Mechanical characterization of Mg-B₄C nanocomposite fabricated at different strain rates

Abstract

Magnesium has wide application in industry. The main purpose of this investigation was to improve the properties of magnesium by reinforcing it using B₄C nanoparticles. The reinforced nanocomposites were fabricated using a powder compaction technique for 0, 1.5vol%, 3vol%, 5vol%, and 10vol% of B₄C. Powder compaction was conducted using a split Hopkinson bar (SHB), drop hammer (DH), and Instron to reach different compaction loading rates. The compressive stress-strain curves of the samples were captured from quasi-static and dynamic tests carried out using an Instron and split Hopkinson pressure bar, respectively. Results revealed that, to achieve the highest improvement in ultimate strength, the contents of B₄C were 1.5vol%, 3vol%, and 3vol% for Instron, DH, and SHB, respectively. These results also indicated that the effect of compaction type on the quasi-static strength of the samples was not as significant, although its effect on the dynamic strength of the samples was remarkable. The improvement in ultimate strength obtained from the quasi-static stress-strain curves of the samples (compared to pure Mg) varied from 9.9% for DH to 24% for SHB. The dynamic strength of the samples was improved (with respect to pure Mg) by 73%, 116%, and 141% for the specimens compacted by Instron, DH, and SHB, respectively. The improvement in strength was believed to be due to strengthening mechanisms, friction, adiabatic heating, and shock waves.

Keywords

powder compaction / B₄C / magnesium / strain rate / ultimate strength / sintering

References

[1] Nguyen QB, Gupta M. Improving compressive strength and oxidation resistance of AZ31B magnesium alloy by addition of nano-Al₂O₃ particulates and Ca. J. Compos. Mater., 2010, 44(7): 883.

[2] Gupta M, Lai MO, Saravanaranganathan D. Synthesis, microstructure and properties characterization of disintegrated melt deposited Mg/SiC composites. J. Mater. Sci., 2000, 35(9): 2155.

[3] Ahmed A, Neely AJ, Shankar K, Nolan P, Moricca S, Eddowes T. Synthesis, tensile testing, and microstructural characterization of nanometric SiC particulate-reinforced Al 7075 matrix composites. Metall. Mater. Trans. A, 2010, 41(6): 1582.

[4] Harichandran R, Selvakumar N. Effect of nano/micro B₄C particles on the mechanical properties of aluminium metal matrix composites fabricated by ultrasonic cavitation-assisted solidification process. Arch. Civ. Mech. Eng., 2016, 16(1): 147.

[5] Ganguly A, Sharma S, Papakonstantinou P, Hamilton J. Probing the thermal deoxygenation of graphene oxide using high-resolution in situ X-ray-based spectroscopies. J. Phys. Chem. C, 2011, 115(34): 17009.

[6] Khelifa I, Belmokhtar A, Berenguer R, Benyoucef A, Morallon E. New poly (o-phenylenediamine)/modified-clay nanocomposites: A study on spectral, thermal, morphological and electrochemical characteristics. J. Mol. Struct., 2019, 1178, 327.

[7] Daikh S, Zeggai FZ, Bellil A, Benyoucef A. Chemical polymerization, characterization and electrochemical studies of PANI/ZnO doped with hydrochloric acid and/or zinc chloride: Differences between the synthesized nanocomposites. J. Phys. Chem. Solids, 2018, 121, 78.

[8] Benyakhou S, Belmokhtar A, Zehhaf A, Benyoucef A. Development of novel hybrid materials based on poly (2-aminophenyl disulfide)/silica gel: preparation, characterization and electrochemical studies. J. Mol. Struct., 2017, 1150, 580.

[9] Rahmani K, Majzoobi GH. An investigation on SiC volume fraction and temperature on static and dynamic behavior of Mg-SiC nanocomposite fabricated by powder metallurgy. Modares Mech. Eng., 2018, 18(3): 361

[10] Abdollahi A, Alizadeh A, Baharvandi HR. Dry sliding tribological behavior and mechanical properties of Al2024-5wt%B4C nanocomposite produced by mechanical milling and hot extrusion. Mater. Des., 2014, 55, 471.

[11] Mohanty RM, Balasubramanian K, Seshadri SK. Boron carbide-reinforced alumnium 1100 matrix composites: fabrication and properties. Mater. Sci. Eng. A, 2008, 498(1–2): 42.

[12] Wang JZ, Qu XH, Yin HQ, Yi MJ, Yuan XJ. High velocity compaction of ferrous powder. Powder Technol., 2009, 192(1): 131.

[13] Gourdin WH. Dynamic consolidation of metal powders. Prog. Mater Sci., 1986, 30(1): 39.

[14] Faruqui AN, Manikandan P, Sato T, Mitsuno Y, Hokamoto K. Mechanical milling and synthesis of Mg-SiC composites using underwater shock consolidation. Met. Mater. Int., 2012, 18(1): 157.

[15] Majzoobi G H, Rahmani K, Atrian A. Temperature effect on mechanical and tribological characterization of Mg–SiC nanocomposite fabricated by high rate compaction. Materials Research Express, 2018, 5(1): 015046.

