Effect of graphite powder as a forming filler on the mechanical properties of SiCp/Al composites by pressure infiltration

Abstract

(38vol% SiCp + 2vol% Al₂O_3f)/2024 Al composites were fabricated by pressure infiltration. Graphite powder was introduced as a forming filler in preform preparation, and the effects of the powder size on the microstructures and mechanical properties of the final composites were investigated. The results showed that the composite with 15 μm graphite powder as a forming filler had the maximum tensile strength of 506 MPa, maximum yield strength of 489 MPa, and maximum elongation of 1.2%, which decreased to 490 MPa, 430 MPa, and 0.4%, respectively, on increasing the graphite powder size from 15 to 60 μm. The composite with 60 μm graphite powder showed the highest elastic modulus, and the value decreased from 129 to 113 GPa on decreasing the graphite powder size from 60 to 15 μm. The differences between these properties are related to the different microstructures of the corresponding composites, which determine their failure modes.

Keywords

metal matrix composites / aluminum / silicon carbide / graphite / preparation / pressure infiltration / mechanical properties

References

[1] Mirzadeh H. Quantification of the strengthening effect of reinforcements during hot deformation of aluminum-based composites. Mater. Des., 2015, 65, 2015.

[2] Umasankar V., Xavior M.A., Karthikeyan S. Experimental evaluation of the influence of processing parameters on the mechanical properties of SiC particle reinforced AA6061 aluminium alloy matrix composite by powder processing. J. Alloys Compd., 2014, 582, 2014.

[3] Boostani A.F., Tahamtan S., Jiang Z.Y., Wei D., Yazdani Y., Azari Khosroshahi R., Taherzadeh Mousavian R., Xu J., Zhang X., Gong D. Enhanced tensile properties of aluminium matrix composites reinforced with graphene encapsulated SiC nanoparticles. Compos. Part A, 2015, 68, 2015.

[4] Liu J.Y., Zhang K.F. Promotion mechanism of electric current on SiCp/Al composite material deformation. Mater. Sci. Technol., 2015, 31(4): 468.

[5] Dong R.H., Yang W.S., Yu Z.H., Wu P., Hussain M., Jiang L.T., Wu G.H. Aging behavior of 6061Al matrix composite reinforced with high content SiC nanowires. J. Alloys Compd., 2015, 649, 2015.

[6] Geng L., Zhang H.W., Li H.Z., Guan L.N., Huang L.J. Effects of Mg content on microstructure and mechanical properties of SiCp/Al?Mg composites fabricated by semi-solid stirring technique. Trans. Nonferrous Met. Soc. China, 2010, 20(10): 1851.

[7] Srivastava V.C., Ojha S.N. Microstructure and electrical conductivity of Al?SiCp composites produced by spray forming process. Bull. Mater. Sci., 2005, 28(2): 125.

[8] Lee H.S., Hong S.H. Pressure infiltration casting process and thermophysical properties of high volume fraction SiCp/Al metal matrix composites. Mater. Sci. Technol., 2003, 19(8): 1057.

[9] Song M., He Y.H., Fang S.F. Yield stress of SiC reinforced aluminum alloy composites. J. Mater. Sci., 2010, 45(15): 4097.

[10] Nardone V.C. Assessment of models used to predict the strength of discontinuous silicon carbide reinforced aluminum alloys. Scripta Metall., 1987, 21(10): 1313.

[11] Nardone V.C., Prewo K.M. On the strength of discontinuous silicon carbide reinforced aluminum composites. Scripta Metall., 1986, 20(1): 43.

[12] H. Sekine and R. Chent, A combined microstructure strengthening analysis of SiCp/Al metal matrix composites, Composites, 26(1995), No. 3, p. 183.

[13] Ashby M.F. The deformation of plastically non-homogeneous materials. Philos. Mag., 1970, 21(170): 399.

[14] Geiger A.L., Jackson M. Low-expansion MMCs boost avionics. Adv. Mater. Processes, 1989, 136(1): 23.

[15] Hashin Z., Shtrikman S. A variational approach to the theory of the elastic behaviour of multiphase materials. J. Mech. Phys. Solids, 1963, 11(2): 127.