Controllable nitridation of Ta₂O₅ in molten salts for enhanced photocatalysis

Abstract

Pyrolysis of the Ta₂O₅/melamine mixture in molten chlorides is herein demonstrated as a facile and controllable method to nitridize and functionalize Ta₂O₅. The influence of the stoichiometry and composition of Ta₂O₅/melamine in molten salts on the nitridation process is rationalized to ensure the controllable preparation of Ta₃N₅ and Ta₃N₅/TaON. The characterization results, including scanning electron microscopy, transmission electron microscopy, elemental mapping, X-ray photoelectron spectroscopy, and photoluminescence spectroscopy, all confirm the existence of the Ta₃N₅/TaON heterojunction, in which the TaON nanoparticles are closely anchored to the Ta₃N₅ nanorods. Benefiting from its composition and structure, the Ta₃N₅/TaON composites show enhanced photocatalytic activity for the degradation of methylene blue. The present study highlights that the molten salt method using a solid nitrogen source can be a new technique for rationalizing the design of nitrides and oxynitrides.

Keywords

molten salts / photocatalysis / Ta₃N₅ / TaON / heterojunction

References

[1] Joseph A, Vellayan K, González B, Vicente MA, Gil A. Effective degradation of methylene blue in aqueous solution using Pd-supported Cu-doped Ti-pillared montmorillonite catalyst. Appl. Clay Sci., 2019, 168, 7.

[2] Molla A, Li YY, Mandal B, Kang SG, Hur SH, Chung JS. Selective adsorption of organic dyes on graphene oxide: theoretical and experimental analysis. Appl. Surf. Sci., 2019, 464, 170.

[3] Kausar A, Iqbal M, Javed A, Aftab K, Nazli ZH, Bhatti HN, Nouren S. Dyes adsorption using clay and modified clay: A review. J. Mol. Liq., 2018, 256, 395.

[4] Bao SY, Wu QF, Chang SZ, Tian BZ, Zhang JL. Z-scheme CdS–Au–BiVO₄ with enhanced photocatalytic activity for organic contaminant decomposition. Catal. Sci. Technol., 2017, 7(1): 124.

[5] H.X. Liu, X.G. Wei, T.D. Li, Z.Y. Jiang, Q.F. Niu, and H.L. Zhou, Mosaic structure ZnO formed by secondary crystallization with enhaned photocatalytic performance, Int. J. Miner. Metall. Mater., https://doi.org/10.1007/s12613-020-2033-0.

[6] Borges ME, Sierra M, Cuevas E, García RD, Esparza P. Photocatalysis with solar energy: Sunlight-responsive photocatalyst based on TiO₂ loaded on a natural material for wastewater treatment. Sol. Energy, 2016, 135, 527.

[7] Garcia-Segura S, Brillas E. Applied photoelectrocatalysis on the degradation of organic pollutants in wastewaters. J. Photochem. Photobiol. C, 2017, 31, 1.

[8] J.G. Hou, Y.Z. Wu, S.Y. Cao, F. Liang, Z.S. Lin, Z.M. Gao, and L.C. Sun, In situ phase-induced spatial charge separation in core-shell oxynitride nanocube heterojunctions realizing robust solar water splitting, Adv. Energy Mater., 7(2017), No. 17, art. No. 1700171.

[9] Hu YD, Chen G, Li CM, Zhou YS, Sun JX, Hao S, Han ZH. Fabrication of {010} facet dominant BiTaO₄ single-crystal nanoplates for efficient photocatalytic performance. J. Mater. Chem. A, 2016, 4(14): 5274.

[10] Ge L, Han CC, Xiao XL, Guo LL. Synthesis and characterization of composite visible light active photocatalysts MoS₂–g-C₃N₄ with enhanced hydrogen evolution activity. Int. J. Hydrogen Energy, 2013, 38(17): 6960.

[11] Y.M. Hunge, A.A. Yadav, A.G. Dhodamani, N. Suzuki, C. Terashima, A. Fujishima, and V.L. Mathe, Enhanced photocatalytic performance of ultrasound treated GO/TiO₂ composite for photocatalytic degradation of salicylic acid under sunlight illumination, Ultrason. Sonochem., 61(2020), art. No. 104849.

[12] Tian L, Li JY, Liang F, Wang JK, Li SS, Zhang HJ, Zhang SW. Molten salt synthesis of tetragonal carbon nitride hollow tubes and their application for removal of pollutants from wastewater. Appl. Catal. B, 2018, 225, 307.

