Characterization of NbSi₂-Al₂O₃ nanocomposite coatings prepared with plasma spraying mechanically alloyed powders

Abstract

The present study characterized NbSi₂-Al₂O₃ nanocomposite powders plasma-sprayed on Ti-6Al-4V substrates. The powders were agglomerated to obtain suitable particle sizes for spraying. The agglomerated powders were then plasma-sprayed using atmospheric plasma spraying. The structural transformations of the powders along with the morphological and mechanical changes of the coatings were examined by X-ray diffraction, scanning electron microscopy, energy dispersive spectroscopy, transmission electron microscopy, and hardness testing. The results showed that after plasma spraying, the grain size increased, and the lattice strain decreased. However, the grain size of this compound after spraying was still in the nanometer range. The coating was uniform and exhibited good adhesion to the substrate. The microhardness and fracture toughness of the nanocomposite coating were higher than those of a nanostructured NbSi₂ coating.

Keywords

nanocomposites / coatings / plasma spraying / mechanical alloying

References

[1] Yeh CL, Chen WH. A comparative study on combustion synthesis of Nb–Si compounds. J. Alloys Compd., 2006, 425(1-2): 216.

[2] Suryanarayana C. Mechanical alloying and milling. Prog. Mater. Sci., 2001, 46(1-2): 1.

[3] Zhu HX, Abbaschian R. In-situ processing of NiAl–alumina composites by thermite reaction. Mater. Sci. Eng. A, 2000, 282(1-2): 1.

[4] Abu Suilik SB, Takeshit K, Kitagawa H, Tetsui T, Hasezaki K. Preparation and high temperature oxidation behavior of refractory disilicide coatings for γ-TiAl intermetallic compounds. Intermetallics, 2007, 15(8): 1084.

[5] Zhu YC, Ding CX. Plasma spraying of porous nanostructured TiO² film. Nanostuct. Mater., 1999, 11(3): 319.

[6] Murty BS, Ranganathan S. Novel materials synthesis by mechanical alloying/milling. Int. Mater. Rev., 1999, 43(3): 101.

[7] Fan GJ, Quan MX, Hu ZQ, Eckert J, Schultz L. In-situ explosive formation of NbSi²-based nanocomposites by mechanical alloying. Scripta Mater., 1999, 41(11): 1147.

[8] Park HK, Shon IJ, Yoon JK, Doh JM, Ko IY, Munir ZA. Simultaneous synthesis and consolidation of nanostructured NbSi2–Si3N4 composite from mechanically activated powders by high-frequency induction-heated combustion. J. Alloys Compd., 2008, 461(1-2): 560.

[9] Yazdani Z, Karimzadeh F, Abbasi MH. Formation mechanism of NbSi²-Al²O³ nanocomposite subject to mechanical alloying. Adv. Powder Technol., 2014, 25(4): 1357.

[10] Williamson GK, Hall WH. X-ray line broadening from filed aluminium and wolfram. Acta Metall., 1953, 1(1): 22.

[11] Smyth RT. Thermal spraying of fine powders, 1973, London, Proceedings of the 7th International Metal Spraying Conference

[12] Eigen N, klassen T, Aust E, Bormann R, Gärtner F. Production of nanocrystalline cermet thermal spray powders for wear resistant coatings by high-energy milling. Mater. Sci. Eng. A, 2003, 356(1-2): 114.

[13] Zimmer A. The effect of cooling rate in thermally sprayed alumina. J. Ceram. Process. Res., 2010, 11(2): 221.

[14] Qian YB, Du LZ, Zhang WG. Preparation of spherical Y2SiO5 powders for thermal-spray coating. Particuology, 2009, 7(5): 368.

[15] Koichi N. Indentation microfracture of ceramics. Ceramics, 1985, 20, 1218.

[16] Ko IY, Kim BR, Nam KS, Moon BM, Lee BS, Shon IJ. Pulsed current activated combustion synthesis and consolidation of ultrafine NbSi2 from mechanically activated powders. Met. Mater. Int., 2009, 15(3): 399.