Microstructure and high-temperature wear properties of in situ TiC composite coatings by plasma transferred arc surface alloying on gray cast iron

Abstract

In this work, an in situ synthesized TiC-reinforced metal matrix composite (MMC) coating of approximately 350–400 µm thickness was fabricated on a gray cast iron (GCI) substrate by plasma transferred arc (PTA) surface alloying of Ti–Fe alloy powder. Microhardness tests showed that the surface hardness increased approximately four-fold after the alloying treatment. The microstructure of the MMC coating was mainly composed of residual austenite, acicular martensite, and eutectic ledeburite. Scanning electron microscopy (SEM) and X-ray diffraction analyzes revealed that the in situ TiC particles, which were formed by direct reaction of Ti with carbon originally contained in the GCI, was uniformly distributed at the boundary of residual austenite in the alloying zone. Pin-on-disc high-temperature wear tests were performed on samples both with and without the MMC coating at room temperature and at elevated temperatures (473 K and 623 K), and the wear behavior and mechanism were investigated. The results showed that, after the PTA alloying treatment, the wear resistance of the samples improved significantly. On the basis of our analysis of the composite coatings by optical microscopy, SEM with energy-dispersive X-ray spectroscopy, and microhardness measurements, we attributed this improvement of wear resistance to the transformation of the microstructure and to the presence of TiC particles.

Keywords

gray cast iron / composite coatings / particle-reinforced composites / titanium carbide / surface alloying / microstructure / wear

References

[1] Riahi A.R., Alpas A.T. Wear map for grey cast iron. Wear, 2003, 255(1–6): 401.

[2] Prasad B.K. Sliding wear response of cast iron as influenced by microstructural features and test condition. Mater. Sci. Eng. A, 2007, 456(1–2): 373.

[3] Qin S.D., Wang S.Q., Chen N.L. Wear behaviors and mechanism of gray cast iron under dry sliding condition. Heat Treat. Met., 2011, 36(6): 73.

[4] Agarwal K., Shivpuri R., Vincent J., Rolinski E., Sharp G. DC pulsed plasma deposition of nanocomposite coatings for improved tribology of gray cast iron stamping dies. J. Mater. Process. Technol., 2013, 213(6): 864.

[5] Balachandran G., Vadiraj A., Kamaraj M., Kazuya E. Mechanical and wear behavior of alloyed gray cast iron in the quenched and tempered and austempered conditions. Mater. Des., 2011, 32(7): 4042.

[6] Balachandran G., Vadiraj A., Sharath B.S., Krishnamurthy B.R. Studies on induction hardening of gray iron and ductile iron. Trans. Indian Inst. Met., 2010, 63(4): 707.

[7] Bourithis L., Papadimitriou G. Boriding a plain carbon steel with the plasma transferred arc process using boron and chromium diboride powders: microstructure and wear properties. Mater. Lett., 2003, 57(12): 1835.

[8] Chen D.Q., Liu D., Liu Y.F., Wang H.M., Huang Z. Microstructure and fretting wear resistance of γ/TiC composite coating in situ fabricated by plasma transferred arc cladding. Surf. Coat. Technol., 2014, 239, 28.

[9] Cao H.T., Dong X.P., Huang Q.W., Pan Z., Li J.J., Fan Z.T. Effect of scanning speed during PTA remelting treatment on the microstructure and wear resistance of nodular cast iron. Int. J. Miner. Metall. Mater., 2014, 21(4): 363.

[10] Wang H.Y., Jiang Q.C., Li X.L., Wang J.G. In situ synthesis of TiC/Mg composites in molten magnesium. Scripta Mater., 2003, 48(9): 1349.

[11] Man H.C., Zhang S., Cheng F.T., Yue T.M. In situ synthesis of TiC reinforced surface MMC on Al₆061 by laser surface alloying. Scripta Mater., 2002, 46(3): 229.

[12] Cui C.Y., Guo Z.X., Wang H.Y., Hu J.D. In situ TiC particles reinforced grey cast iron composite fabricated by laser cladding of Ni–Ti–C system. J.^Mater. Process. Technol., 2007, 183(2-3): 380.

[13] Qu S.Y., Wang X.H., Zhang M., Zou Z.D. Microstructure and wear properties of Fe–TiC surface composite coating by laser cladding. J.^Mater. Sci., 2008, 43(5): 1546.

[14] Wang X.H., Zhang M., Du B.S., Qu S.Y., Zou Z.D. Microstructure and wear properties of in situ multiple carbides reinforced Fe based surface composite coating produced by laser cladding. Mater. Sci. Technol., 2010, 26(8): 935.

[15] Wang X.H., Zhang M., Qu S.Y. Development and characterization of (Ti,Mo)C carbides reinforced Fe-based surface composite coating produced by laser cladding. Opt. Lasers Eng., 2010, 48(9): 893.

[16] Park H.I., Nakata K., Tomida S. In situ formation of TiC particulate composite layer on cast iron by laser alloying of thermal sprayed titanium coating. J.^Mater. Sci., 2000, 35(3): 747.

[17] Shi K.Y., Hu S.B., Zheng H.F. Microstructure and fatigue properties of plasma transferred arc alloying TiC-W-Cr on gray cast iron. Surf. Coat. Technol., 2011, 206(6): 1211.

[18] Zeng D.W., Xie C.S., Wang M.Q. In situ synthesis and characterization of Fe_p/Cu composite coating on SAE 1045 carbon steel by laser cladding. Mater. Sci. Eng. A, 2003, 344(1-2): 357.

[19] Agarwal A., Dahotre N.B. Pulsed electrode surfacing of steel with TiC coating: microstructure and wear properties. J. Mater. Eng. Perform., 1999, 8(4): 479.

[20] Wang X.H., Zou Z.D., Qu S.Y., Song S.L. Microstructure and properties of the TiC/Fe-based alloy hardfacing layers. J. Mater. Sci., 2005, 40(14): 3629.

[21] Stott F.H. High-temperature sliding wear of metals. Tribol. Int., 2002, 35(8): 489.

[22] Kesavan D., Kamaraj M. The microstructure and high temperature wear performance of a nickel base hardfaced coating. Surf. Coat. Technol., 2010, 204(24): 4034.

[23] Li Q.H., Savalani M.M., Zhang Q.M., Huo L. High temperature wear characteristics of TiC composite coatings formed by laser cladding with CNT additives. Surf. Coat. Technol., 2014, 239, 206.

[24] Monfared A., Kokabi A.H., Asgari S. Microstructural studies and wear assessments of Ti/TiC surface composite coatings on commercial pure Ti produced by titanium cored wires and TIG process. Mater. Chem. Phys., 2013, 137(3): 959.

[25] Sun N., Shan H.Y., Zhou H., Chen D.R., Li X.Y., Xia W., Ren L.Q. Friction and wear behaviors of compacted graphite iron with different biomimetic units fabricated by laser cladding. Appl. Surf. Sci., 2012, 258(19): 7699.

[26] Mishra R.S. Dislocation-particle interaction at elevated temperatures. JOM, 2009, 61(2): 52.

[27] So H., Yu D.S., Chuang C.Y. Formation and wear mechanism of tribo-oxides and the regime of oxidational wear of steel. Wear, 2002, 253(9-10): 1004.

[28] So H. The mechanism of oxidational wear. Wear, 1995, 184(2): 161.