Influence of multi-stage heat treatment on the microstructure and mechanical properties of TC21 titanium alloy

Abstract

Duplex-structured TC21 alloy samples were first solution-treated at a higher temperature in the α + β region (940°C) with furnace cooling (FC), air cooling (AC), and water cooling (WC), followed by a second-stage solution treatment at a lower temperature in the α + β region (900°C), and then finally aged at 590°C. The effects of the morphology and quantity of α phases on the structure and properties of the TC21 alloy after the different heat treatments were analyzed. The in-situ tensile deformation process and crack propagation behavior were observed using scanning electron microscopy (SEM). The quantity of equiaxed α phases as well as the thickness of lamellar α phases reduced, the tensile strength increased firstly and then decreased, the elongation decreased with the increasing cooling rate after the first-stage solution treatment. The amount and size of lamellar α phases increased after the second-stage solution treatment because of sufficient diffusion of the alloying elements, thereby leading to increased tensile strength. The amount of dispersed α phases increased after the third-stage aging treatment owing to the increase in the nucleation rate, resulting in a noteworthy strengthening effect. After the third-stage aging treatment, the first-stage FC sample exhibited better mechanical properties because it contained more equiaxed α and β_trans phases than the first-stage AC and WC samples.

Keywords

multi-stage heat treatment / titanium alloy / in-situ tension / microstructure / mechanical properties

References

[1] Ustundag M, Varol R. Comparison of a commercial powder and a powder produced from Ti-6Al-4V chips and their effects on compacts sintered by the sinter-HIP method. Int. J. Miner. Metall. Mater., 2019, 26(7): 878.

[2] Karkalos NE, Galanis NI, Markopoulos AP. Surface roughness prediction for the milling of Ti-6Al-4V ELI alloy with the use of statistical and soft computing techniques. Measurement, 2016, 90, 25.

[3] X. Wen, M.P. Wang, C.W. Huang, Y.B. Tan, M. Lei, Y.L. Liang, and X. Cai, Effect of microstructure on tensile properties, impact toughness and fracture toughness of TC21 alloy, Mater. Des., 180(2019), art. No. 107898.

[4] Zhang S, Liang YL, Xia QF, Ou MG. Study on tensile deformation behavior of TC21 titanium alloy. J. Mater. Eng. Perform., 2019, 28(3): 1581.

[5] Hou ZM, Zhao YQ, Zeng WD, Mao XN, Lei WG, Zhang PS. Effect of heat treatment on the microstructure development of TC21 alloy. Rare Met. Mater. Eng., 2017, 46(8): 2087.

[6] Sarma J, Kumar R, Sahoo AK, Panda A. Enhancement of material properties of titanium alloys through heat treatment process: A brief review. Mater. Today: Proc., 2020, 23, 561.

[7] Liu WY, Lin YH, Chen YH, Shi TH, Singh A. Effect of different heat treatments on microstructure and mechanical properties of Ti6Al4V titanium alloy. Rare Met. Mater. Eng., 2017, 46(3): 634.

[8] Shi ZF, Guo HZ, Han JY, Yao ZK. Microstructure and mechanical properties of TC21 titanium alloy after heat treatment. Trans. Nonferrous Met. Soc. China, 2013, 23(10): 2882.

[9] Shi JH. Study on Heat-Treatment and Cold-Forging Process of TC16 Titanium Alloy, 2012, Dalian, Dalian University of Technology, 61 [Dissertation]

[10] Wang GX. Effect of heat treatment on the microstructure and properties of TC21 titanium alloy. J. Henan Sci. Technol., 2014, 22(11): 56.

[11] Wu C, Zhan M. Microstructural evolution, mechanical properties and fracture toughness of near β titanium alloy during different solution plus aging heat treatments. J. Alloys Compd., 2019, 805, 1144.

[12] Hou ZM, Mao XN, Zhao YQ, Zhang PS, Lei WG, Yu LL. Effect of β solution treatment on morphology and mechanical properties of TC21 alloy. Chin. J. Nonferrous Met., 2013, 23(Suppl. 1): s480.

[13] Zhang XD, Wiezorek JMK, Baeslack WA, Evans DJ, Fraser HL. Precipitation of ordered α₂ phase in Ti-6-22-22 alloy. Acta Mater., 1998, 46(13): 4485.

[14] Ou MG, Xia QF, Song HC, Liang YL. Effect of different cooling rates on microstructure and mechanical properties of TC4 alloy. Rare Met. Mater. Eng., 2019, 48(2): 638.

[15] Hou ZM, Mao XN, Lei WG, Lu YF, Zhang PS, Han D. Effect of solution treatment on morphology of near β forged TC21 alloy. Chin. J. Nonferrous Met, 2010, 20(Suppl. 1): s581.

[16] Li Z, Kang SP, Yu HH, Jiang H, Qiu DT, Yu T, Li ZH. The microstructural evolution of TC4 alloy during cooling from the solution temperature. J. Shenyang Aerosp. Univ., 2014, 31(5): 44.

[17] Dang W, Xue XY, Kou HC, Chang H, Li JS, Zhang FS, Zhou L. Phase and microstructure of TC21 titanium alloy during slow cooling. J. Aeronaut. Mater., 2010, 30(3): 19.

[18] Guo P, Zhao YQ, Zeng WD, Hong Q, Mao XN, Jia WJ, Zhao YQ. Effect of heat treatment in α+β zone on fracture toughness of TC4-DT titanium alloy. Rare Met. Mater. Eng., 2018, 47(4): 1221.

