Preparing high-purity iron by direct reduction‒smelting separation of ultra-high-grade iron concentrate

Abstract

A new process for preparing high-purity iron (HPI) was proposed, and it was investigated by laboratory experiments and pilot tests. The results show that under conditions of a reduced temperature of 1075°C, reduced time of 5 h, and CaO content of 2.5wt%, a DRI with a metallization rate of 96.5% was obtained through coal-based direct reduction of ultra-high-grade iron concentrate. Then, an HPI with a Fe purity of 99.95% and C, Si, Mn, and P contents as low as 0.0008wt%, 0.0006wt%, 0.0014wt%, and 0.0015wt%, respectively, was prepared by smelting separation of the DRI using a smelting temperature of 1625°C, smelting time of 45 min, and CaO content of 9.3wt%. The product of the pilot test with a scale of 0.01 Mt/a had a lower impurity content than the Chinese industry standard. An HPI with a Fe purity of 99.98wt% can be produced through the direct reduction?smelting separation of ultra-high-grade iron concentrate at relatively low cost. The proposed process shows a promising prospect for application in the future.

Keywords

ultra-high-grade iron concentrate / high-purity iron / coal-based direct reduction / smelting separation / pilot test

References

[1] Wang HJ, Rong Z, Xiang L, Qiu ST, Li JX, Dong TL. Effect of decarburization annealing temperature and time on the carbon content, microstructure, and texture of grain-oriented pure iron. Int. J. Miner. Metall. Mater, 2017, 24, 393.

[2] Biswas RK, Begum DA. Study of kinetics of forward extraction of Fe(III) from chloride medium by di-2-ethylhexyl phosphoric acid in kerosene using the single drop technique. Hydrometallurgy, 1999, 54, 1.

[3] Abiko K. Why do we study ultra-high purity base metals. Mater. Trans., JIM, 2000, 41, 233.

[4] Prokhodtseva A, Décamps B, Schäublin R. Comparison between bulk and thin foil ion irradiation of ultra high purity Fe. J. Nucl. Mater, 2013, 442, S786.

[5] Matsumiya H, Kuromiya M, Hiraide M. Matrix-precipitation for the determination of trace impurities in high-purity iron. ISIJ Int, 2013, 53, 81.

[6] Kekesi T, Mimura K, Isshiki M. Ultra-high purification of iron by anion-exchange in hydrochloric acid solutions. Hydrometallurgy, 2002, 63, 1.

[7] Murakami K, Nishida N, Osamura K, Tomota Y, Suzuki T. Plasma nitridation of aluminized high purity iron. Acta Mater, 2005, 53, 2563.

[8] Uchikoshi M, Imaizumi J, Shibuya H, Kékesi T, Mimura K, Isshiki M. Production of semiconductor grade high-purity iron. Thin Solid Films, 2004, 461, 94.

[9] Saitoh T, Sakurai K, Hiraide M. Thermoresponsive polymer-mediated extraction for graphite furnace atomic absorption spectrometric determination of trace metals in high purity iron. Microchem. J, 2018, 139, 410.

[10] Uchikoshi M, Shibuya H, Kekesi T, Mimura K, Isshiki M. Mass production of high-purity iron using anion-exchange separation and plasma arc melting. Metall. Mater. Trans. B, 2009, 40, 615.

[11] Takaki S, Abiko K. Ultra-purification of electrolytic iron by cold-crucible induction melting and induction-heating floating-zone melting in ultra-high vacuum. Maer Trans., JM, 2000, 41, 2.

[12] Faudot F, Rouchaud JC, Debove L, Fedoroff M, Bigot J. Elaboration of high purity iron (RRR>4000) by horizontal zone melting-attempts for chemical characterization. J. Phys. Chem. Solids, 1987, 48, 761.

[13] Tudu K, Pal S, Mandre NR. Comparison of selective flocculation of low grade goethitic iron ore fines using natural and synthetic polymers and a graft copolymer. Int. J. Miner. Metall. Mater, 2018, 25, 498.

[14] Bada SO, Afolabi AS, Makhula MJ. Effect of reverse flotation on magnetic separation concentrates. Int. J. Miner. Metall. Mater, 2012, 19, 669.

[15] Ye QX, Zhu HB, Zhang LB, Ma J, Zhou L, Liu P, Chen J, Chen G, Peng JH. Preparation of reduced ironpowder using combined distribution of wood-charcoal by microwave heating. J. Alloys Compd, 2014, 613, 102.

[16] Cho YI, Kim BH, Kim SJ, Yun JJ, Lee H, Park SH, Jung SC. Preparation and characterization of zero valent iron powders via transfer type reductor using iron oxide from the acid regeneration process. Adv. Powder Technol, 2013, 24, 858.

[17] Li WF, Zhan J, Fan YQ, Wei C, Zhang CF, Wang JY. J.Y. Research and industrial application of a process for direct reduction of molten high-lead smelting slag. JOM, 2017, 69, 784.

[18] Tang J, Chu MS, Li F, Tang YT, Liu ZG, Xin XX. Reduction mechanism of high-chromium vanadium-titanium magnetite pellets by H₂-CO-CO₂ gas mixtures. Int. J. Miner. Metall. Mater, 2015, 22, 562.

[19] He SY, Sun HY, Hu CQ, Li J, Zhu QS, Li HZ. Direct reduction of fine iron ore concentrate in a conical fluidized bed. Powder Technol, 2017, 313, 161.

[20] Li F, Chu MS, Tang J, Liu ZG, Feng C, Tang YT. Swelling behavior of high-chromium, vanadium-bearing titanomagnetite pellets in H₂-CO-CO₂ gas mixtures. JOM, 2017, 69, 1751.

[21] Zhou W, Xie B, Tan WF, Diao J, Zhang X, Li HY. W.F Non-isothermal crystallization kinetics of spinels in vanadium slag with high CaO content. JOM, 2016, 68, 2520.

[22] Sun HY, Wang JS, Han YH, She XF, Xue QG. Reduction mechanism of titanomagnetite concentrate by hydrogen. Int. J. Miner. Process, 2013, 125, 122.

[23] Zhao YQ, Sun TC, Zhao HY, Chen C, Wang XP. Effect of reductant type on the embedding direct reduction of beach titanomagnetite concentrate. Int. J. Miner. Metall. Mater, 2019, 26, 152.

[24] Park E, Ostrovski O. Reduction of titania-ferrous ore by carbon monoxide. ISIJ Int, 2003, 43, 1316.

[25] Standards Press China, GB/T 9971-2017. Pure Iron Raw Material, 2017 1.