Addition of cerium and yttrium to ferritic steel weld metal to improve hydrogen trapping efficiency

Sung Jin Kim , Kang Mook Ryu , Min-suk Oh

International Journal of Minerals, Metallurgy, and Materials ›› 2017, Vol. 24 ›› Issue (4) : 415 -422.

PDF
International Journal of Minerals, Metallurgy, and Materials ›› 2017, Vol. 24 ›› Issue (4) : 415 -422. DOI: 10.1007/s12613-017-1422-5
Article

Addition of cerium and yttrium to ferritic steel weld metal to improve hydrogen trapping efficiency

Author information +
History +
PDF

Abstract

The applicability of Ce and Y as promising candidate elements to form irreversible traps in weld metal was investigated by thermal desorption spectroscopy (TDS) with gas chromatography (GC). The precise nature of the precipitate particles newly formed in the weld metal by the addition of Ce and Y to a certain alloy system was characterized. Moreover, the hydrogen trapping efficiency expressed as the reduction of the diffusible hydrogen in the weld metal was analyzed. The results showed that the addition of Ce and/or Y to this alloy system led to the formation of a mixed type of (Ce,Ti)-based oxide, (Y,Ni)-based carbide, or (Ce,Y,Ti)-based oxide particles. Because of the high activation energy of the mixed type of particles (≥ 150 kJ/mol), the trapping efficiency for hydrogen was considered to be sufficiently high to effectively reduce the diffusible hydrogen content.

Keywords

hydrogen trapping / weld / rare earth metals / cerium / yttrium / activation energy

Cite this article

Download citation ▾
Sung Jin Kim, Kang Mook Ryu, Min-suk Oh. Addition of cerium and yttrium to ferritic steel weld metal to improve hydrogen trapping efficiency. International Journal of Minerals, Metallurgy, and Materials, 2017, 24(4): 415-422 DOI:10.1007/s12613-017-1422-5

登录浏览全文

4963

注册一个新账户 忘记密码

References

[1]

Pitrun M. The Effect of Welding Parameters on Levels of Diffusible Hydrogen in Weld Metal Deposited Using Gas Shielded Rutile Flux Cored Wires, 2004, Australia, University of Wollongong, 83.

[2]

Padhy G.K., Komizo Y.I. Diffusible hydrogen in steel weldments. Trans. JWRI, 2013, 42(1): 39.

[3]

Ćwiek J. Hydrogen degradation of high-strength steels. J. Achiev. Mater. Manuf. Eng., 2009, 37(2): 193.

[4]

Glickstein S.S. Temperature measurements in a free burning arc. Weld. J., 1976, 55, 222.

[5]

Chew B. Prediction of weld metal hydrogen levels obtained under test conditions. Weld. J., 1973, 52, 386.

[6]

Kim D.Y., Hwang I.S., Kim D.C., Kang M.J. Effect of preheat temperature on diffusible hydrogen content in weld metal deposited using flux cored wire. J. Weld. Joining, 2014, 32(2): 18.

[7]

McKeown D. Hydrogen and its control in weld metal. Met. Construct., 1985, 17(10): 655.

[8]

Gedeon S.A., Eagar T.W. Thermochemical analysis of hydrogen absorption in welding. Weld. J., 1990, 69, 264.

[9]

Maroef I., Olson D.L., Eberhart M., Edwards G.R. Hydrogen trapping in ferritic steel weld metal. Int. Mater. Rev., 2002, 47(4): 191.

[10]

Park Y.D., Lensing C., Maroef I., Olson D.L., Gavra Z. Advances in hydrogen management for high strength steel. Proceedings of the 9th CF/DRDC Meeting on Naval Applications of Materials Technology, 2001

[11]

Granjon H. Cold cracking in welding of steels. Indian Weld. J., 1973, 5(2): 43.

[12]

Lee H.G., Lee J.Y. Hydrogen trapping by TiC particles in iron. Acta Metall., 1984, 32(1): 131.

[13]

Pressouyre G.M., Bernstein I.M. A quantitative analysis of hydrogen trapping. Metall. Trans. A, 1978, 9(11): 1571.

[14]

Szost B.A., Vegter R.H., Rivera-Díaz-del-Castillo P.E.J. Developing bearing steels combining hydrogen resistance and improved hardness. Mater. Des., 2013, 43, 499.

[15]

Yamasaki S., Bhadeshia H.K.D.H. M4C3 precipitation in Fe−C−Mo−V steels and relationship to hydrogen trapping. Proc. R. Soc. Ser. A, 2006, 462(2072): 2315.

[16]

Lee H.G., Lee J.Y. The interaction of hydrogen with the interface of Al2O3 particles in iron. Metall. Trans. A, 1986, 17(12): 2183.

[17]

Podgurski H.H., Oriani R.A. Nitrogenation of Fe−Al alloys: III. Absorption of hydrogen in nitrogenated Fe−Al alloys. Metall. Trans., 1972, 3, 2055.

[18]

Maroef I., Lensing C., Park Y.D., Landau A., Olson D.L. Joining of advanced and specialty materials II. Proceedings of the International Conference on Materials Solution’99, 1999

[19]

Lensing C.A., Park Y.D., Maroef I.S., Olson D.L. Yttrium hydrogen trapping to manage hydrogen in HSLA steel welds. Weld. J., 2004, 83, 254.

[20]

Choo W.Y., Lee J.Y. Thermal analysis of trapped hydrogen in pure iron. Metall. Trans. A, 1982, 13(1): 135.

[21]

Kissinger H.E. Reaction kinetics in differential thermal analysis. Anal. Chem., 1957, 29(11): 1702.

[22]

Wang W.W. Alloying Composition for Self-shielded FCAW Wires with Low Diffusible Hydrogen and High Charpy V-notch Impact Toughness, 2014

[23]

Yoo J.S., Xian G., Lee M.J., Kim Y.D., Kang N.H. Hydrogen embrittlement resistance and diffusible hydrogen desorption behavior of multipass FCA weld metals. J. Weld. Joining, 2013, 31(6): 112.

[24]

Chun Y.S., Kim J.S., Park K.T., Lee Y.K., Lee C.S. Role of ε martensite in tensile properties and hydrogen degradation of high-Mn steels. Mater. Sci. Eng. A, 2012, 533, 87.

[25]

Kim J.S., Lee Y.H., Lee D.L., Park K.T., Lee C.S. Microstructural influences on hydrogen delayed fracture of high strength steels. Mater. Sci. Eng. A, 2009, 505(1-2): 105.

[26]

Ryu J.H., Chun Y.S., Lee C.S., Bhadeshia H.K.D.H., Suh D.W. Effect of deformation on hydrogen trapping and effusion in TRIP-assisted steel. Acta Mater., 2012, 60(10): 4085.

[27]

Liu S., Clasper C., Moline K., Scott J. Ultra-low hydrogen consumables for welding of high strength steels with 690−750 MPa-yield strength. Proceedings of the 25th International Conference on Offshore Mechanics and Arctic Engineering, 2006 661.

[28]

Lee S.M., Lee J.Y. The effect of the interface character of TiC particles on hydrogen trapping in steel. Acta Metall., 1987, 35(11): 2695.

AI Summary AI Mindmap
PDF

113

Accesses

0

Citation

Detail

Sections
Recommended

AI思维导图

/