Hydrogen storage properties of MgH₂ co-catalyzed by LaH₃ and NbH

Abstract

To improve the hydrogen storage properties of Mg-based alloys, a composite material of MgH₂ + 10wt%LaH₃ + 10wt%NbH was prepared by a mechanical milling method. The composite exhibited favorable hydrogen desorption properties, releasing 0.67wt% H₂ within 20 min at 548 K, which was ascribed to the co-catalytic effect of LaH₃ and NbH upon dehydriding of MgH₂. By contrast, pure MgH₂, an MgH₂ + 20wt%LaH₃ composite, and an MgH₂ + 20wt%NbH composite only released 0.1wt%, 0.28wt%, and 0.57wt% H₂, respectively, under the same conditions. Analyses by X-ray diffraction and scanning electron microscopy showed that the composite particle size was small. Energy-dispersive X-ray spectroscopic mapping demonstrated that La and Nb were distributed homogeneously in the matrix. Differential thermal analysis revealed that the dehydriding peak temperature of the MgH₂ + 10wt%LaH₃ + 10wt%NbH composite was 595.03 K, which was 94.26 K lower than that of pure MgH₂. The introduction of LaH₃ and NbH was beneficial to the hydrogen storage performance of MgH₂.

Keywords

energy storage materials / hydrogen absorbing materials / mechanical milling / phase transformation / activation analysis

References

[1] Mori D., Hirose K. Recent challenges of hydrogen storage technologies for fuel cell vehicles. Int. J. Hydrogen Energy, 2009, 34(10): 4569.

[2] Pei L.C., Han S.M., Wang J.S., Hu L., Zhao X., Liu B.Z. Hydrogen storage properties and phase structures of RMg₂Ni (R = La, Ce, Pr, Nd) alloys. Mater. Sci. Eng. B, 2012, 177(18): 1589.

[3] Sakintuna B., Lamari-Darkrim F., Hirscher M. Metal hydride materials for solid hydrogen storage: A review. Int. J. Hydrogen Energy, 2007, 32(9): 1121.

[4] Zhao W., Fierro V., Fernández-Huerta N., Izquierdo M.T., Celzard A. Impact of synthesis conditions of KOH activated carbons on their hydrogen storage capacities. Int. J. Hydrogen Energy, 2012, 37(19): 14278.

[5] Au M. Hydrogen storage properties of magnesium based nanostructured composite materials. Mater. Sci. Eng. B, 2005, 117(1): 37.

[6] Dong H.W., Ou Yang L.Z., Sun T., Zhu M. Effect of ball milling on hydrogen storage of Mg3La alloy. J. Rare Earths, 2008, 26(2): 303.

[7] Abdellatief M., Campostrini R., Leoni M., Scardi P. Effects of SnO2 on hydrogen desorption of MgH₂. Int. J. Hydrogen Energy, 2013, 38(11): 4664.

[8] Pei P., Song X.P., Liu J., Song A.N., Zhang P.L., Chen G.L. Study on the hydrogen desorption mechanism of a Mg–V composite prepared by SPS. Int. J. Hydrogen Energy, 2012, 37(1): 984.

[9] Ares J.R., Leardini F., Díaz-Chao P., Bodega J., Koon D.W., Ferrer I.J., Fernández J.F., Sánchez C. Hydrogen desorption in nanocrystalline MgH₂ thin films at room temperature. J. Alloys Compd., 2010, 495(2): 650.

[10] Ma L.P., Wang P., Cheng H.M. Improving hydrogen sorption kinetics of MgH₂ by mechanical milling with TiF3. J. Alloys Compd., 2007, 432(1-2): 1.

[11] Zhu M., Lu Y.S., Ouyang L.Z., Wang H. Thermodynamic tuning of Mg-based hydrogen storage alloys: a review. Materials, 2013, 6(10): 4654.

[12] Tian M., Shang C.X. Effect of TiC and Mo₂C on hydrogen desorption of mechanically milled MgH₂. J. Chem. Sci. Technol., 2012, 1, 54.

[13] Wang H., Zhang S.F., Liu J.W., Ou Yang L.Z., Zhu M. Enhanced dehydrogenation of nanoscale MgH₂ confined by ordered mesoporous silica. Mater. Chem. Phys., 2012, 136(1): 146.

[14] Zhou D.W., Peng P., Liu J.S., Chen L., Hu Y.J. First-principles study on structural stability of 3d transition metal alloying magnesium hydride. Trans. Nonferrous Met. Soc. China, 2006, 16(1): 23.

[15] Riktor M.D., Deledda S., Herrich M., Gutfleisch O., Fjellvåg H., Hauback B.C. Hydride formation in ball-milled and cryomilled Mg–Fe powder mixtures. Mater. Sci. Eng. B, 2009, 158(1-3): 19.

[16] Miloševic S., Raškovic-Lovre Z., Kurko S., Vujasin R., Cvjeticanin N., Matovic L., Novakovic J.G. Influence of VO₂ nanostructured ceramics on hydrogen desorption properties from magnesium hydride. Ceram. Int., 2013, 39(1): 51.