[19] Castany P, Diologent F, Rossoll A, Despois J-F, Bezençon C, Mortensen A. Influence of quench rate and microstructure on bendability of AA6016 aluminum alloys. Mater. Sci. Eng. A, 2013, 559, 558.

[20] Illarionov AG, Popov AA, Leder MO, Vodolazskii FV, Zhloba AV. Formation of structure, phase composition and properties in a two-phase titanium alloy upon variation of the temperature and rate parameters of heat treatment. Met. Sci. Heat Treat, 2015, 56(9–10): 499.

[21] Tan GY, Wu YF, Yang G, Sun YH, Yue YC. Effect of solution aging treatment on impact property of TC4 titanium alloy. Foundry Technol., 2016, 37(5): 902.

[22] Maury N, Denand B, Dehmas M, Archambeau-Mirguet C, Delfosse J, Aeby-Gautier E. Influence of the ageing conditions and the initial microstructure on the precipitation of α phase in Ti-17 alloy. J. Alloys Compd., 2018, 763, 446.

[23] Ge P, Zhou W, Zhao YQ, Zhou L. Aging characteristics of new metastable beta titanium alloy. Trans. Nonferrous Met. Soc. China, 2007, 17, s88.

[24] Gao XX, Zeng WD, Zhang SF, Wang QJ. A study of epitaxial growth behaviors of equiaxed alpha phase at different cooling rates in near alpha titanium alloy. Acta Mater., 2017, 122, 298.

[25] Xu JW, Zeng WD, Jia ZQ, Sun X, Zhou JH. Microstructure coarsening behavior of Ti-17 alloy with equiaxed alpha during heat treatment. J. Alloys Compd., 2015, 618, 343.

[26] Huang CW, Zhao YQ, Xin SW, Tan CS, Zhou W, Li Q, Zeng WD. High cycle fatigue behavior of Ti-5Al-5Mo-5V-3Cr-1Zr titanium alloy with lamellar microstructure. Mater. Sci. Eng. A, 2017, 682, 107.

[27] Shao H, Zhao YQ, Ge P, Zeng WD. Crack initiation and mechanical properties of TC21 titanium alloy with equiaxed microstructure. Mater. Sci. Eng. A, 2013, 586, 215.

[28] Xiong Y, Xiao GQ. Effect of heat treatment on microstructure and mechanical properties of TC21 titanium alloy. Foundry Technol., 2015, 36(3): 638.

[29] Tan CS, Sun QY, Xiao L, Zhao YQ, Sun J. Characterization of deformation in primary α phase and crack initiation and propagation of TC21 alloy using in-situ SEM experiments. Mater. Sci. Eng. A, 2018, 725, 33.

[30] Banerjee D, Williams JC. Perspectives on titanium science and technology. Acta Mater., 2013, 61(3): 844.

[31] Savage MF, Tatalovich J, Zupan M, Hemker KJ, Mills MJ. Deformation mechanisms and microtensile behavior of single colony Ti-6242Si. Mater. Sci. Eng. A, 2001, 319–321, 398.

[32] Suri S, Viswanathan GB, Neeraj T, Hou D-H, Mills MJ. Room temperature deformation and mechanisms of slip transmission in oriented single-colony crystals of an α/β titanium alloy. Acta Mater., 1999, 47(3): 1019.

[33] Li C, Chen J, Li W, Ren YJ, He JJ, Song ZX. Effect of heat treatment variations on the microstructure evolution and mechanical properties in a β metastable Ti alloy. J. Alloys Compd., 2016, 684, 466.

[34] Liu AJ, Wang L, Dai HX. Effect of heat treatment on the microstructure and dynamic behavior of Ti-10V-2Fe-3Al alloy. Mater. Sci. Forum, 2018, 910, 155.

[35] Liu JY, Pu X, Sun C, Zha WS. Effects of hydrides on fracture behavior of N18 zirconium alloy during in situ tension. Rare Met. Mater. Eng., 2017, 46(3): 711.

[36] Zeng LY, Hong Q, Zhao YQ, Qi YL. Thermal stability of one type of near α titanium alloy Ti-600. Mater. Res. Innovations, 2014, 18(Suppl. 4): 207.

[37] Liu HJ, Cao R, He H, Zhang J, Chen JH. Notch sensitivity of K418 alloy. Chin. J. Rare Met., 2010, 34(5): 699.

[38] Wang T, Guo HZ, Wang YW, Peng XN, Zhao Y, Yao ZK. The effect of microstructure on tensile properties, deformation mechanisms and fracture models of TG6 high temperature titanium alloy. Mater. Sci. Eng. A, 2011, 528(6): 2370.

[39] Guo S, Meng QK, Liao GY, Hu L, Zhao XQ. Microstructural evolution and mechanical behavior of metastable β-type Ti-25Nb-2Mo-4Sn alloy with high strength and low modulus. Prog. Nat. Sci: Mater. Int., 2013, 23(2): 174.

[40] Liu HJ, Feng XL. Study of diffusion bonding of fine grain TC21 titanium alloy. Rare Met. Mater. Eng., 2009, 38(9): 1509.

[41] Lütjering G. Influence of processing on microstructure and mechanical properties of (α+β) titanium alloys. Mater. Sci. Eng. A, 1998, 243(1–2): 32.