Effect of initial microstructure on austenite formation kinetics in high-strength experimental microalloyed steels

Abstract

Austenite formation kinetics in two high-strength experimental microalloyed steels with different initial microstructures comprising bainite–martensite and ferrite–martensite/austenite microconstituents was studied during continuous heating by dilatometric analysis. Austenite formation occurred in two steps: (1) carbide dissolution and precipitation and (2) transformation of residual ferrite to austenite. Dilatometric analysis was used to determine the critical temperatures of austenite formation and continuous heating transformation diagrams for heating rates ranging from 0.03°C•s⁻¹ to 0.67°C•s⁻¹. The austenite volume fraction was fitted using the Johnson–Mehl–Avrami–Kolmogorov equation to determine the kinetic parameters k and n as functions of the heating rate. Both n and k parameters increased with increasing heating rate, which suggests an increase in the nucleation and growth rates of austenite. The activation energy of austenite formation was determined by the Kissinger method. Two activation energies were associated with each of the two austenite formation steps. In the first step, the austenite growth rate was controlled by carbon diffusion from carbide dissolution and precipitation; in the second step, it was controlled by the dissolution of residual ferrite to austenite.

Keywords

non-isothermal kinetics / microalloyed steel / austenite / heating / dilatometry

References

[1] Teoh L.L. Thermo-mechanical processing and microstructure of microalloyed steel bar and wire rod products. J. Mater. Process. Technol., 1995, 48(1-4): 475.

[2] Korchynsky M. A new role for microalloyed steels: adding economic value. Proceedings of the 9th International Ferroalloy Conference, 2001 11.

[3] Kou S. Welding Metallurgy, 2002 2 Hoboken, NJ, USA, Wiley-Interscience

[4] Boumerzoug Z., Derfouf C., Baudin T. Effect of welding on microstructure and mechanical properties of an industrial low carbon steel. Engineering, 2010, 2(7): 502.

[5] Francis J.A., Bhadeshia H.K.D.H., Withers P.J. Welding residual stresses in ferritic power plant steels. Mater. Sci. Technol., 2007, 23(9): 1009.

[6] Zinn W., Scholtes B. Totten G., Howes M., Inoue T. Residual stress formation processes during welding and joining. Handbook of Residual Stress and Deformation of Steel, 2002 391.

[7] Chang M., Yu H. Kinetics of bainite-to-austenite transformation during continuous reheating in low carbon microalloyed steel. Int. J. Miner. Metall. Mater., 2013, 20(5): 427.

[8] Moszner F., Povoden-Karadeniz E., Pogatscher S., Uggowitzer P.J., Estrin Y., Gerstl S.S.A., Kozeschnik E., Löffler J.F. Reverse a transformation mechanisms of martensitic Fe-Mn and age-hardenable Fe-Mn-Pd alloys upon fast and slow continuous heating. Acta Mater., 2014, 72, 99.

[9] Oliveira F.L.G., Andrade M.S., Cota A.B. Kinetics of austenite formation during continuous heating in a low carbon steel. Mater. Charact., 2007, 58(3): 256.

[10] Pawblowski B. Dilatometric examination of continuously heated austenite formation in hypoeutectoid steels. J. Achiev. Mater. Manuf. Eng., 2012, 54(2): 185.

[11] Azizi-Alizamini H., Militzer M., Poole W.J. Austenite formation in plain low-carbon steels. Metall. Mater. Trans. A, 2011, 42(6): 1544.

[12] Caballero F.G., Capdevila C., de Andrés C.G. Modelling of kinetics of austenite formation in steels with different initial microstructures. ISIJ Int., 2001, 41(10): 1093.

[13] San Martín D., Rivera-Díaz-del-Castillo P.E.J., García-de-Andrés C. In situ study of austenite formation by dilatometry in a low carbon microalloyed steel. Scripta Mater., 2008, 58(10): 926.

[14] Vázquez-Gómez O., Barrera-Godínez J.A., Vergara-Hernández H.J. Kinetic study of austenite formation during continuous heating of unalloyed ductile iron. Int. J. Miner. Metall. Mater., 2015, 22(1): 27.

[15] Abdollahi P., Amirsadeghi A., Kheirandish S., Mirdamadi S. Formation kinetics of austenite in pearlitic ductile iron. Int. J. Miner. Metall. Mater., 2012, 19(6): 506.

[16] Girault E., Jacques P., Harlet P.h., Mols K., Van Humbeeck J., Aernoudt E., Delannay F. Metallographic methods for revealing the multiphase microstructure of TRIP-assisted steels. Mater. Charact., 1998, 40(2): 111.

[17] Han J., Lee Y.K. The effects of the heating rate on the reverse transformation mechanism and the phase stability of reverted austenite in medium Mn steels. Acta Mater., 2014, 67, 354.

[18] Lee Y.K., Shin H.C., Leem D.S., Choi J.Y., Jin W., Choi C.S. Reverse transformation mechanism of martensite to austenite and amount of retained austenite after reverse transformation in Fe-3Si-13Cr-7Ni (wt%) martensitic stainless steel. Mater. Sci. Technol., 2003, 19(3): 393.

[19] Lopes M.M.B., Cota A.B. A study of isochronal austenitization kinetics in a low carbon steel. Rev. Esc. Minas, 2014, 67(1): 61.

[20] Avrami M. Kinetics of phase change: I. General theory. J. Chem. Phys., 1939, 7(12): 1103.

[21] Avrami M. Kinetics of phase change: II. Transformation-time relations for random distribution of nuclei. J. Chem. Phys., 1940, 8(2): 212.

[22] Avrami M. Granulation, phase change, and microstructure: kinetics of phase change. III. J. Chem. Phys., 1941, 9(2): 177.

[23] Johnson W.A., Mehl R.F. Reaction kinetics in processes of nucleation and growth. Trans. AIME, 1939, 135, 416.

[24] Kolmogorov A.N. A statistical theory for the recrystallization of metals. Bull. Acad. Sci. USSR Ser. 1, 1937, 1, 355.

[25] Cahn J.W. The kinetics of grain boundary nucleated reactions. Acta Metall., 1956, 4(5): 449.

[26] Howell P.R. The pearlite reaction in steels mechanisms and crystallography: Part I. Mater. Charact., 1998, 40(4-5): 227.

[27] Liu F., Liu X.N., Wang Q. Examination of Kissinger's equation for solid-state transformation. J. Alloys Compd., 2009, 473(1-2): 152.

[28] Kapoor R., Batra I.S. On the a to γ transformation in maraging (grade 350), PH 13-8 Mo and 17-4 PH steels. Mater. Sci. Eng. A, 2004, 371(1-2): 324.

[29] Guo Z., Sha W., Li D. Quantification of phase transformation kinetics of 18 wt.% Ni C250 maraging steel. Mater. Sci. Eng. A, 2004, 373(1-2): 10.

[30] de Carvalho L.G., Andrade M.S., Plaut R.L., Souza F.M., Padilha A.F. A dilatometric study of the phase transformations in 300 and 350 maraging steels during continuous heating rates. Mater. Res., 2013, 16(4): 740.