Investigation on the homogenization treatment and element segregation on the microstructure of a γ/γ′-cobalt-based superalloy

Abstract

The aim of the present study was to investigate the effect of element segregation on the microstructure and γ′ phase in a γ/γ′ cobalt- based superalloy. Several samples were prepared from a cast alloy and homogenized at 1300°C for different times, with a maximum of 24 h. A microstructural study of the cast alloy using wavelength-dispersive spectroscopic analysis revealed that elements such as Al, Ti, and Ni segregated mostly within interdendritic regions, whereas W atoms were segregated within dendrite cores. With an increase in homogenization time, segregation decreased and the initial dendritic structure was eliminated. Field-emission scanning electron microscopy micrographs showed that the γ′ phases in the cores and interdendritic regions of the as-cast alloy were 392 and 124 nm, respectively. The size difference of γ′ was found to be due to the different segregation behaviors of constituent elements during solidification. After homogenization, particularly after 16 h, segregation decreased; thus, the size, chemical composition, and hardness of the precipitated γ′ phase was mostly uniform throughout the samples.

Keywords

superalloy / segregation / homogenization / microstructure / γ′ phase

References

[1] Wills V.A., McCartney DG. A comparative study of solidification features in nickel-base superalloys: Microstructural evolution and microsegregation. Mater. Sci. Eng. A, 1991, 145(2): 223.

[2] Warnken N, Ma D, Drevermann A, Reed RC, Fries SG, Steinbach I. Phase-field modelling of as-cast microstructure evolution in nickel-based superalloys. Acta Mater., 2009, 57(19): 5862.

[3] Merz GD, Kattamis TZ, Giamei AF. Microsegration and homogenization of Ni-7.5wt%Al-2.0wt%Ta dendritic monocrystals. J. Mater. Sci., 1979, 14(3): 663.

[4] Karunaratne MSA, Cox DC, Carter P, Reed RC. Modelling of the microsegregation in CMSX-4 superalloy and its homogenisation during heat treatment, Superalloys, 2000 263.

[5] Miao ZJ, Shan AD, Wu YB, Lu J, Xu Wl, Song HW. Quantitative analysis of homogenization treatment of INCONEL718 superalloy. Trans. Nonferrous Met. Soc. China, 2011, 21(5): 1009.

[6] Li YJ, Teng YF, Feng XH, Yang YS. Effects of pulsed magnetic field on microsegregation of solute elements in a Ni-based single crystal superalloy. J. Mater. Sci. Technol., 2017, 33(1): 105.

[7] le Graverend JB, Cormier J, Caron P, Kruch S, Gallerneau F, Mendez J. Numerical simulation of γ/γ′ microstructural evolutions induced by TCP-phase in the MC2 nickel base single crystal superalloy. Mater. Sci. Eng. A, 2011, 528(6): 2620.

[8] Golezani AS, Bageri M, Samadi R. Microstructural change, and impact toughness property of Inconel 738LC after 12 years of service. Eng. Fail. Anal., 2016, 59, 624.

[9] Jahangiri MR, Boutorabi SMA, Arabi H. Study on incipient melting in cast Ni base IN939 superalloy during solution annealing and its effect on hot workability. Mater. Sci. Technol., 2012, 28(12): 1402.

[10] Fu SH, Dong JX, Zhang MC, Xie XS. Alloy design and development of INCONEL718 type alloy. Mater. Sci. Eng. A, 2009, 499(1–2): 215.

[11] Zhou YZ, Volek A. Effect of carbon additions on hot tearing of a second generation nickel-base superalloy. Mater. Sci. Eng. A, 2008, 479(1–2): 324.

[12] Wei CN, Bor HY, Chang L. The effects of carbon content on the microstructure and elevated temperature tensile strength of a nickel-base superalloy. Mater. Sci. Eng. A, 2010, 527(16–17): 3741.

[13] Long F, Yoo YS, Jo CY, Seo SM, Song YS, Jin T, Hu ZQ. Formation of η and σ phase in three polycrystalline superalloys and their impact on tensile properties. Mater. Sci. Eng. A, 2009, 527(1–2): 361.

[14] Zhang J, Singer RF. Effect of Zr and B on castability of Ni-based superalloy IN792. Metall. Mater. Trans. A, 2004, 35(4): 1337.

[15] Epishin A, Link T, Brückner U, Fedelich B, Portella P. Effects of segregation in nickel-base superalloys: Dendritic stresses, Superalloys, 2004 537.

