Innovative method for boron extraction from iron ore containing boron

Abstract

A novel process for boron enrichment and extraction from ludwigite based on iron nugget technology was proposed. The key steps of this novel process, which include boron and iron separation, crystallization of boron-rich slag, and elucidation of the boron extraction behavior of boron-rich slag by acid leaching, were performed at the laboratory. The results indicated that 95.7% of the total boron could be enriched into the slag phase, thereby forming a boron-rich slag during the iron and slag melting separation process. Suanite and kotoite were observed to be the boron-containing crystalline phases, and the boron extraction properties of the boron-rich slag depended on the amounts and grain sizes of these minerals. When the boron-rich slag was slowly cooled to 1100°C, the slag crystallized well and the efficiency of extraction of boron (EEB) of the slag was the highest observed in the present study. The boron extraction property of the slow-cooled boron-rich slag obtained in this study was much better than that of szaibelyite ore under the conditions of 80% of theoretical sulfuric acid amount, leaching time of 30 min, leaching temperature of 40°C, and liquid-to-solid ratio of 8 mL/g.

Keywords

ludwigite / reduction / melting separation / boron extraction

References

[1] Ken S., Marcia K.M. Mineral Commodity Summaries, 2015 32.

[2] Zhang X.P., Lang J.F., Cui C.M., Liu S.L. Comprehensive utilization of low grade ludwigite ore with blast furnace smelting. Iron Steel, 1995, 30(12): 9.

[3] Sui Z.T., Zhang P.X., Yamauchi C. Precipitation selectivity of boron compounds from slags. Acta Mater., 1999, 47(4): 1337.

[4] Wang C.R., Lian X.Q. On some problems of the beneficiation of boron iron ores. Met. Mine, 1995, 9, 33.

[5] Zhang J.L., Cai H.T. Enrichment of boron in low-grade paigeite. J. Univ. Sci. Technol. Beijing, 2009, 31(1): 36.

[6] Liu R., Xue X.X., Jiang T., Zhang S.H., Huang D.W. Comprehensive utilization of ludwigite and its prospect. Multipurpose Util. Miner. Res., 2006, 2, 33.

[7] Liu S.L., Cui C.M., Zhang X.P. Pyrometallurgical separation of boron from iron in ludwigite ore. ISIJ Int., 1998, 38(10): 1077.

[8] Zhao Q.J. Separating iron from boric iron ore by selective reduction. J. Northeast. Univ. Technol., 1990, 11(2): 122.

[9] Zhu R., Ren J.T., Liu G., Wan T.J., Xu M. Development and practice on the rotary hearth furnace ironmaking process. J. Univ. Sci. Technol. Beijing, 2007, 29(S1): 171.

[10] Griscom F.N., Lyles D.R. The Fastmet process-direct reduction technology for modern steelmaking. Proceedings of the 52nd Electric Furnace Conference, Nashville, 1994 75.

[11] Miyagawa K., Matsumura T., Takenaka Y., Shimizu M. Development of the FASTMET as a new direct reduction process. Proceedings of the 2nd International Congress on the Science and Technology of Ironmaking, Toronto, 1998 877.

[12] Kikuchi S., Ito S., Kobayashi I., Tsuge O., Tokuda K. ITmk3 process. Kobelco Technol. Rev., 2010, 29, 77.

[13] Anameric B., Kawatra S.K. Laboratory study related to the production and properties of pig iron nuggets. Miner. Metall. Process., 2006, 23(1): 52.

[14] Anameric B., Kawatra S.K. The microstructure of the pig iron nuggets. ISIJ Int., 2007, 47(1): 53.

[15] Nagata K., Kojima R., Murakami T., Susa M., Fukuyama H. Mechanisms of pig-iron making from magnetite ore pellets containing coal at low temperature. ISIJ Int., 2001, 41(11): 1316.

[16] Borra C.R., Dwarapudi S., Kapure G., Tathavadkar V., Denys M.B. Effect of alumina on slag-metal separation during iron nugget formation from high alumina Indian iron ore fines. Ironmaking Steelmaking, 2013, 40(6): 443.

[17] Liang Y.J., Che Y.C. Inorganic Thermodynamic Data Manual, 1993, Shenyang, Northeastern University Press, 450.

[18] Wang G., Wang J.S., Ding Y.G., Ma S., Xue Q.G. New separation method of boron and iron from ludwigite based on carbon bearing pellet reduction and melting technology. ISIJ Int., 2012, 52(1): 45.

[19] Zhang P.X., Sui Z.T. Effect of factors on the extraction of boron from slags. Metall. Mater. Trans. B, 1995, 26(2): 345.

[20] Li J., Lei L., Wang L.J., Jiang T., Fan Z.G. Study on preparation of boric acid from boric slag using sulfuric acid method. J. Chin. Rare Earth Soc., 2010, 28, 680.

[21] Zheng X.J. Production and Application of Borides, 2008, Beijing, Chemical Industry Press, 114.