Effect of spheroidization of cementite in ductile cast iron

Abstract

The research aims to provide an alternative to austempering treatment of ductile cast iron with a simple and cost-effective heat-treatment process. This goal was accomplished by applying a simple one-step spheroidization heat treatment to the as-cast ductile iron, which would normally possess a coarse pearlitic microstructure to a significant extent. Spheroidization experiments involving isothermal holding below the lower critical temperature (A1) were conducted followed by standard mechanical testing and microstructural characterization for an experimental ductile iron. After improving the spheroidization holding time at a given temperature, the work shows that the ductility and toughness of an as-cast ductile iron can be improved by 90% and 40%, respectively, at the cost of reducing the tensile strength by 8%. Controlled discretization of the continuous cementite network in pearlitic matrix of the ductile iron is deemed responsible for the improved properties. The work also shows that prolonged holding time during spheroidization heat treatment leads to degradation of mechanical properties due to the inhomogenous microstructure formation caused by heterogeneous decomposition and cementite clustering in the material. The main outcome of this work is the demonstration of ductile cast iron’s necking behavior due to spheroidization heat treatment.

Keywords

spheroidization / cementite / ductile iron / toughness / heat treatment

References

[1] Stefanescu DM. Stefanescu DM. A history of cast iron. Cast Iron Science and Technology, 2017, Materials Park, OH, ASM International, 3.

[2] de Bouw M, Wouters I, Vereecken J, Lauriks L. Iron and steel varieties in building industry between 1860 and 1914 — A complex and confusing situation resolved. Constr. Build. Mater., 2009, 23(8): 2775.

[3] Iacoviello F, Cocco VD, Favaro G. Pearlitic ductile cast iron: Mechanical properties gradient analysis in graphite elements. Procedia Struct. Integrity, 2018, 9, 9.

[4] Gagg CR, Lewis PR. The rise and fall of cast iron in Victorian structures — A case study review. Eng. Fail. Anal., 2011, 18(8): 1963.

[5] Labrecque C, Gagné M. Ductile iron: Fifty years of continuous development. Can. Metall. Q., 1998, 37(5): 343.

[6] Cui JJ, Chen LQ. Microstructure and abrasive wear resistance of an alloyed ductile iron subjected to deep cryogenic and austempering treatments. J. Mater. Sci. Technol., 2017, 33(12): 1549.

[7] Cui JJ, Chen LQ. Microstructures and mechanical properties of a wear-resistant alloyed ductile iron austempered at various temperatures. Metall. Mater. Trans. A, 2015, 46(8): 3627.

[8] Hsu CH, Chuang TL. Influence of stepped austempering process on the fracture toughness of austempered ductile iron. Metall. Mater. Trans. A, 2001, 32(10): 2509.

[9] Voigt RC, Lee YH. Kabil YH, Said ME. Properties and application of austempered ductile irons. Current Advances in Mechanical Design and Production IV, 1989, Oxford, Pergamon Press, 29.

[10] Trudel A, Gagné M. Effect of composition and heat treatment parameters on the characteristics of austempered ductile irons. Can. Metall. Q., 1997, 36(5): 289.

[11] Stouģhton B, Billinger RD. The spheroidizing of cementite. Ind. Eng. Chem., 1926, 18(8): 785.

[12] Shin DH, Han SY, Park KT, Kim YS, Paik YN. Spheroidization of low carbon steel processed by equal channel angular pressing. Mater. Trans., 2003, 44(8): 1630.

[13] Lv ZQ, Wang B, Wang ZH, Sun SH, Fu WT. Effect of cyclic heat treatments on spheroidizing behavior of cementite in high carbon steel. Mater. Sci. Eng. A, 2013, 574, 143.

[14] Tokaji K, Horie T, Enomoto Y. Effects of microstructure and carbide spheroidization on fatigue behaviour in high V-Cr-Ni cast irons. Int. J. Fatigue, 2006, 28(3): 281.

[15] Casteletti LC, Kinap PEB, Nascente PAP. Heat treatments for obtaining spheroidal cementite in ductile cast iron. Int. J. Mater. Prod. Technol., 2005, 24(1–4): 375.