Microstructure and properties of a wear resistant Al-25Si-4Cu-1Mg coating prepared by supersonic plasma spraying

Abstract

A high content silicon aluminum alloy (Al-25Si-4Cu-1Mg) coating was prepared on a 2A12 aluminum alloy by supersonic plasma spraying. The morphology and microstructure of the coating were observed and analyzed. The hardness, elastic modulus, and bonding strength of the coating were measured. The wear resistance of the coating and 2A12 aluminum alloy was studied by friction and wear test. The results indicated that the coating was compact and the porosity was only 1.5%. The phase of the coating was mainly composed of α-Al and β-Si as well as some hard particles (Al₉Si, Al_3.21Si_0.47, and CuAl₂). The average microhardness of the coating was HV 242, which was greater than that of 2A12 aluminum alloy (HV 110). The wear resistance of the coating was superior to 2A12 aluminum alloy. The wear mechanism of the 2A12 aluminum alloy was primarily adhesive wear, while that of the coating was primarily abrasive wear. Therefore, it is possible to prepare a high content silicon aluminum alloy coating with good wear resistance on an aluminum alloy by supersonic plasma spraying.

Keywords

coating / high silicon aluminum alloy / microstructure / mechanical properties / wear resistance

References

[1] Hou LG, Cui CL, Zhang JS. Optimizing microstructures of hypereutectic Al-Si alloys with high Fe content via spray forming technique. Mater. Sci. Eng. A, 2010, 527(23): 6400.

[2] Du FM, Li CD, Mi ZT, Shen Y, Huang RX, Han XG, Dong Y, Xu JJ. Anti-wear property of aluminum-silicon alloy treated by chemical etching, mechanical honing and laser finishing. Materials, 2019, 12(8): 1273.

[3] Lawrynowicz D, Liang X, Srivatsan TS, Lavernia EJ. Processing, microstructure and fracture behaviour of a spray-atomized and deposited nickel aluminide intermetallic. J. Mater. Sci., 1998, 33(6): 1661.

[4] Y.G. Chen, H. Yang, B.Q. Zhang, Y.L. Liu, J.C. Yin, W. Wei, and Y. Zhong, A novel restraint spraying-conform process for manufacturing hypereutectic Al-Si alloy with enhanced properties, Mater. Res. Express, 4(2017), No. 2, art. No. 026502.

[5] Hou LG, Cai YH, Cui H, Zhang JS. Microstructure evolution and phase transformation of traditional cast and spray-formed hypereutectic aluminium-silicon alloys induced by heat treatment. Int. J. Miner. Metall. Mater., 2010, 17(3): 297.

[6] Y.S. Niu, J.C. Yin, Y.L. Liu, B.Q. Zhang, Y.F. Li, Y.G. Chen, and Y. Zhong, Microstructure, mechanical properties and wear behaviour of Al-20Si-3Fe alloy prepared by spray Conform, Mater. Res. Express, 6(2019), No. 8, art. No. 086578.

[7] Cai ZY, Zhang C, Wang RC, Peng CQ, Qiu K, Feng Y. Preparation of Al-Si alloys by a rapid solidification and powder metallurgy route. Mater. Des., 2015, 87, 996.

[8] M.L. Dong, X.F. Cui, B.W. Lu, X.R. Feng, G. Jin, L. Shi, and H.D. Wang, Accelerated diffusion of carbon and grain refinement of vacuum carburized layer by La ion implantation, J. Alloys Compd., 814(2020), art. No. 152308.

[9] Su J, Kang JJ, Yue W, Ma GZ, Fu ZQ, Zhu LN, She DS, Wang HD, Wang CB. Comparison of tribological behavior of Fe-based metallic glass coatings fabricated by cold spraying and high velocity air fuel spraying. J. Non-Cryst. Solids, 2019, 522, 119582.

[10] Z.Y. Piao, B.S Xu, H.D Wang, and X.X. Yu, Rolling contact fatigue behavior of thermal-sprayed coating: A review, Crit. Rev. Solid State Mater. Sci. (2019). DOI: https://doi.org/10.1080/10408436.2019.1671798

[11] Chen CM, Yang CC, Chao CG. A novel method for net-shape forming of hypereutectic Al-Si alloys by thixocasting with powder preforms. J. Mater. Process. Technol., 2005, 167(1): 103.

[12] Zhao JF, Yuan XG. Densification of spray-formed Al-22%Si alloy. J. Mudanjiang Univ., 2017, 26(11): 148.

[13] Jia YD, Cao FY, Ma P, Scudino S, Eckert J, Sun JF, Wang G. Microstructure and thermal conductivity of hyper-eutectic Al-high Si produced by casting and spray deposition. J. Mater. Res., 2016, 31(19): 2948.

[14] Wang F, Ma YJ, Zhang ZY, Cui XH, Jin YS. A comparison of the sliding wear behavior of a hypereutectic Al-Si alloy prepared by spray-deposition and conventional casting methods. Wear, 2004, 256(3–4): 342.

[15] Yang FL, Zhang W, Yi DQ, Wang RC, Chen ZK. Microstructure analysis of rapidly solidified Al-40Si alloy fabricated by spray deposition. Powder Metall. Technol., 2006, 24(3): 166.

[16] Rabinowicz E. Friction and Wear of Materials, 1965, New York, John Wiley & Sons, Inc.

[17] Frérot L, Aghrotababaei R, Molinari JF. A mechanistic understanding of the wear coefficient: From single to multiple asperities contact. J. Mech. Phys. Solids, 2018, 114, 172.

[18] Si HL. Study on Heat Treatment and Wear Resistance of Spray Formed High Silicon Aluminum Alloy, 2008, Harbin, Harbin University of Science and Technology [Dissertation]