Hydrogen embrittlement of X80 pipeline steel in H₂S environment: Effect of hydrogen charging time, hydrogen-trapped state and hydrogen charging–releasing–recharging cycles

Abstract

This study investigated the susceptibility of X80 pipeline steel to hydrogen embrittlement given different hydrogen pre-charging times and hydrogen charging–releasing–recharging cycles in H₂S environment. The fracture strain of the steel samples decreased with increasing hydrogen pre-charging time; this steel degradation could almost be recovered after diffusible hydrogen was removed when the hydrogen pre-charging time was <8 d. However, unrecoverable degeneration occurred when the hydrogen pre-charging time extended to 16–30 d. Moreover, nanovoid formation meant that the hydrogen damage to the steel under intermittent hydrogen pre-charging–releasing–recharging conditions was more serious than that under continuous hydrogen pre-charging conditions. This study illustrated that the mechanical degradation of steel is inevitable in an H₂S environment even if diffusible hydrogen is removed or visible hydrogen-induced cracking is neglected. Furthermore, the steel samples showed premature fractures and exhibited a hydrogen fatigue effect because the repeated entry and release of diffusible hydrogen promoted the formation of vacancies that aggregated into nanovoids. Our results provide valuable information on the mechanical degradation of steel in an H₂S environment, regarding the change rules of steel mechanical properties under different hydrogen pre-charging times and hydrogen charging–releasing–recharging cycles.

Keywords

high-strength steel / hydrogen embrittlement / corrosion / hydrogen diffusion

References

[1] Louthan MR Jr Caskey GR Jr Donovan JA, Rawl DE Jr. Hydrogen embrittlement of metals. Mater. Sci. Eng., 1972, 10, 357

[2] Bai PP, Zhou J, Luo BW, Zheng SQ, Chen CF. Roles of carbon dioxide and steam on the hydrogen embrittlement of 3Cr tube steel in synthetic natural gas environment. Corros. Eng Sci. Technol, 2018, 53, 1

[3] Koyama M, Akiyama E, Lee YK, Raabe D, Tsuzaki K. Overview of hydrogen embrittlement in high-Mn steels. Int. J. Hydrogen Energy, 2017, 42, 12706

[4] Kawashima A, Hashimoto K, Shimodaira S. Hydrogen electrode reaction and hydrogen embrittlement of mild steel in hydrogen sulfide solutions. Corrosion, 1976, 32, 321

[5] Berkowitz BJ, Horowitz HH. The role of H₂S in the corrosion and hydrogen embrittlement of steel. J. Electrochem. Soc, 1982, 129, 468

[6] Woodtli J, Kieselbach R. Damage due to hydrogen embrittlement and stress corrosion cracking. Eng Fail.Anal, 2000, 7, 427

[7] de Moraes FD, Bastian FL, Ponciano JA. Influence of dynamic straining on hydrogen embrittlement of UNS-G41300 and UNS-S31803 steels in a low H₂S concentration environment. Corros. Sci., 2005, 47, 1325

[8] Monnot M, Nogueira RP, Roche V, Berthomé G, Chauveau E, Estevez R, Mantel M. Sulfide stress corrosion study of a super martensitic stainless steel in H₂S sour environments: Metallic sulfides formation and hydrogen embrittlement. Appl. Surf. Sci., 2017, 394, 132

[9] Li SH, Chen CF, Liu YN, Yu HB, Wang XL. Influence of surface martensite layer on hydrogen embrittlement of Fe-Mn-C-Mo steels in wet H₂S environment. Int. J. Hydrogen Energy, 2018, 43, 16728

[10] Chu WY, Qiao LJ, Chen QZ, Gao KW. Fracture and Environment Induced Cracking, 2000, Beijing, Sciences Express, 106

[11] Hirth JP. Effects of hydrogen on the properties of iron and steel. Metall. Trans. A, 1980, 11, 861

[12] Takai K, Shoda H, Suzuki H, Nagumo M. Lattice defects dominating hydrogen-related failure of metals. Acta Mater, 2008, 56, 5158

[13] Neeraj T, Srinivasan R, Li J. Hydrogen embrittlement of ferritic steels: observations on deformation micro-structure, nanoscale dimples and failure by nanovoiding. Acta Mater., 2012, 60, 5160

[14] D.G. Xie, S.Z. Li, M. Li, Z.J. Wang, P. Gumbsch, J. Sun, E. Ma, and Z. Shan, Hydrogenated vacancies lock dislocations in aluminium, Nat. Commun., 7(2016), art. No. 13341.

[15] Hattori M, Suzuki H, Seko Y, Takai K. The role of hydrogen-enhanced strain-induced lattice defects on hydrogen embrittlement susceptibility of X80 pipeline steel. JOM, 2017, 69, 1375

[16] Wan L, Geng WT, Ishii A, Du JP, Mei QS, Ishikawa N, Kimizuka H, Ogata S. Hydrogen embrittlement controlled by reaction of dislocation with grain boundary in alpha-iron. Int. J. Plast, 2019, 112, 206

[17] Momotani Y, Shibata A, Terada D, Tsuji N. Effect of strain rate on hydrogen embrittlement in low-carbon martensitic steel. Int. J. Hydrogen Energy, 2017, 42, 3371

[18] Escobar D P, Depover T, Wallaert E, Duprez L, Verhaege M, Verbeken K. Thermal desorption spectroscopy study of the interaction between hydrogen and different microstructural constituents in lab cast Fe-C alloys. Corros. Sci, 2012, 65, 199

[19] Noh HS, Kang JH, Kim KM, Kim SJ. The effect of carbon on hydrogen embrittlement in stable Cr-Ni-Mn-N austenitic stainless steels. Corros. Sci, 2017, 124, 63