[16] Majzoobi GH, Rahmani K, Atrian A. An experimental investigation into wear resistance of Mg-SiC nanocomposite produced at high rate of compaction. J. Stress Anal., 2018, 3(1): 35

[17] Rahmani K, Majzoobi GH, Atrian A. A novel approach for dynamic compaction of Mg-SiC nanocomposite powder using a modified Split Hopkinson Pressure Bar. Powder Metall., 2018, 61(2): 164.

[18] Jiang QC, Wang HY, Ma BX, Wang Y, Zhao F. Fabrication of B4C particulate reinforced magnesium matrix composite by powder metallurgy. J. Alloys Compd., 2005, 386(1–2): 177.

[19] Aydin M, Koç R, Akkoyunlu A. Fabrication and characterisation of Mg-nano B₄C and B composites by powder metallurgy method. Adv. Mater. Process. Technol., 2015, 1(1–2): 181

[20] Aatthisugan I, Rose AR, Jebadurai DS. Mechanical and wear behaviour of AZ91D magnesium matrix hybrid composite reinforced with boron carbide and graphite. J. Magnesium Alloys, 2017, 5(1): 20.

[21] Kevorkijan V, Škapin SD. Mg/B₄C composites with a high volume fraction of fine ceramic reinforcement. Mater. Manuf. Processes, 2009, 24(12): 1337.

[22] Yao YT, Jiang L, Fu GF, Chen LQ. Wear behavior and mechanism of B4C reinforced Mg-matrix composites fabricated by metal-assisted pressureless infiltration technique. Trans. Nonferrous Metal. Soc. China, 2015, 25(8): 2543.

[23] K. Rahmani, G.H. Majzoobi, and A. Atrian, Simultaneous effects of strain rate and temperature on mechanical response of fabricated Mg-SiC nanocomposite, J. Compos. Mater., 2019, art. No. 0021998319864629.

[24] Majzoobi GH, Atrian A, Pipelzadeh MK. Effect of densification rate on consolidation and properties of Al7075-B₄C composite powder. Powder Metall., 2015, 58(4): 281.

[25] Tavoosi M, Karimzadeh F, Enayati MH, Heidarpour A. Bulk Al-Zn/Al₂O₃ nanocomposite prepared by reactive milling and hot pressing methods. J. Alloys Compd., 2009, 475(1–2): 198.

[26] Atrian A, Majzoobi GH, Enayati MH, Bakhtiari H. Mechanical and microstructural characterization of Al7075/SiC nanocomposites fabricated by dynamic compaction. Int. J. Miner. Metall. Mater., 2014, 21(3): 295.

[27] Majzoobi GH, Freshteh-Saniee F, Khosroshahi SFZ, Mohammadloo HB. Determination of materials parameters under dynamic loading. Part I: Experiments and simulations. Comput. Mater. Sci, 2010, 49(2): 192.

[28] Hassan SF, Gupta M. Effect of submicron size Al₂O₃ particulates on microstructural and tensile properties of elemental Mg. J. Alloys Compd., 2008, 457(1–2): 244.

[29] Mo ZQ, Liu YZ, Geng JJ, Wang T. The effects of temperatures on microstructure evolution and mechanical properties of B₄C-AA2024 composite strips prepared by semi-solid powder rolling. Mater. Sci. Eng. A, 2016, 652, 305.

[30] Sankaranarayanan S, Habibi MK, Jayalakshmi S, Ai KJ, Almajid A, Gupta M. Nano-AlN particle reinforced Mg composites: Microstructural and mechanical properties. Mater. Sci. Technol., 2015, 31(9): 1122.

[31] Wei CT, Vitali E, Jiang F, Du SW, Benson DJ, Vecchio KS, Thadhani NN, Meyers MA. Quasi-static and dynamic response of explosively consolidated metal-aluminum powder mixtures. Acta Mater., 2012, 60(3): 1418.

[32] Eisen WB, Ferguson BL, German RM, Iacocca R, Lee PW, Madan D, Moyer K, Sanderow H, Trudel Y. Powder Metal Technologies and Applications, 1998, USA, ASM International

[33] Yim D, Kim W, Praveen S, Jang MJ, Bae JW, Moon J, Kim E, Hong ST, Kim HS. Shock wave compaction and sintering of mechanically alloyed CoCrFeMnNi highentropy alloy powders. Mater. Sci. Eng. A, 2017, 708, 291.

[34] Williamson RL. Parametric studies of dynamic powder consolidation using a particle-level numerical model. J. Appl. Phys., 1990, 68(3): 1287.

[35] Meyers MA, Benson DJ, Olevsky EA. Shock consolidation: microstructurally-based analysis and computational modeling. Acta Mater., 1999, 47(7): 2089.

[36] Kondo KI, Soga S, Sawaoka A, Araki M. Shock compaction of silicon carbide powder. J. Mater. Sci., 1985, 20(3): 1033.

[37] Meyers MA. A mechanism for dislocation generation in shock-wave deformation. Scripta Metall., 1978, 12(1): 21.