Synthesis and characterization of carbon-coated cobalt ferrite nanoparticles

Abstract

Cobalt ferrite nanoparticles (CFNPs) were prepared via a reverse micelle method. The CFNPs were subsequently coated with carbon shells by means of thermal chemical vapor deposition (TCVD). In this process, acetylene gas (C₂H₂) was used as a carbon source and the coating was carried out for 1, 2, or 3 h at 750°C. The Ar/C₂H₂ ratio was 10:1. Heating during the TCVD process resulted in a NP core size that approached 30 nm; the thickness of the shell was less than 10 nm. The composition, structure, and morphology of the fabricated composites were characterized using X-ray diffraction, simultaneous thermal analysis, transmission electron microscopy, high-resolution transmission electron microscopy, and selected-area diffraction. A vibrating sample magnetometer was used to survey the samples’ magnetic properties. The deposited carbon shell substantially affected the growth and magnetic properties of the CFNPs. Micro-Raman spectroscopy was used to study the carbon coating and revealed that the deposited carbon comprised graphite, multiwalled carbon nanotubes, and diamond- like carbon. With an increase in coating time, the intensity ratio between the amorphous and ordered peaks in the Raman spectra decreased, which indicated an increase in crystallite size.

Keywords

nanoparticles / cobalt ferrite / carbon coatings / chemical vapor deposition / Raman spectroscopy

References

[1] Matsumoto N., Oshima A., Sakurai S., Yamada T., Yumura M., Hata K., Futaba D.N. The application of gas dwell time control for rapid single wall carbon nanotube forest synthesis to acetylene feedstock. Nanomaterials, 2015, 5(3): 1200.

[2] Bacsa R.R., Cameán I., Ramos A., Garcia A.B., Tishkova V., Bacsa W.S., Gallagher J.R., Miller J.T., Navas H., Jourdain V., Girleanu M., Ersen O., Serp P. Few layer graphene synthesis on transition metal ferrite catalysts. Carbon, 2015, 89, 350.

[3] Novoselov K.S., Geim A.K., Morozov S.V., Jiang D., Katsnelson M.I., Grigorieva I.V., Dubonos S.V., Firsov A.A. Two-dimensional gas of massless Dirac fermions in graphene. Nature, 2005, 438, 197.

[4] Santhosh C., Saranya M., Ramachandran R., Pradeep N., Uma V., Kollu P., Grace A.N. Synthesis of magnetic nanoparticles and their effect on growth of carbon nanotubes. J. Indian Chem. Soc., 2015, 92, 800.

[5] Zhang T., Zhou Y.M., Bu X.H., Wang Y.J., Qiu F.X. Controlled fabrication of hierarchical MgAl₂O₄ spinel/carbon fiber composites by crystal growth and calcination processes. Ceram. Int., 2015, 41(9): 12504.

[6] Li P.X., Ma R.Q., Zhou Y., Chen Y.F., Liu Q., Peng G.H., Liang Z.H., Wang J.C. Spinel nickel ferrite nanoparticles strongly cross-linked with multiwalled carbon nanotubes as a bi-efficient electrocatalyst for oxygen reduction and oxygen evolution. RSC Adv., 2015, 5, 73834.

[7] Ohashi T., Shima T. Synthesis of vertically aligned single-walled carbon nanotubes with metallic chirality through facet control of catalysts. Carbon, 2015, 87, 453.

[8] Zhang M., Yang X., Kan X.F., Wang X., Ma L., Jia M.Q. Carbon-encapsulated CoFe₂O₄/graphene nanocomposite as high performance anode for lithium ion batteries. Electrochim. Acta, 2013, 112, 727.

[9] Kim J., Kim H.S., Lee N., Kim T., Kim H., Yu T., Song I.C., Moon W.K., Hyeon T. Multifunctional uniform nanoparticles composed of a magnetite nanocrystal core and a mesoporous silica shell for magnetic resonance and fluorescence imaging and for drug delivery. Angew. Chem. Int. Ed., 2008, 47(44): 8438.

[10] Xue X.Z., Wang J.C., Furlani E.P. Self-assembly of crystalline structures of magnetic core–shell nanoparticles for fabrication of nanostructured materials. ACS Appl. Mater. Interfaces, 2015, 7(40): 22515.

[11] Verma V.K., Kamaraju S.R., Kancherla R., Kona L.K., Beevi S.S., Debnath T., Usha S.P., Vadapalli R., Arbab A.S., Chelluri L.K. Fluorescent magnetic iron oxide nanoparticles for cardiac precursor cell selection from stromal vascular fraction and optimization for magnetic resonance imaging. Int. J. Nanomed., 2015, 10, 711.

[12] Sanpo N., Wen C., Berndt C.C., Wang J. Multifunctional spinel ferrite nanoparticles for biomedical application. Adv. Funct. Mater., 2015 183.

[13] Dai B., Fu L., Zou Z., Wang M., Xu H., Wang S., Liu Z. Rational design of a binary metal alloy for chemical vapour deposition growth of uniform single-layer graphene. Nat. Commun., 2011, 2, 522.

[14] Chen Z.P., Ren W.C., Gao L.B., Liu B.L., Pei S.F., Cheng H.M. Three-dimensional flexible and conductive interconnected graphene networks grown by chemical vapour deposition. Nat. Mater., 2011, 10, 424.

[15] Park S., Ruoff R.S. Chemical methods for the production of graphenes. Nat. Nanotechnol., 2009, 4, 217.

[16] Kurian M., Thankachan S., Nair D.S., Aswathy E.K., Babu A., Thomas A., Binu Krishna K.T. Structural, magnetic, and acidic properties of cobalt ferrite nanoparticles synthesised by wet chemical methods. J. Adv. Ceram., 2015, 4(3): 199.