[20] Oriani RA. The diffusion and trapping of hydrogen in steel. Acta Metall, 1970, 18, 147

[21] Wang MQ, Akiyama E, Tsuzaki K. Effect of hydrogen on the fracture behavior of high strength steel during slow strain rate test. Corros. Sci, 2007, 49, 4081

[22] Kim WK, Koh SU, Yang BY, Kim KY. Effect of environmental and metallurgical factors on hydrogen induced cracking of HSLA steels. Corros. Sci, 2008, 50, 3336

[23] Takai K, Watanuki R. Hydrogen in trapping states innocuous to environmental degradation of high-strength steels. ISIJ Int, 2003, 43, 520

[24] Koyama M, Tasan CC, Akiyama E, Tsuzaki K, Raabe D. Hydrogen-assisted decohesion and localized plasticity in dual-phase steel. Acta Mater, 2014, 70, 174

[25] Doshida T, Takai K. Dependence of hydrogen-induced lattice defects and hydrogen embrittlement of cold-drawn pearlitic steels on hydrogen trap state, temperature, strain rate and hydrogen content. Acta Mater, 2014, 79, 93

[26] Moro I, Briottet L, Lemoine P, Andrieu E, Blanc C, Odemer G. Hydrogen embrittlement susceptibility of a high strength steel X80. Mater. Sci Eng. A, 2010, 527, 7252

[27] Zhu X, Li W, Zhao HS, Wang L, Jin XJ. Hydrogen trapping sites and hydrogen-induced cracking in high strength quenching & partitioning (Q&P) treated steel. Int. J. Hydrogen Energy, 2014, 39, 13031

[28] Kim SJ, Yun DW, Jung HG, Kim KY. Determination of hydrogen diffusion parameters of ferritic steel from electrochemical permeation measurement under tensile loads. J. Electrochem. Soc, 2014, 161, E173

[29] Huang F, Li XG, Liu J, Qu YM, Jia J, Du CW. Hydrogen-induced cracking susceptibility and hydrogen trapping efficiency of different microstructure X80 pipeline steel. J. Mater. Sci, 2011, 46, 715

[30] Koyama M, Akiyama E, Tsuzaki K. Effect of hydrogen content on the embrittlement in a Fe-Mn-C twinning-induced plasticity steel. Corros. Sci, 2012, 59, 277

[31] Chen YX, Zheng SQ, Zhou J, Wang PY, Chen LQ, Qi YM. Influence of H₂S interaction with prestrain on the mechanical properties of high-strength X80 steel. Int. J. Hydrogen Energy, 2016, 41, 10412

[32] Okonkwo PC, Shakoor RA, Soliman A, Mohammed AMA. Corrosion behavior of API X-80 steel in hydrogen sulfide environment at different temperatures. Corrosion 2016, 2016

[33] Shen K, Xu L, Guo Y, Shi J, Wang MQ. Effect of microstructure on hydrogen diffusion and notch tensile strength of large steel forging. Mater. Sci Eng. A, 2015, 628, 149

[34] Michler T, Lindner M, Eberle U, Meusinger J. Gangloff RP, Somerday BP. Assessing hydrogen embrittlement in automotive hydrogen tanks. Gaseous Hydrogen Embrittlement of Materials in Energy Technologies, 2012, Cambridge, Woodhead Publishing, 94

[35] Depover T, Verbeken K. The effect of TiC on the hydrogen induced ductility loss and trapping behavior of Fe-C-Ti alloys. Corros. Sci, 2016, 112, 308

[36] Qi YM, Luo HY, Zheng SQ, Chen CF, Wang DN. Effect of immersion time on the hydrogen content and tensile properties of A350LF2 steel exposed to hydrogen sulphide environments. Corros. Sci, 2013, 69, 164

[37] Kittel J, Smanio V, Fregonese M, Garnier L, Lefebvre X. Hydrogen induced cracking (HIC) testing of low alloy steel in sour environment: Impact of time of exposure on the extent of damage. Corros. Sci, 2010, 52, 1386

[38] Chu WY, Qiao LJ, Wang YB, Cheng YH. Quantitative study for sulfide stress corrosion cracking of tubular steel. Corrosion, 1999, 55, 667

[39] Hultquist G, Graham MJ, Smialek JL, Jönsson B. Hydrogen in metals studied by thermal desorption spectroscopy (TDS). Corros. Sci, 2015, 93, 324

[40] Kaneko M, Doshida T, Takai K. Changes in mechanical properties following cyclic prestressing of martensitic steel containing vanadium carbide in presence of nondiffusible hydrogen. Mater. Sci. Eng. A, 2016, 674, 375

[41] Vo D, Lipnitskii A, Nguyen T, Nguyen TK. Nitrogen trapping ability of hydrogen-induced vacancy and the effect on the formation of AlN in aluminum. Coatings, 2017, 7, 79

[42] Sugimoto H, Fukai Y. Hydrogen-induced superabundant vacancy formation by electrochemical methods in bcc Fe: Monte Carlo simulation. Scripta Mater., 2017, 134, 20

[43] Robertson IM, Sofronis P, Nagao A, Martin ML, Wang S, Gross DW, Nygren KE. Hydrogen embrittlement understood. Metall. Mater. Trans. A, 2015, 46, 2323

[44] Y. Tateyama and T. Ohno, Stability and clusterization of hydrogen-vacancy complexes in α-Fe: an ab initio study, Phys. Rev. B, 67(2003), No. 17, art. No. 174105.

[45] Wilsdorf HGF. The ductile fracture of metals: a micro-structural viewpoint. Mater. Sci. Eng., 1983, 59, 1

[46] Wilsdorf HGF. The role of glide and twinning in the final separation of ruptured gold crystals. Acta Metall, 1982, 30, 1247