[16] Li P, Li SS, Han YF. Influence of solution heat treatment on microstructure and stress rupture properties of a Ni3Al base single crystal superalloy IC6SX. Intermetallics, 2011, 19(2): 182.

[17] Kim MT, Kim DS, Oh OY. Effect of γ′ precipitation during hot isostatic pressing on the mechanical property of a nickel-based superalloy. Mater. Sci. Eng. A, 2008, 480(1–2): 218.

[18] Sponseller DL. Differential thermal analysis of nickel-base superalloys, Superalloys, 1996 259.

[19] Porter DA, Easterling KE. Phase Transformations in Metals and Alloys, 1992, State of Florida, CRC Press 61.

[20] Humphreysand FJ, Hatherly M. Recrystallization and Related Annealing Phenomena, 2004, The Netherlands, Elsevier 137.

[21] Sato J, Omori T, Oikawa K, Ohnuma I, Kainuma R, Ishida K. Cobalt-base high-temperature alloys. Science, 2006, 312(5770): 90.

[22] Tanaka K, Ooshima M, Tsuno N, Sato A, Inui H. Creep deformation of single crystals of new Co-Al-W-based alloys with fcc/L1₂ two-phase microstructures. Philos. Mag., 2012, 92(32): 4011.

[23] Titus MS, Suzuki A, Pollock TM. Creep and directional coarsening in single crystals of new γ-γ′ cobalt-base alloys. Scripta Mater., 2012, 66(8): 574.

[24] Xue F, Zhou HJ, Chen XH, Shi QY, Chang H, Wang ML, Ding XF, Feng Q. Creep behavior of a novel Co-Al-W-base single crystal alloy containing Ta and Ti at 982°C. MATEC Web of Conferences, 2014, 14, 15002.

[25] Bauer A, Neumeier S, Pyczak F, Singer RF, Göken M. Creep properties of different γ′-strengthened Co-base superalloys. Mater. Sci. Eng. A, 2012, 550, 333.

[26] Neumeier S, Freund LP, Göken M. Novel wrought γ/γ′ cobalt base superalloys with high strength and improved oxidation resistance. Scripta Mater., 2015, 109, 104.

[27] Suzuki A, Pollock TM. High-temperature strength and deformation of γ/γ′ two-phase Co-Al-W-base alloys. Acta Mater., 2008, 56(6): 1288.

[28] Tsunekane M, Suzuki A, Pollock TM. Single-crystal solidification of new Co-Al-W-base alloys. Intermetallics, 2011, 19(5): 636.

[29] Ding XF, Mi T, Xue F, Zhou HJ, Wang ML. Microstructure formation in γ-γ′ Co-Al-W-Ti alloys during directional solidification. J. Alloys Compd., 2014, 599, 159.

[30] McDevitt ET. Feasibility of cast and wrought Co-Al-WX gamma-prime superalloys. Mater. Sci. Forum, 2014, 783–786, 1159.

[31] Lopez-Galilea I, Zenk C, Neumeier S, Huth S, Theisen W, Göken M. The thermal stability of intermetallic compounds in an as-cast SX Co-base superalloy. Adv. Eng. Mater., 2015, 17(6): 741.

[32] Koßmann J, Zenk CH, Lopez-Galilea I, Neumeier S, Kostka A, Huth S, Theisen W, Göken M, Drautz R, Hammerschmidt T. Microsegregation and precipitates of an as-cast Co-based superalloy—microstructural characterization and phase stability modelling. J. Mater. Sci., 2015, 50(19): 6329.

[33] Bocchini PJ, Lass EA, Moon KW, Williams ME, Campbell CE, Kattner UR, Dunand DC, Seidman DN. Atom-probe tomographic study of γ/γ′ interfaces and compositions in an aged Co-Al-W superalloy. Scripta Mater., 2013, 68(8): 563.

[34] Pyczak F, Bauer A, Göken M, Lorenz U, Neumeier S, Oehring M, Paul J, Schell N, Schreyer A, Stark A, Symanzik F. The effect of tungsten content on the properties of L12-hardened Co-Al-W alloys. J. Alloys Compd., 2015, 632, 110.

[35] Yan HY, Vorontsov VA, Dye D. Alloying effects in polycrystalline γ′ strengthened Co-Al-W base alloys. Intermetallics, 2014, 48, 44.