[17] Briceño S., Brämer-Escamilla W., Silva P., Delgado G.E., Plaza E., Palacios J., Cañizales E. Effects of synthesis variables on the magnetic properties of CoFe₂O₄ nanoparticles. J. Magn. Magn. Mater., 2012, 324(18): 2926.

[18] Yao Y.J., Yang Z.H., Zhang D.W., Peng W.C., Sun H.Q., Wang S.B. Magnetic CoFe₂O₄–graphene hybrids: facile synthesis, characterization, and catalytic properties. Ind. Eng. Chem. Res., 2012, 51(17): 6044.

[19] P.F. Wang, J.C. Xu, Y.B. Han, B. Hong, H.X. Jin, D.F. Jin, X.L. Peng, J. Li, H.L. Ge, and X.Q. Wang, Magnetic CoFe₂O₄/carbon nanotubes composites: fabrication, microstructure and magnetic response, Mod. Phys. Lett. B, 28(2014), doi: 10.1142/s021798491450095X.

[20] Ferrari A.C., Basko D.M. Raman spectroscopy as a versatile tool for studying the properties of graphene. Nat. Nanotechnol., 2013, 8, 235.

[21] Tomasini E.P., Halac E.B., Reinoso M., Di Liscia E.J., Maier M.S. Micro-Raman spectroscopy of carbon-based black pigments. J. Raman Spectrosc., 2012, 43(11): 1671.

[22] Wang C.C., Chen D.H., Huang T.C. Synthesis of palladium nanoparticles in water-in-oil microemulsions. Colloids Surf. A, 2001, 189(1-3): 145.

[23] Grill A. Diamond-like carbon coatings as biocompatible materials: an overview. Diamond Relat. Mater., 2003, 12(2): 166.

[24] Rao M.S.R., Kundaliya D.C., Dhar S., Cardoso C.A., Curtin A., Welz S.J., Erni R., Browning N.D., Lofland S.E., Metting C.J., Ogale S.B., Venkatesan T. Search for magnetism in Co and Fe-doped HfO₂ thin films for potential spintronic applications. MRS Proceedings, 2004

[25] Sivakumar P., Ramesh R., Ramanand A., Ponnusamy S., Muthamizhchelvan C. Synthesis and characterization of NiFe₂O₄ nanosheet via polymer assisted co-precipitation method. Mater. Lett., 2011, 65(3): 483.

[26] Ganguli A.K., Ganguly A., Vaidya S. Microemulsionbased synthesis of nanocrystalline materials. Chem. Soc. Rev., 2010, 39(2): 474.

[27] Mathew D.S., Juang R.-S. An overview of the structure and magnetism of spinel ferrite nanoparticles and their synthesis in microemulsions. Chem. Eng. J., 2007, 129(1-3): 51.

[28] Wang X.M., Zhu M.Q., Koopal L.K., Li W., Xu W.Q., Liu F., Zhang J., Liu Q.S., Feng X.H., Sparks D.L. Effects of crystallite size on the structure and magnetism of ferrihydrite. Environ. Sci. Nano, 2016, 3, 190.

[29] Lu S.C., Yao M.G., Yang X.G., Li Q.J., Xiao J.P., Yao Z., Jiang L.H., Liu R., Liu B., Chen S.L., Zou B., Cui T., Liu B.B. High pressure transformation of graphene nanoplates: A Raman study. Chem. Phys. Lett., 2013, 585, 101.

[30] Ferrari A.C. Raman spectroscopy of graphene and graphite: disorder, electron–phonon coupling, doping and nonadiabatic effects. Solid State Commun., 2007, 143(1): 47.

[31] Bokobza L., Bruneel J.-L., Couzi M. Raman spectroscopy as a tool for the analysis of carbon-based materials (highly oriented pyrolitic graphite, multilayer graphene and multiwall carbon nanotubes) and of some of their elastomeric composites. Vib. Spectrosc., 2014, 74, 57.

[32] Saito R., Hofmann M., Dresselhaus G., Jorio A., Dresselhaus M.S. Raman spectroscopy of graphene and carbon nanotubes. Adv. Phys., 2011, 60(3): 413.

[33] Samaniego J.E., Perez J.F., Solorza O., Garcia A. Al₂O₃+FeCo and Al₂O₃+FeNi coatings for multiwalled carbon nanotubes growth. Diamond Relat. Mater., 2015, 53, 18.

[34] Tyagi M., Kumari M., Chatterjee R., Sharma P. Raman scattering spectra, magnetic and ferroelectric properties of BiFeO3–CoFe₂O₄ nanocomposite thin films structure. Phys. B, 2014, 448, 128.

[35] Park Y.P., Kim T.G., Cheon M.W. Microstructure analysis of DLC thin film fabricated by filtered arc ion plating method. J. Ceram. Process. Res., 2012, 13, S363.

[36] Golden T.D. Investigation of the Structure and Properties of Diamond-Like Carbon Films Deposited Electrochemically at low Temperatures, 2004

[37] Tuinstra F., Koenig J.L. Raman spectrum of graphite. J. Chem. Phys., 1970, 53(3): 1126.

[38] Cappelli E., Orlando S., Mattei G., Zoffoli S., Ascarelli P. SEM and Raman investigation of RF plasma assisted pulsed laser deposited carbon films. Appl. Surf. Sci., 2002, 197-198, 452.

[39] Capano M.A., McDevitt N.T., Singh R.K., Qian F. Characterization of amorphous carbon thin films. J. Vac. Sci. Technol. A, 1996, 14(2): 431.

[40] Bunshah R.F. Handbook of Deposition Technologies for Films and Coatings: Science, Technology and Applications, 1994 2