding time on microstructure and mechanical properties of resistance spot welds between low carbon steel and advanced high strength steel. Comput. Mater. Sci., 2016, 117, 556.

[7] Mallick PK. Rowe J. Advanced materials for automotive applications: An overview. Advanced Materials in Automotive Engineering, 2012, Cambridge, Woodhead Publishing, 5.

[8] Safanama DS, Marashi SPH, Pouranvari M. Similar and dissimilar resistance spot welding of martensitic advanced high strength steel and low carbon steel: Metallurgical characteristics and failure mode transition. Sci. Technol. Weld. Joining, 2012, 17(4): 288.

[9] Kuziak R, Kawalla R, Waengler S. Advanced high strength steels for automotive industry. Arch. Civ. Mech. Eng., 2008, 8(2): 103.

[10] Zuidema BK. Bridging the design-manufacturing-materials data gap: Material properties for optimum design and manufacturing performance in light vehicle steel-intensive body structures. JOM, 2012, 64(9): 1039.

[11] Chao YJ, Ward JD, Sands RG. Charpy impact energy, fracture toughness and ductile-brittle transition temperature of dual-phase 590 Steel. Mater. Des., 2007, 28(2): 551.

[12] J. Ha, H. Huh, H. Lee, and K.S. Kim, Failure characteristics of spot welds of AHSS under quasi-static conditions, [in] T. Proulx, ed., Experimental and Applied Mechanics, Volume 6: Proceedings of the 2011 Annual Conference on Experimental and Applied Mechanics, Uncasville, Connecticut, 2011, p. 623.

[13] Němeček S, Mužík T, Míšek M. Differences between laser and arc welding of HSS steels. Phys. Procedia, 2012, 39, 67.

[14] Marashi P, Pouranvari M, Amirabdollahian S, Abedi A, Goodarzi M. Microstructure and failure behavior of dissimilar resistance spot welds between low carbon galvanized and austenitic stainless steels. Mater. Sci. Eng. A., 2008, 480(1–2): 175.

[15] Ashiri R, Haque MA, Ji CW, Shamanian M, Salimijazi HR, Park YD. Supercritical area and critical nugget diameter for liquid metal embrittlement of Zn-coated twining induced plasticity steels. Scripta Mater., 2015, 109, 6.

[16] Zhao DW, Wang YX, Zhang L, Zhang P. Effects of electrode force on microstructure and mechanical behavior of the resistance spot welded DP600 joint. Mater. Des., 2013, 50, 72.

[17] Khan MI, Kuntz ML, Zhou Y. Effects of weld microstructure on static and impact performance of resistance spot welded joints in advanced high strength steels. Sci. Technol. Weld. Joining, 2008, 13(3): 294.

[18] Noh W, Kim W, Yang X, Kang M, Lee MG, Chung K. Simple and effective failure analysis of dissimilar resistance spot welded advanced high strength steel sheets. Int. J. Mech. Sci., 2017, 121, 76.

[19] Podržaj P, Polajnar I, Diaci J, Kariž Z. Overview of resistance spot welding control. Sci. Technol. Weld. Joining, 2008, 13(3): 215.

[20] Ashiri R, Shamanian M, Salimijazi HR, Haque MA, Bae JH, Ji CW, Chin KG, Park YD. Liquid metal embrittlement-free welds of Zn-coated twinning induced plasticity steels. Scripta Mater., 2016, 114, 41.

[21] Khanna SK, Long X. Residual stresses in resistance spot welded steel joints. Sci. Technol. Weld. Joining, 2008, 13(3): 278.

[22] Pouranvari M, Marashi SPH. Critical review of automotive steels spot welding: Process, structure and properties. Sci. Technol. Weld. Joining, 2013, 18(5): 361.

[23] Kumar P, Sinha AN. Effect of average beam power on microstructure and mechanical properties of Nd: YAG laser welding of 304L and st37 steel. World J. Eng., 2019, 16(3): 377.

[24] Wang B, Duan QQ, Yao G, Pang JC, Li XW, Wang L, Zhang ZF. Investigation on fatigue fracture behaviors of spot-welded Q&P980 steel. Int. J. Fatigue, 2014, 66, 20.

[25] Dancette S, Fabrègue D, Massardier V, Merlin J, Dupuy T, Bouzekri M. Experimental and modeling investigation of the failure resistance of advanced high strength steels spot welds. Eng. Fract. Mech., 2011, 78(10): 2259.

[26] Dancette S, Fabrègue D, Massardier V, Merlin J, Dupuy T, Bouzekri M. Investigation of the tensile shear fracture of advanced high strength steel spot welds. Eng. Fail. Anal., 2012, 25, 112.