[17] Jia Y.H., Han S.M., Zhang W., Zhao X., Sun P.F., Liu Y.Q., Shi , H., Wang J.S. Hydrogen absorption and desorption kinetics of MgH₂ catalyzed by MoS₂ and MoO₂. Int. J. Hydrogen Energy, 2013, 38(5): 2352.

[18] Jin S.A., Shim J.H., Cho Y.W., Yi K.W. Dehydrogenation and hydrogenation characteristics of MgH₂ with transition metal fluoride. J. Power Sources, 2007, 172(2): 859.

[19] Malka I.E., Pisarek M., Czujko T., Bystrzycki J. A study of the ZrF4 NbF5, TaF5, and TiCl3 influences on the MgH₂ sorption properties. Int. J. Hydrogen Energy, 2011, 36(20): 12909.

[20] Singh R.K., Sadhasivam T., Sheeja G.I., Singh P., Srivastava O.N. Effect of different sized CeO₂ nano particles on decomposition and hydrogen absorption kinetics of magnesium hydride. Int. J. Hydrogen Energy, 2013, 38(14): 6221.

[21] Gupta R., Agresti F., Russo S.L., Maddalena A., Palade P., Principi G. Structure and hydrogen storage properties of MgH₂ catalysed with La₂O₃. J. Alloys Compd., 2008, 450(1-2): 310.

[22] Shahi R.R., Tiwari A.P., Shaz M.A., Srivastava O.N. Studies on de/rehydrogenation characteristics of nanocrystalline MgH₂ co-catalyzed with Ti, Fe and Ni. Int. J. Hydrogen Energy, 2013, 38(6): 2778.

[23] Wang H., Lin H.J., Cai W.T., Ou Yang L.Z., Zhu M.S. Tuning kinetics and thermodynamics of hydrogen storage in light metal element based systems—a review of recent progress. J. Alloys Compd., 2016, 658, 280.

[24] Xiao X.Z., Xu C.C., Shao J., Zhang L.T., Qin T., Li S.Q., Ge H.W., Wang Q.D., Chen L.X. Remarkable hydrogen desorption properties and mechanisms of the Mg2FeH6@MgH₂ core–shell nanostructure. J. Mater. Chem. A, 2015, 3(10): 5517.

[25] Xue H., Xiao X.Z., Shao J., Zhai B., Fan X.L., Cheng C.J., Li S.Q., Ge H.W., Wang Q.D., Chen L.X. Building robust architectures of carbon wrapped transition metal nanoparticles toward high-catalytic enhancement of 2LiBH₄–MgH₂ system for hydrogen storage cycling performances. Nanoscale, 2016, 8, 14898.

[26] Wang K., Du H.F., Wang Z.Y., Gao M.X., Pan H.G., Liu Y.F. Novel MAX-phase Ti₃AlC₂ catalyst for improving the reversible hydrogen storage properties of MgH₂. Int. J. Hydrogen Energy, 2017, 42, 4244.

[27] Liu Y.F., Du H.F., Zhang X., Yang Y.X., Gao M.X., Pan H.G. Superior catalytic activity derived from a two-dimensional Ti₃C₂ precursor towards the hydrogen storage reaction of magnesium hydride. Chem. Commun., 2016, 52(4): 705.

[28] Xiao X.Z., Liu Z., Yarahmadi S.S., Gregory D.H. Facile preparation of β-/γ-MgH₂ nanocomposites under mild conditions and pathways to rapid dehydrogenation. Phys. Chem. Chem. Phys., 2016, 18(15): 10492.

[29] Li Y., Tao Y., Huo Q. Effect of stoichiometry and Cu-substitution on the phase structure and hydrogen storage properties of Ml–Mg–Ni-based alloys. Int. J. Miner. Metall. Mater., 2015, 22(1): 86.

[30] Zhu X.L., Pei L.C., Zhao Z.Y., Liu B.Z., Han S.M., Wang R.B. The catalysis mechanism of La hydrides on hydrogen storage properties of MgH₂ in MgH₂ + xwt% LaH₃ (x = 0, 10, 20, and 30) composites. J. Alloys Compd., 2013, 577, 64.

[31] Zhao X., Han S.M., Li Y., Chen X.C., Ke D.D. Effect of CeH_2.29 on the microstructures and hydrogen properties of LiBH4–Mg2NiH4 composites. Int. J. Miner. Metall. Mater., 2015, 22(4): 423.

[32] da Conceição M.O.T., Brum M.C., dos Santos D.S., Dias M.L. Hydrogen sorption enhancement by Nb₂O₅ and Nb catalysts combined with MgH₂. J. Alloys Compd., 2013, 550, 179.

[33] Jin S.A., Shim J.H., Ahn J.P., Cho Y.W., Yi K.W. Improvement in hydrogen sorption kinetics of MgH₂ with Nb hydride catalyst. Acta Mater., 2007, 55(15): 5073.

[34] Zhang L.T., Xiao X.Z., Xu C.C., Zheng J.G., Fan X.L., Shao J., Li S.Q., Ge H.W., Wang Q.D., Chen L.X. Remarkably improved hydrogen storage performance of MgH₂ catalyzed by multi-valence NbHx nanoparticles. J. Phys. Chem. C, 2015, 119(16): 8554.