[13] Sun JH, Dong SY, Wang YK, Sun SP. Preparation and photocatalytic property of a novel dumbbell-shaped ZnO microcrystal photocatalyst. J. Hazard. Mater., 2009, 172(2–3): 1520.

[14] T.F. Wang, A. Arakaki, and D. Kisailus, Template-free synthesis of Ta₃N₅ hollow nanospheres as a visible-light-driven photocatalyst, J. Phys. Commun., 3(2019), No. 7, art. No. 075010.

[15] Wang SM, Li ZY, Guan Y, Lu L, Shi Z, Weng P, Yan SC, Zou ZG. Visible light driven TaON/V₂O₅ heterojunction photocatalyst for deep elimination of volatile-aromatic compounds. Appl. Catal. B, 2019, 245, 220.

[16] Kado Y, Hahn R, Lee CY, Schmuki P. Strongly enhanced photocurrent response for Na doped Ta₃N₅-nano porous structure. Electrochem. Commun., 2012, 17, 67.

[17] Nguyen TDC, Nguyen TPLC, Mai HTT, Dao VD, Nguyen MP, Nguyen VN. Novel photocatalytic conversion of CO₂ by vanadium-doped tantalum nitride for valuable solar fuel production. J. Catal., 2017, 352, 67.

[18] Shi Z, Feng JY, Shan H, Wang X, Xu Z, Huang HT, Qian QF, Yan SC, Zou ZG. Low onset potential on single crystal Ta₃N₅ polyhedron array photoanode with preferential exposure of {001} facets. Appl. Catal. B, 2018, 237, 665.

[19] Murthy DHK, Matsuzaki H, Wang Z, Suzuki Y, Hisatomi T, Seki K, Inoue Y, Domen K, Furube A. Origin of the overall water splitting activity of Ta₃N₅ revealed by ultra-fast transient absorption spectroscopy. Chem. Sci., 2019, 10(20): 5353.

[20] Chen RZ, Zhen C, Yang YQ, Sun XD, Irvine JTS, Wang LZ, Liu G, Cheng HM. Boosting photoelectrochemical water splitting performance of Ta₃N₅ nanorod array photoanodes by forming a dual co-catalyst shell. Nano Energy, 2019, 59, 683.

[21] J.Y. Feng, H.T. Huang, T. Fang, X. Wang, S.C. Yan, W.J. Luo, T. Yu, Y.X. Zhao, Z.S. Li, and Z.G. Zou, Defect egineering in semiconductors: manipulating nonstoichiometric defects and understanding their impact in oxynitrides for solar energy conversion, Adv. Funct. Mater., 29(2019), No. 11, art. No. 1808389.

[22] Zhang P, Zhang JJ, Gong JL. Tantalum-based semiconductors for solar water splitting. Chem. Soc. Rev., 2014, 43(13): 4395.

[23] Gao QS, Giordano C, Antonietti M. Controlled synthesis of tantalum oxynitride and nitride nanoparticles. Small, 2011, 7(23): 3334.

[24] Gao QS, Wang SN, Ma YC, Tang Y, Giordano C, Antonietti M. SiO₂-surface-assisted controllable synthesis of TaON and Ta₃N₅ nanoparticles for alkene epoxidation. Angew. Chem. Int. Ed., 2012, 51(4): 961.

[25] B. Niu, B.Y. Liu, and Z.M. Xu, Controllable synthesis of high-efficient TaO_xN_y and Ta₃N₅ photocatalysts through vacuum nitriding using melamine as a nitrogen source, J. Alloys Compd., 809(2019), art. No. 151846.

[26] Adhikari SP, Hood ZD, More KL, Ivanov I, Zhang LF, Gross M, Lachgar A. Visible light assisted photocatalytic hydrogen generation by Ta₂O₅/Bi₂O₃, TaON/Bi₂O₃, and Ta₃N₅/Bi₂O₃ composites. RSCAdv., 2015, 5(68): 54998.

[27] Kanigaridou Y, Petala A, Frontistis Z, Antonopoulou M, Solakidou M, Konstantinou I, Deligiannakis Y, Mantzavinos D, Kondarides DI. Solar photocatalytic degradation of bisphenol A with CuO_x/BiVO₄: Insights into the unexpectedly favorable effect of bicarbonates. Chem. Eng. J., 2017, 318, 39.

[28] Weng W, Zhou J, Gu D, Xiao W. Thermoelectrochemical formation of Fe/Fe₃C@hollow N-doped carbon in molten salts for enhanced catalysis. J. Mater. Chem. A, 2020, 8, 4800.

[29] Weng W, Wang Z, Guo ZC, Jiao SQ, Wang MY. Enhanced electrodeposition and separation of metallic Cr from soluble K₂CrO₄ on a liquid Zn. J. Energy Chem., 2020, 40, 204.

