Analysis of oxide layer structure in nitrided grain-oriented silicon steel

Abstract

The production of low-temperature reheated grain-oriented silicon steel is mainly based on the acquired inhibitor method. Due to the additional nitriding process, a high nitrogen content exists in the oxide layer, which changes the structure of the oxide layer. In this study, the structure of the surface oxide layer after nitriding was analyzed by scanning electron microscopy (SEM), electron back-scattered diffraction (EBSD), glow discharge spectrometry (GDS), and X-ray diffraction (XRD). The size and orientation of ferritic grains in the oxide layer were characterized, and the distribution characteristics of the key elements along the thickness direction were determined. The results show that the oxide layer of the steel sample mainly comprised particles of Fe2SiO4 and spherical and lamellar SiO2, and Fe4N and fcc-Fe phases were also detected. Moreover, the size and orientation of ferritic grains in the oxide layer were different from those of coarse matrix ferritic grains beneath the oxide layer; however, some ferritic grains exhibited same orientations as those in the neighboring matrix. Higher nitrogen content was detected in the oxide layer than that in the matrix beneath the oxide layer. The form of nitrogen enrichment in the oxide layer was analyzed, and the growth mechanism of ferritic grains during the oxide layer formation is proposed.

Keywords

grain-oriented silicon steel / decarburization annealing / oxide layer / ferritic grains / silica

References

[1] Eloot K, Dilewijns J, Standaert C, De Cooman BC. Evaluation of the susceptibility of an electrical steel to magnetic aging using a new internal friction technique. J. Magn. Magn. Mater., 1994, 133, 223.

[2] Wang HJ, Rong Z, Xiang L, Qiu ST, Li JX, Dong TL. Effect of decarburization annealing temperature and time on the carbon content, microstructure, and texture of grain-oriented pure iron. Int. J. Miner. Metall. Mater., 2017, 24, 393.

[3] Puzhevich RB, Borisenko VG, Shvartsman LA. Reaction of a thermal insulating coating with the surface of electrical engineering steel during high-temperature annealing. Met. Sci. Heat Treat., 1986, 28, 687.

[4] Fujii H, Yamazaki S, Nagashima T, Kobayashi H, Masui H, Shiozaki M. Glass film structure of grain-oriented silicon steel using aluminum nitride as an inhibitor. J. Mater. Eng. Perform, 1994, 3, 214.

[5] Silveira CC, da Cunha MA, Buono VTL. The influence of internal oxidation during decarburization of a grain oriented silicon steel on the morphology of the glass film formed at high temperature annealing. J. Magn. Magn. Mater., 2014 358-359.

[6] Yamazaki S, Takahashi F, Kubota T, Yanagihara K. Internal oxidation of Fe-3%Si alloys annealed under H2O-H2 atmosphere. Mater. Corros., 2011, 62, 476.

[7] Maria das Gracas MM, Mantel MJ. Effect of the temperature and dew point of the decarburization process on the oxide subscale of a 3% silicon steel. J. Magn. Magn. Mater., 2003, 254-255, 337.

[8] Fu YJ, Jiang QW, Wang BC, Yang P, Jin WX. Morphologies and influential factors of forsterite film in grain-oriented silicon steel. J. Iron Steel Res. Int., 2013, 20, 105.

[9] Yanagihara K, Suzuki S, Yamazaki S. Microscopic features in the transition from external to internal oxidation in an Fe-6 mol.% Si alloy annealed under various H2O-H2 atmospheres. Oxid. Met, 2002, 57, 281.

[10] Jung S, Kwon MS, Park J, Kim SB, Huh Y. A TEM study of oxide layers formed during decarburization annealing of electrical steel. ISIJ Int., 2011, 51, 1163.

[11] Diéz-Ercilla M, Ros-Yáñez T, Petrov R, Houbaert Y, Colás R. Oxidation of silicon steels. Corros. Eng. Sci. Technol., 2004, 39, 295.

[12] Inokuti Y, Suzuki K, Kobayashi Y. Grain oriented silicon steel sheet with new ceramic films characterized by ultra-low iron loss. Mater. Tran., JIM, 1992, 33, 946.

[13] Lyudkovsky G, Preban AG, Shapiro JM. The influence of annealing conditions on the internal oxidation and magnetic properties of silicon-aluminum bearing electrical steels. J. Appl. Phys., 1982, 53, 2419.

[14] Jung S, Kwon MS, Kim SB, Shin KS. Characterization of chemical information and morphology for in-depth oxide layers in decarburized electrical steel with glow discharge sputtering. Surf. Interface Anal., 2013, 45, 1119.

[15] Block WF, Jayaraman N. Reactions during decarburization annealing of electrical steel. Mater. Sci. Technol., 1986, 2, 22.

[16] Jung S, Park J, Han M, Kim SB. Rapid quantitative analysis of fayalite and silica formed during decarburization of electrical steel. Surf. Interface Anal., 2012, 44, 270.

[17] Poultney D, Snell D. Evaluation of oxide layers formed during the decarburisation of grain-oriented electrical steel using a Fourier transform infrared (FTIR) technique. J. Magn. Magn. Mater., 2008, 320, e645.

[18] Toda H, Sato K, Komatsubara M. Characterization of internal oxide layers in 3% Si grain-oriented steel by electrochemical methods. J. Mater. Eng. Perform., 1997, 6, 722.

[19] Kumano T, Haratani T, Ushigami Y. The improvement of primary texture for sharp Goss orientation on grain oriented silicon steel. ISIJ Int, 2003, 43, 736.

[20] Wriedt HA, Gokcen NA, Nafziger RH. The Fe-N (iron-nitrogen) system. Bull. Alloy Phase Diagrams, 1987, 8, 355.