Shape of slab solidification end under non-uniform cooling and its influence on the central segregation with mechanical soft reduction

Abstract

In order to study the effect of continuous casting process parameters on the shape of slab solidification end under non-uniform cooling, a solidification model of a continuous-cast slab with non-uniform cooling condition was established with ProCAST software. The model was verified by the results of nail shooting tests and the infrared temperature measurement equipment. Four characteristic parameters were defined to evaluate the uniformity of the shape of slab solidification end. The results showed that the nonuniformity at the beginning and end of solidification, the solidification end length, and the solidification unevenness increased with the rise of casting speed. For each 10°C increase of superheat, the solidification unevenness increased by about 0.022. However, the effect of superheat on the solidification end length can be ignored. The secondary cooling strength showed minimal effect on the nonuniformity at the beginning and end of solidification. With the increase in secondary cooling intensity, the solidification end length decreased, but the solidification unevenness increased. In addition, the central segregation of the slab produced with and without the mechanical soft reduction (MSR) process was investigated. The transverse flow of molten steel with low solid fraction influenced the central segregation morphology under MSR.

Keywords

continuous casting / heat transfer model / nail shooting / shape of solidification end / central segregation

References

[1] Flemings MC. Our understanding of macrosegregation: Past and present. ISIJ Int., 2000, 40(9): 833.

[2] Chen Z, Shen HF. Simulation of macrosegregation in a 36-t steel ingot using a multiphase model. Int. J. Miner. Metall. Mater., 2020, 27(2): 200.

[3] Zhang XG, Matsuura K, Ohno M. Abnormal grain growth in austenite structure reversely transformed from ferrite/pearlite-banded structure. Metall. Mater. Trans. A, 2014, 45(10): 4623.

[4] Majka TF, Matlock DK, Krauss G. Development of microstructural banding in low-alloy steel with simulated Mn segregation. Metall. Mater. Trans. A, 2002, 33(6): 1627.

[5] Krauss G. Solidification. segregation, 2003, andbandingincarbonandalloysteelsMetall.Mater.Trans.B34(6): 781.

[6] Han YS, Yan W, Zhang JS, Chen WQ, Chen J, Liu Q. Optimization of thermal soft reduction on continuous-casting billet. ISIJ Int., 2020, 60(1): 106.

[7] Chen Y, Xiao MF, Wu GR. Dynamic soft reduction technology for bloom casting. J. Iron Steel Res. Int., 2010, 17(6): 1.

[8] Han ZW, Chen DF, Feng K, Long MJ. Development and application of dynamic soft-reduction control model to slab continuous casting process. ISIJ Int., 2010, 50(11): 1637.

[9] Vynnycky M. Applied mathematical modelling of continuous casting processes: A review. Metals, 2018, 8(11): 928.

[10] Zeng J, Chen WQ, Wang QX, Wang GS. Improving inner quality in continuous casting rectangular billets: Comparison between mechanical soft reduction and final electromagnetic stirring. Trans. Indian Inst. Met., 2016, 69(8): 1623.

[11] Zavalishchin AN, Rumyantsev MI, Chikishev DN, Efremova MV, Kozhevnikova EV. Influence of “soft” reduction on the structure of continuous cast ingot and the properties of rolled products of microalloyed steels. Metallurgist, 2019, 63(3-4): 238.

[12] Li L, Zhao X, Lan P, Tie ZP, Tang HY, Zhang JQ. Effect of roll surface profile on thermal-mechanical behavior of continuously cast bloom in soft reduction process. TMS 2019 148th Annual Meeting & Exhibition Supplemental Proceedings, 2019, Cham, Springer, 93.

[13] Thome R, Harste K. Principles of billet soft-reduction and consequences for continuous casting. ISIJ Int., 2006, 46(12): 1839.

[14] Yim CH, Park JK, You BD, Yang SM. The effect of soft reduction on center segregation in C.C. slab. ISIJ Int., 1996, 36(Suppl): S231.

[15] Jauhola M, Haapala M. The latest results of dynamic soft reduction in slab CC-machine. 83rd Steelmaking Conference Proceedings, 2000 201.

