Influence of rolling temperature on the interfaces and mechanical performance of graphene-reinforced aluminum-matrix composites

Abstract

To study the influence of rolling on the interfaces and mechanical performance of graphene-reinforced Al-matrix composites, a rolling method was used to process them. Using scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), Raman spectroscopy, and tensile testing, this study analyzed the micromorphology, interfaces, and mechanical performance of the composites before and after rolling. The experimental results demonstrates that the composites after hot rolling has uniform structures with strong interfacial bonding. With an increase in rolling temperature, the tensile strength and elastic modulus of the composites gradually increase. However, when the rolling temperature is higher than 500°C, granular and rod-like Al₄C₃ phases are observed at the interfaces and the mechanical performance of the composites is degraded. When the rolling temperature is 480°C, the composites show the optimal comprehensive mechanical performance, with a tensile strength and elastic modulus of 403.3 MPa and 77.6 GPa, respectively, which represent increases of 31.6% and 36.9%, respectively, compared with the corresponding values prior to rolling.

Keywords

rolling / graphene / composite / interface / mechanical performance

References

[1] Zhang D, Zhang GD, Li ZQ. The current state and trend of metal matrix composites. Mater. China, 2010, 29(4): 1.

[2] Joel J, Xavior MA. Aluminium alloy composites and its machinability studies; A review. Mater. Today Proc., 2018, 5(5): 13556.

[3] Surappa MK. Aluminium matrix composites: Challenges and opportunities. Sadhana, 2003, 28(1–2): 319.

[4] Ibrahim IA, Mohamed FA, Lavernia EJ. Particulate reinforced metal matrix composites—a review. J. Mater. Sci., 1991, 26(5): 1137.

[5] Nair RR, Blake P, Grigorenko AN, Novoselov KS, Booth TJ, Stauber T, Peres NMR, Geim AK. Fine structure constant defines visual transparency of graphene. Science, 2008, 320(5881): 1308.

[6] Geim AK. Graphene: Status and prospects. Science, 2009, 324(5934): 1530.

[7] Service RF. Carbon sheets an atom thick give rise to graphene dreams. Science, 2009, 324(5929): 875.

[8] Lee C, Wei XD, Kysar JW, Hone J. Measurement of the elastic properties and intrinsic strength of monolayer graphene. Science, 2008, 321(5887): 385.

[9] Weitz RT, Yacoby A. Nanomaterials: graphene rests easy. Nat. Nanotechnol., 2010, 5(10): 699.

[10] Balandin AA, Ghosh S, Bao WZ, Calizo I, Teweldebrhan D, Miao F, Lau CN. Superior thermal conductivity of single-layer graphene. Nano. Lett., 2008, 8(3): 902.

[11] Volder MFLD, Tawfick SH, Baughman RH, Hart AJ. Carbon nanotubes: present and future commercial applications. Science, 2013, 339(6119): 535.

[12] Rafiee MA, Rafiee J, Wang Z, Song HH, Yu ZZ, Koratkar N. Enhanced mechanical properties of nanocomposites at low graphene content. ACS Nano, 2009, 3(12): 3884.

[13] Bisht A, Srivastava M, Kumar RM, Lahiri I, Lahiri D. Strengthening mechanism in graphene nanoplatelets reinforced aluminum composite fabricated through spark plasma sintering. Mater. Sci. Eng. A, 2017, 695, 20.

[14] Zeng X, Teng J, Yu JG, Tan AS, Fu DF, Zhang H. Fabrication of homogeneously dispersed graphene/Al composites by solution mixing and powder metallurgy. Int. J. Miner. Metall. Mater, 2018, 25(1): 102.

[15] Shin SE, Choi HJ, Shin JH, Bae DH. Strengthening behavior of few-layered graphene/aluminum composites. Carbon, 2015, 82, 143.

[16] Tian WM, Li SM, Wang B, Chen X, Liu JH, Yu M. Graphene-reinforced aluminum matrix composites prepared by spark plasma sintering. Int. J. Miner. Metall. Mater., 2016, 23(6): 723.

[17] Wu GH, Jiang LT, Chen GQ, Zhang Q. Research progress on the control of interfacial reactions in metal matrix composites. Mater. China, 2012, 31(7): 51.

[18] Rajan TPD, Pillai RM, Pai BC. Reinforcement coatings and interfaces in aluminium metal matrix composites. J. Mater. Sci., 1998, 33(14): 3491.

[19] Lin JL, Xiong YC, Wang XD, Yan SJ, Yang C, He WW, Chen JZ, Wang SQ, Zhang XY, Dai SL. Microstructure and tensile properties of bulk nanostructured aluminum/graphene composites prepared via cryomilling. Mater. Sci. Eng. A, 2015, 626, 400.

[20] Pérez-Bustamante R, Pérez-Bustamante F, Estrada-Guel I, Licea-Jiménez L, Miki-Yoshida M, Martínez-Sánchez R. Effect of milling time and CNT concentration on hardness of CNT/Al₂₀₂₄ composites produced by mechanical alloying. Mater Charact., 1970, 75, 13.

[21] Li G, Xiong BW. Effects of graphene content on microstructures and tensile property of graphene-nanosheets / aluminum composites. J. Alloys. Compd., 2017, 697, 31.

[22] Shin SE, Ko YJ, Bae DH. Mechanical and thermal properties of nanocarbon-reinforced aluminum matrix composites at elevated temperatures. Composites. Part. B, 2016, 106, 66.

[23] Wang JY, Li ZQ, Fan GL, Pan HH, Chen ZX, Zhang D. Reinforcement with graphene nanosheets in aluminum matrix composites. Scr. Mater., 2012, 66(8): 594.

[24] Radha A, Vijayakumar KR. An investigation of mechanical and wear properties of AA6061 reinforced with silicon carbide and graphene nano particles-particulate composites. Mater. Today: Proc., 2016, 3(6): 2247.