[30] Xiao W, Zhou J, Yu L, Wang D, Lou XW. Electrolytic formation of crystalline silicon/germanium alloy nanotubes and hollow particles with enhanced lithium-storage properties. Angew. Chem. Int. Ed, 2016, 55(26): 7427.

[31] Li N, Zhou J, Sheng ZQ, Xiao W. Molten salt-mediated formation of g-C₃N₄–MoS₂ for visible-light-driven photocatalytic hydrogen evolution. Appl. Surf. Sci., 2018, 430, 218.

[32] Kartal L, Daryal MB, Şireli GK, Timur S. One-step electrochemical reduction of stibnite concentrate in molten borax. Int. J. Miner. Metall. Mater., 2019, 26(10): 1258.

[33] Costa L, Camino G. Thermal behaviour of melamine. J. Therm. Anal., 1988, 34(2): 423.

[34] McLamb N, Sahoo PP, Fuoco L, Maggard PA. Flux growth of single-crystal Na₂Ta₄O₁₁ particles and their photocatalytic hydrogen production. Cryst. Growth Des., 2013, 13(6): 2322.

[35] Ma SS, Hisatomi T, Maeda K, Moriya Y, Domen K. Enhanced water oxidation on Ta₃N₅ photocatalysts by modification with alkaline metal salts. J. Am. Chem. Soc., 2012, 134(49): 19993.

[36] Shi Z, Xu Z, Feng JY, Huang HT, Qian QF, Yan SC, Zou ZG. Molten salt-assisted a-axis-oriented growth of Ta₃N₅ nanorod arrays with enhanced charge transport for efficient photoelectrochemical water oxidation. CrystEngComm, 2018, 20(36): 5364.

[37] Kim YW, Cha S, Kwak I, Kwon IS, Park K, Jung CS, Cha EH, Park J. Surface-modified Ta₃N₅ nanocrystals with boron for enhanced visible-light-driven photoelectrochemical water splitting. ACS Appl. Mater. Inter., 2017, 9(42): 36715.

[38] Lu L, Wang SM, Zhou CG, Shi Z, Zhu H, Xin ZY, Wang XH, Yan SC, Zou ZG. Surface chemistry imposes selective reduction of CO₂ to CO over Ta₃N₅/LaTiO₂N photocatalyst. J. Mater. Chem. A, 2018, 6(30): 14838.

[39] Le Chi NTP, Dieu Cam NT, Van Thuan D, Truong TT, Thanh Truc NT, Van Hoang C, Thu Phuong TT, Pham TD, Thanh Tung MH, Minh Thu NT, Phuong NM, Nguyen VN. Synthesis of vanadium doped tantalum oxy-nitride for photocatalytic reduction of carbon dioxide under visible light. Appl. Surf. Sci., 2019, 467–468, 1249.

[40] I. Narkeviciute and T.F. Jaramillo, Effects of Ta₃N₅ morphology and composition on the performance of Si–Ta₃N₅ photoanodes, Solar RRL, 1(2017), No. 11, art. No. 1700121.

[41] Bae ST, Shin H, Lee S, Kim DW, Jung HS, Hong KS. Visible-light photocatalytic activity of NH₃-heat-treated Ta₂O₅ to decompose rhodamine B in aqueous solution. React. Kinet. Mech. Catal., 2011, 106(1): 67.

[42] Gao J, Yu JY, Zhou L, Muhammad J, Dong XL, Wang YN, Yu HT, Quan X, Li SJ, Jung YG. Interface evolution in the platelet-like SiC@C and SiC@SiO₂ monocrystal nanocapsules. Nano Res., 2017, 10(8): 2644.

[43] Wang HH, Liu WX, Ma J, Liang Q, Qin W, Lartey PO, Feng XJ. Design of GO/TiO₂ one-dimensional photonic crystal photocatalytic photocatalysts with improved photocatalytic activities for tetracycline. Int. J. Miner. Metall. Mater., 2020, 27(6): 830.

[44] W. Weng, B.M. Jiang, Z. Wang, and W. Xiao, In situ electrochemical conversion of CO₂ in molten salts to advanced energy materials with reduced carbon emissions, Sci. Adv., 6(2020), No. 9, art. No. 9278.

[45] Wang Z, Hou JG, Jiao SQ, Huang K, Zhu HM. In situ chemical reduction of the Ta₃N₅ quantum dots coupled TaON hollow spheres heterojunction photocatalyst for water oxidation. J. Mater. Chem, 2012, 22(41): 21972.