Temperature-dependent evolution of oxide inclusions during heat treatment of stainless steel with yttrium addition

Abstract

The evolution of oxide inclusions during isothermal heating of 18Cr-8Ni stainless steel with yttrium addition at temperatures of 1273 to 1573 K was investigated systematically. Homogeneous spherical Al-Y-Si(-Mn-Cr) oxide inclusions were observed in as-cast steel. After heating, most of the homogeneous inclusions were transformed into heterogeneous inclusions with Y-rich and Al-rich parts, even though some homogeneous oxide particles were still observed at 1273 and 1573 K. With the increase in heating temperature, more large-sized inclusions were formed. The shape of the inclusions also changed from spherical to irregular. The maximum transformation temperature of inclusions was determined to be 1373 K. The evolution mechanism of inclusions during heating was proposed to be the combined effect of the (i) internal transformation of inclusions due to the crystallization of glassy oxide and (ii) interfacial reaction between inclusions and steel matrix. Meanwhile, the internal transformation of inclusions was considered to be the main factor at heating temperatures less than 1473 K.

Keywords

stainless steel / rare earth metals / oxide inclusions / heating temperature

References

[1] Yang SF, Wang QQ, Zhang LF, Li JS, Peaslee K. Formation and modification of MgO·Al₂O₃-based inclusions in alloy steels. Metall. Mater. Trans. B, 2012, 43(4): 731.

[2] Park JH, Todoroki H. Control of MgO·Al₂O₃ spinel inclusions in stainless steels. ISIJ Int., 2010, 50(10): 1333.

[3] Choi JY, Kim SK, Kang YB, Lee HG. Compositional evolution of oxide inclusions in austenitic stainless steel during continuous casting. Steel Res. Int., 2015, 86(3): 284.

[4] Park JH, Lee SB, Kim DS. Inclusion control of ferritic stainless steel by aluminum deoxidation and calcium treatment. Metall. Mater. Trans. B, 2005, 36(1): 67.

[5] Gu C, Bao YP, Gan P, Wang M, He JS. Effect of main inclusions on crack initiation in bearing steel in the very high cycle fatigue regime. Int. J. Miner. Metall. Mater., 2018, 25(6): 623.

[6] Wang R, Bao YP, Yan ZJ, Li DZ, Kang Y. Comparison between the surface defects caused by Al₂O₃ and TiN inclusions in interstitial-free steel auto sheets. Int. J. Miner. Metall. Mater., 2019, 26(2): 178.

[7] Vahed A, Kay DAR. Thermodynamics of rare earths in steelmaking. Metall. Trans. B, 1976, 7(3): 375.

[8] Waudby PE. Rare earth additions to steel. Int. Met. Rev., 1978, 23(1): 74.

[9] Li QL, Zhang HR, Gao M, Li JP, Tao TX, Zhang H. Mechanisms of reactive element Y on the purification of K4169 superalloy during vacuum induction melting. Int. J. Miner. Metall. Mater., 2018, 25(6): 696.

[10] Gao JZ, Fu PX, Liu HW, Li DZ. Effects of rare earth on the microstructure and impact toughness of H13 steel. Metals, 2015, 5(1): 383.

[11] Lan J, He JJ, Ding W, Wang QD, Zhu YP. Effect of rare earth metals on the microstructure and impact toughness of a cast 0.4C-5Cr-1.2Mo-1.0V steel. ISIJ Int., 2000, 40(12): 1275.

[12] Kim ST, Jeon SH, Lee IS, Park YS. Effects of rare earth metals addition on the resistance to pitting corrosion of super duplex stainless steel—Part 1. Corros. Sci., 2010, 52(6): 1897.

[13] Kwon SK, Park JS, Park JH. Influence of refractory-steel interfacial reaction on the formation behavior of inclusions in Ce-containing stainless steel. ISIJ Int., 2015, 55(12): 2589.

[14] Kim SJ, Ryu KM, Oh MS. Addition of cerium and yttrium to ferritic steel weld metal to improve hydrogen trapping efficiency. Int. J. Miner. Metall. Mater., 2017, 24(4): 415.

[15] Katsumata A, Todoroki H. Effect of rare earth metal on inclusion composition in molten stainless steel. Iron Steelmaker, 2002, 29(7): 51.

[16] Dan T, Gunji K. Deoxidation Characteristics and shape modification of deoxidation products with Al-Ce and Al-Y complex deoxidizers. Tetui-tto-Hagant, 1982, 68(14): 1915.

[17] Li YD, Liu CJ, Zhang TS, Jiang MF, Peng C. Inclusions modification in heat resistant steel containing rare earth elements. Ironmaking Steelmaking, 2018, 45(1): 76.

[18] Li YD, Liu CJ, Zhang TS, Jiang MF, Peng C. Liquid inclusions in heat-resistant steel containing rare earth elements. Metall. Mater. Trans. B, 2017, 48(2): 956.

[19] Nabeel M, Karasev A, Jönsson P. Formation and growth mechanism of clusters in liquid REM-alloyed stainless steels. ISIJ Int., 2015, 55(11): 2358.

[20] Bi YY, Karasev AV, Jönsson PG. Three dimensional evaluations of REM clusters in stainless steel. ISIJ Int., 2014, 54(6): 1266.

