Microstructure and mechanical properties of high-strength low alloy steel by wire and arc additive manufacturing

Abstract

A high-building multi-directional pipe joint (HBMDPJ) was fabricated by wire and arc additive manufacturing using high-strength low-alloy (HSLA) steel. The microstructure characteristics and transformation were observed and analyzed. The results show that the forming part includes four regions. The solidification zone solidifies as typical columnar crystals from a molten pool. The complete austenitizing zone forms from the solidification zone heated to a temperature greater than 1100°C, and the typical columnar crystals in this zone are difficult to observe. The partial austenitizing zone forms from the completely austenite zone heated between Ac1 (austenite transition temperature) and 1100°C, which is mainly equiaxed grains. After several thermal cycles, the partial austenitizing zone transforms to the tempering zone, which consistes of fully equiaxed grains. From the solidification zone to the tempering zone, the average grain size decreases from 75 to 20 µm. The mechanical properties of HBMDPJ satisfies the requirement for the intended application.

Keywords

wire and arc additive manufacturing / high strength low alloy steel / microstructure / inclusions / fine grain ferrite / mechanical properties

References

[1] Herion S, de Oliveira JC, Packer JA, Christopoulos C, Gray MG. Castings in tubular structures—The state of the art. Proc. Inst. Civ. Eng. Struct. Build., 2010, 163(6): 403.

[2] Xia J, Jin H. Analysis of residual stresses and variation mechanism in dissimilar girth welded joints between tubular structures and steel castings. Int. J. Press. Vessels Pip., 2018, 165, 104.

[3] Liu JP, Wei J. Study on casting process of cast steel joints for buildings. Hot Working Technol., 2015, 44(5): 13.

[4] de Oliveira JC, Packer JA, Christopoulos C. Cast steel connectors for circular hollow section braces under inelastic cyclic loading. J. Struct. Eng., 2008, 134(3): 374.

[5] Lu LX. Discussion on application of cast-steel node in lager-span pipe truss architecture steel structure. Steel Constr., 2003, 18(5): 28.

[6] Ding DH, Pan ZX, Cuiuri D, Li HJ. Wire-feed additive manufacturing of metal components: Technologies, developments and future interests. Int. J. Adv. Manuf. Technol., 2015, 81(1–4): 465.

[7] Panchagnula JS, Simhambhatla S. Manufacture of complex thin-walled metallic objects using weld-deposition based additive manufacturing. Rob. Cimput. Integr. Manuf., 2018, 49, 194.

[8] Lei YY, Xiong J, Li R. Effect of inter layer idle time on thermal behavior for multi-layer single-pass thin-walled parts in GMAW-based additive manufacturing. Int. J. Adv. Manuf. Technol., 2018, 96(1–4): 1355.

[9] Kazanas P, Deherkar P, Almeida P, Lockett H, Williams S. Fabrication of geometrical features using wire and arc additive manufacture. J. Eng. Manuf., 2012, 226(6): 1042.

[10] Fachinotti VD, Cardona A, Baufeld B, der Biest OV. Finite-element modelling of heat transfer in shaped metal deposition and experimental validation. Acta. Mater, 2012, 60(19): 6621.

[11] Ge JG, Lin J, Lei YP, Fu H G. Location-related thermal history, microstructure, and mechanical properties of arc additively manufactured 2Cr13 steel using cold metal transfer welding. Mater. Sci. Eng. A, 2018, 715, 144.

[12] Asala G, Khan AK, Andersson J, Ojo OA. Microstructural analyses of ATI 718Plus produced by wire-arc additive manufacturing process. Metall. Mater. Trans. A, 2017, 48(9): 4211.

[13] Chen XH, Li J, Cheng X, He B, Wang HM, Huang Z. Microstructure and mechanical properties of the austenitic stainless steel 316L fabricated by gas metal arc additive manufacturing. Mater. Sci. Eng. A, 2017, 703, 567.

[14] Wang JF, Sun QJ, Wang H, Liu JP, Feng JC. Effect of location on microstructure and mechanical properties of additive layer manufactured Inconel 625 using gas tungsten arc welding. Mater. Sci. Eng. A, 2016, 676, 395.

[15] Rodrigues TA, Duarte V, Avila JA, Santos TG, Miranda RM, Oliveira JP. Wire and arc additive manufacturing of HSLA steel: Effect of thermal cycles on microstructure and mechanical properties. Addit. Manuf., 2019, 27, 440.

[16] Goldak J, Chakravarti A, Bibby M. A new finite element model for welding heat sources. Metall. Mater. Trans. B, 1984, 15(2): 299.

[17] D.S. Liu, Y.M. Lü, W.J. Zhou, H. Yang, and K. Yang, Numerical simulation of temperature field in TIG arc additive manufacturing based on ANSYS, Laser Optoelectron. Prog., 56(2019), No. 24, art. No. 241405.

[18] Jing YM, Zhang YS, Liang WK, Zheng XY, Li Y. Effect of heating rate on austenitization of 22MnB5 ultra high strength steel. Mater. Mech. Eng., 2016, 40(4): 80.

[19] Pu J, Yu SF, Li YY. Role of inclusions in flux aided backing submerged arc welding. J. Mater. Process. Technol., 2017, 240, 145.

[20] Guo AM, Li SR, Guo J, Li PH, Ding QF, Wu KM, He XL. Effect of zirconium addition on the impact toughness of the heat affected zone in a high strength low alloy pipeline steel. Mater. Charact., 2008, 59(2): 134.

[21] Zhang HQ. Metallics of Steel Melt Welded Joint, 2000, Beijing, China Machine Press, 301.

[22] Liu ZC, Ren HP, Ji YP. New Theory of Solid Phase Transition, 2015, Beijing, Science Press, 120.

[23] Cui ZQ, Qin YC. Metallography and Heat-Treatment, 2007, Beijing, China Machine Press, 175.