[36] Shinagawa K, Omori T, Sato J, Oikawa K, Ohnuma I, Kainuma R, Ishida K. Phase equilibria and microstructure on γ′ phase in Co-Ni-Al-W system. Mater. Trans., 2008, 49(6): 1474.

[37] Kramb RC, Antony MM, Semiatin SL. Homogenization of a nickel-base superalloy ingot material. Scripta Mater., 2006, 54(9): 1645.

[38] Hegde SR, Kearsey RM, Beddoes JC. Designing homogenization-solution heat treatments for single crystal superalloys. Mater. Sci. Eng. A, 2010, 527(21–22): 5528.

[39] Janotti A, Krčmar M, Fu CL, Reed RC. Solute diffusion in metals: Larger atoms can move faster. Phys. Rev. Lett., 2004, 92(8): 85901.

[40] Naghavi SS, Hegde VI, Wolverton C. Diffusion coefficients of transition metals in fcc cobalt. Acta Mater., 2017, 132, 467.

[41] Gong L, Chen B, Du ZH, Zhang MS, Liu RC, Liu K. Investigation of solidification and segregation characteristics of cast Ni-base superalloy K417G. J. Mater. Sci. Technol., 2016, 34(3): 541.

[42] Pan XL, Yu HY, Tu GF, Sun WR, Hu ZQ. Segregation and diffusion behavior of niobium in a highly alloyed nickel-base superalloy. Trans. Nonferrous Met. Soc. China, 2011, 21(11): 2402.

[43] Minamino Y, Koizumi Y, Tsuji N, Yamada T, Takahashi T. Interdiffusion in Co solid solutions of Co-Al-Cr-Ni system at 1423 K. Mater. Trans., 2003, 44(1): 63.

[44] Obata S, Moniruzzaman M, Murata Y. Interdiffusion in Co-based Co-Al-W ternary alloys at elevated temperatures. ISIJ Int., 2014, 54(10): 2129.

[45] Chang H, Xu GL, Lu XG, Zhou L, Ishida K, Cui YW. Experimental and phenomenological investigations of diffusion in Co-Al-W alloys. Scripta Mater., 2015, 106, 13.

[46] Chen J, Zhang L, Zhong J, Chen W, Du Y. High-throughput measurement of the composition-dependent interdiffusivity matrices in Ni-rich fcc Ni-Al-Ta alloys at elevated temperatures. J. Alloys Compd., 2016, 688, 320.

[47] Neumeier S, Rehman HU, Neuner J, Zenk CH, Michel S, Schuwalow S, Rogal J, Drautz R, Göken M. Diffusion of solutes in fcc cobalt investigated by diffusion couples and first principles kinetic Monte Carlo. Acta Mater., 2016, 106, 304.

[48] Green A, Swindells N. Measurement of interdiffusion coefficients in Co-AI and Ni-AI systems between 1000 and 1200°C. Mater. Sci. Technol., 1985, 1(2): 101.

[49] Povstugar I, Choi PP, Neumeier S, Bauer A, Zenk CH, Göken M, Raabe D. Elemental partitioning and mechanical properties of Ti- and Ta-containing Co-Al-W-base superalloys studied by atom probe tomography and nanoindentation. Acta Mater., 2014, 78, 78.

[50] Povstugar I, Zenk CH, Li R, Choi PP, Neumeier S, Dolotko O, Hoelzel M, Göken M, Raabe D. Elemental partitioning, lattice misfit and creep behaviour of Cr containing γ′ strengthened Co base superalloys. Mater. Sci. Technol., 2016, 32(3): 220.

[51] Vorontsov VA, Barnard JS, Rahman KM, Yan HY, Midgley PA, Dye D. Coarsening behaviour and interfacial structure of γ′ precipitates in Co-Al-W based superalloys. Acta Mater., 2016, 120, 14.

[52] Zenk CH, Neumeier S, Stone HJ, Göken M. Mechanical properties and lattice misfit of γ/γ′ strengthened Co-base superalloys in the Co-W-Al-Ti quaternary system. Intermetallics, 2014, 55, 28.

[53] Bauer A, Neumeier S, Pyczak F, Göken M. Microstructure and creep strength of different γ/γ′-strengthened Co-base superalloy variants. Scripta Mater., 2010, 63(12): 1197.

[54] Donachie MJ, Donachie SJ. Superalloys: A Technical Guide, 2002, New York, ASM international 82.

[55] Reed RC. The Superalloys: Fundamentals and Applications, 2008, Cambridge, Cambridge University Press 216.