[21] Takahashi I, Sakae T, Yoshida T. Changes of the nonmetallic inclusion by heating. Tetsu-to-Hagané, 1967, 53(3): 350.

[22] Shibata H, Tanaka T, Kimura K, Kitamura S. Composition change in oxide inclusions of stainless steel by heat treatment. Ironmaking Steelmaking, 2010, 37(7): 522.

[23] Shibata H, Kimura K, Tanaka T, Kitamura SY. Mechanism of change in chemical composition of oxide inclusions in Fe-Cr Alloys deoxidized with Mn and Si by heat treatment at 1473 K. ISIJ Int., 2011, 51(12): 1944.

[24] Ren Y, Zhang LF, Pistorius PC. Transformation of oxide inclusions in type 304 stainless steels during heat treatment. Metall. Mater. Trans. B, 2017, 48(5): 2281.

[25] Li MG, Matsuura H, Tsukihashi F. Evolution of Al-Ti oxide inclusion during isothermal heating of Fe-Al-Ti Alloy at 1573 K (1300°C). Metall. Mater. Trans. B, 2017, 48(3): 1915.

[26] Li MG, Matsuura H, Tsukihashi F. Time-dependent evolution of Ti-bearing oxide inclusions during isothermal holding at 1573 K (1300°C). Metall. Mater. Trans. A, 2019, 50(2): 863.

[27] Zou XD, Zhao DP, Sun JC, Wang C, Matsuura H. An integrated study on the evolution of inclusions in EH36 shipbuilding steel with Mg addition: From casting to welding. Metall. Mater. Trans. B, 2018, 49(2): 481.

[28] Zou XD, Sun JC, Matsuura H, Wang C. In situ observation of the nucleation and growth of ferrite laths in the heat-affected zone of EH36-Mg shipbuilding steel subjected to different heat inputs. Metall. Mater. Trans. B, 2018, 49(5): 2168.

[29] Yan JB, Gao YM, Liang L, Ye ZZ, Li YF, Chen W, Zhang JJ. Effect of yttrium on the cyclic oxidation behaviour of HP40 heat-resistant steel at 1373 K. Corros. Sci., 2011, 53(1): 329.

[30] Chen L, Ma XC, Wang LM, Ye XN. Effect of rare earth element yttrium addition on microstructures and properties of a 21Cr-11Ni austenitic heat-resistant stainless steel. Mater. Des., 2011, 32(4): 2206.

[31] Murakami Y, Yamamoto H. Phase equilibria in Al₂O₃-Y₂O₃-SiO₂ system and phase separation and crystallization behavior of glass. J. Ceram. Soc. Jpn., 1991, 99(1147): 215.

[32] Ahmad S, Ludwig T, Herrmann M, Mahmoud MM, Lippmann W, Seifert HJ. Phase evaluation during high temperature long heat treatments in the Y₂O₃-Al₂O₃-SiO₂ system. J. Eur. Ceram. Soc., 2014, 34(15): 3835.

[33] Ahmad S, Herrmann M, Mahmoud MM, Leiste H, Lippmann W, Seifert HJ. Crystallisation studies of RE₂O₃-Al₂O₃-SiO₂ glasses under long heat-treatment conditions. J. Alloys Compd., 2016, 688, 762. Part B

[34] Kolitsch U, Seifert HJ, Ludwig T, Aldinger F. Phase equilibria and crystal chemistry in the Y₂O₃-Al₂O₃-SiO₂ system. J. Mater. Res., 1999, 14(2): 447.

[35] Harrysson R, Vomacka P. Glass formation in the system Y₂O₃-Al₂O₃-SiO₂ under conditions of laser melting. J. Eur. Ceram. Soc., 1994, 14(4): 377.

[36] Herrmann M, Lippmann W, Hurtado A. Y₂O₃-Al₂O₃-SiO₂-based glass-ceramic fillers for the laser-supported joining of SiC. J. Eur. Ceram. Soc., 2014, 34(8): 1935.

[37] Wisniewski W, Keshavarzi A, Zscheckel T, Rüssel C. EBSD-based phase identification in glass-ceramics of the Y₂O₃-Al₂O₃-SiO₂ system containing α-and β-Y₂Si₂O₇. J. Aloys. Compd., 2017, 699, 832.

[38] Han QY, Xiang CX, Dong YC, Yang SF, Chen D. Equilibria between the rare earth elements, oxygen and sulfur, in molten iron. Metall. Mater. Trans. B, 1988, 19(3): 409.

[39] D.P. Zhan, G.X. Qiu, Z.H. Jiang, and H.S. Zhang, Effect of yttrium and titanium on inclusions and the mechanical properties of 9Cr RAFM steel fabricated by vacuum melting, Steel Res. Int., 88(2017), No. 12, art. No. 1700159.

[40] Ishii F, Banya S. Equilibrium between yttrium and oxygen in liquid iron and nickel. ISIJ Int., 1995, 35(3): 280.

[41] Seo WG, Han WH, Kim JS, Pak JJ. Deoxidation equilibria among Mg, Al and O in liquid iron in the presence of MgO·Al₂O₃ spinel. ISIJ Int., 2003, 43(2): 201.