[16] Ji C, Luo S, Zhu MY, Sahai Y. Uneven solidification during wide-thick slab continuous casting process and its influence on soft reduction zone. ISIJ Int., 2014, 54(1): 103.

[17] Ito Y, Yamanaka A, Watanabe T. Internal reduction efficiency of continuously cast strand with liquid core. Rev. Met. Paris, 2000, 97(10): 1171.

[18] Wu MH, Domitner J, Ludwig A. Using a two-phase columnar solidification model to study the principle of mechanical soft reduction in slab casting. Metall. Mater. Trans. A, 2012, 43(3): 945.

[19] Domitner J, Wu MH, Kharicha A, Ludwig A, Kaufmann B, Reiter J, Schaden T. Modeling the effects of strand surface bulging and mechanical softreduction on the macrosegregation formation in steel continuous casting. Metall. Mater. Trans. A, 2014, 45(3): 1415.

[20] Li J. Shape of slab solidification end under non-uniform cooling and its influence on the central... 1797 Trans. A. 45(2014), 2018, 3p.1415.B.RogbergandL.EkInfluenceofsoftreductionthefluidflowporosityandcentersegregationinCChighcarbon-andstainlesssteelbloomsISIJInt.58(3): 478.

[21] Cai ZZ, Zhu MY. Non-uniform heat transfer behavior during shell solidification in a wide and thick slab continuous casting mold. Int. J. Miner. Metall. Mater., 2014, 21(3): 240.

[22] Li DP, Wu HZ, Wang HF, Li H. Growth of solidified shell in bloom continuous casting mold of hypo-peritectic steel based on a FeS tracer method. J. Iron Steel Res. Int., 2020, 27(7): 782.

[23] Long MJ, Dong ZH, Chen DF, Liao Q, Ma YG. Effect of uneven solidification on the quality of continuous casting slab. Int. J. Mater. Prod. Technol., 2013, 47(1/2/3/4): 216.

[24] Preßlinger H, Ilie S, Reisinger P, Schiefermüller A, Pissenberger A, Parteder E, Bernhard C. Methods for assessment of slab centre segregation as a tool to control slab continuous casting with soft reduction. ISIJ Int., 2006, 46(12): 1845.

[25] Choudhary SK, Ganguly S, Sengupta A, Sharma V. Solidification morphology and segregation in continuously cast steel slab. J. Mater. Process. Technol., 2017, 243, 312.

[26] Fei P, Min Y, Liu CJ, Jiang MF. Effect of continuous casting speed on mold surface flow and the related near-surface distribution of non-metallic inclusions. Int. J. Miner. Metall. Mater., 2019, 26(2): 186.

[27] Savage J, Pritchard WH. The problem of rupture of the billet in the continuous casting of steel. J. Iron Steel Inst., 1954, 178, 3.

[28] Louhenkilpi S, Miettinen J, Holappa L. Simulation of microstructure of as-cast steels in continuous casting. ISIJ Int., 2006, 46(6): 914.

[29] Nozaki T, Matsuno JI, Murata K, Ooi H, Kodama M. A secondary cooling pattern for preventing surface cracks of continuous casting slab. Trans. Iron Steel Inst. Jpn., 1978, 18(6): 330.

[30] Ha JS, Cho JR, Lee BY, Ha MY. Numerical analysis of secondary cooling and bulging in the continuous casting of slabs. J. Mater. Process. Technol., 2001, 113(1-3): 257.

[31] Hardin RA, Liu K, Beckermann C, Kapoor A. A transient simulation and dynamic spray cooling control model for continuous steel casting. Metall. Mater. Trans. B, 2003, 34(3): 297.

[32] Long MJ, Chen DF, Wang QX, Luo DH, Han ZW, Liu Q, Gao WX. Determination of CC slab solidification using nail shooting technique. Ironmaking Steelmaking, 2012, 39(5): 370.

[33] Ji C, Luo S, Zhu MY. Analysis and application of soft reduction amount for bloom continuous casting process. ISIJ Int., 2014, 54(3): 504.

[34] Réger M, Vero B, Józsa R, Csepeli Z. Effect of mushy zone permeability on the formation of centerline segregation in slab casting. Mater. Sci. Forum, 2014, 790-791, 296.