Corrosion behavior of the friction-stir-welded joints of 2A14-T6 aluminum alloy

Abstract

The corrosion behavior of friction-stir-welded 2A14-T6 aluminum alloy was investigated by immersion testing in immersion exfoliation corrosion (EXCO) solution. Electrochemical measurements (open circuit potential, potentiodynamic polarization curves, and electrochemical impedance spectroscopy), scanning electron microscopy, and energy dispersive spectroscopy were employed for analyzing the corrosion mechanism. The results show that, compared to the base material, the corrosion resistance of the friction-stir welds is greatly improved, and the weld nugget has the highest corrosion resistance. The pitting susceptibility originates from the edge of Al-Cu-Fe-Mn-Si phase particles as the cathode compared to the matrix due to their high self-corrosion potential. No corrosion activity is observed around the θ phase (Al₂Cu) after 2 h of immersion in EXCO solution.

Keywords

aluminum alloys / friction stir welding / joints / corrosion / in-situ observation

References

[1] Mishra R.S., Ma Z.Y. Friction stir welding and processing. Mater. Sci. Eng. R, 2005, 50, 1.

[2] Ericsson M., Sandström R. Influence of welding speed on the fatigue of friction stir welds, and comparison with MIG and TIG. Int. J. Fatigue, 2003, 25(12): 1379.

[3] Squillace A., De Fenzo A., Giorleo G., Bellucci F. A comparison between FSW and TIG welding techniques: modifications of microstructure and pitting corrosion resistance in AA 2024-T3 butt joints. J. Mater. Process. Technol, 2004, 152(1): 97.

[4] Yau Y.H., Hussain A., Lalwani R.K., Chan H.K., Hakimi N. Temperature distribution study during the friction stir welding process of Al2024-T3 aluminum alloy. Int. J. Miner. Metall. Mater, 2013, 20, 779.

[5] Jones M.J., Heurtier P., Desrayaud C., Montheillet F., Allehaux D., Driver J.H. Correlation between microstructure and microhardness in a friction stir welded 2024 aluminium alloy. Scripta Mater, 2005, 52(8): 693.

[6] Paglia C.S., Buchheit R.G. A look in the corrosion of aluminium alloy friction stir welds. Scripta Mater, 2008, 58(5): 383.

[7] Fonda R.W., Pao P.S., Jones H.N., Feng C.R., Connolly B.J., Davenport A.J. Microstructure, mechanical properties, and corrosion of friction stir welded Al 5456, Mater. Sci. Eng. A, 2009, 519(1-2): 1.

[8] Li S.M., Li Y.D., Zhang Y., Liu J.H., Yu M. Effect of intermetallic phases on the anodic oxidation and corrosion of 5A06 aluminum alloy. Int. J. Miner. Metall. Mater, 2015, 22, 167.

[9] Bousquet E., Poulon-Quintin A., Puiggali M., Devos O., Touzet M. Relationship between microstructure, microhardness and corrosion sensitivity of an AA 2024-T3 friction stir welded joint. Corros. Sci, 2011, 53(9): 3026.

[10] Fahimpour V., Sadrnezhaad S.K., Karimzadeh F. Corrosion behavior of aluminum 6061 alloy joined by friction stir welding and gas tungsten arc welding methods. Mater. Des, 2012, 39, 329.

[11] Kang J., Fu R.D., Luan G.H., Dong C.L., He M. In-situ investigation on the pitting corrosion behavior of friction stir welded joint of AA2024-T3 aluminium alloy. Corros. Sci, 2010, 52, 620.

[12] Xu W.F., Liu J.H., Zhu H.Q. Pitting corrosion of friction stir welded aluminium alloy thick plate in alkaline chloride solution. Electrochim. Acta, 2010, 55(8): 2918.

[13] Xu W.F., Liu J.H. Microstructure and pitting corrosion of friction stir welded joints in 2219-O aluminum alloy thick plate. Corros. Sci, 2009, 51(11): 2743.

[14] Proton V., Alexis J., Andrieua E., Delfossec J., Lafonta M.C., Blanc C. Characterisation and understanding of the corrosion behaviour of the nugget in a 2050 aluminium alloy friction stir welding joint. Corros. Sci, 2013, 73, 130.

[15] Tra T.H., Okazaki M., Suzuki K. Fatigue crack propagation behavior in friction stir welding of AA6063-T5: roles of residual stress and microstructure. Int. J. Fatigue, 2012, 43, 23.

[16] Bala Srinivasan P., Dietzel W., Zettler R., dos Santos J.F., Sivan V. Stress corrosion cracking susceptibility of friction stir welded AA7075-AA6056 dissimilar joint. Mater. Sci. Eng. A, 2005, 392(1-2): 292.

[17] Li H.B., Jiang Z.H., Feng H., Zhu H.C., Sun B.H., Li Z. Corrosion behavior of ferritic stainless steel with 15wt% chromium for the automobile exhaust system. Int. J. Miner. Metall. Mater, 2013, 20, 850.

[18] Yang Y., Zhou L.L. Improving corrosion resistance of friction stir welding joint of 7075 aluminum alloy by micro- arc oxidation. J. Mater. Sci. Technol, 2014, 30(12): 1251.

[19] Jariyaboon M., Davenport A.J., Ambat R., Connolly B.J., Williams S.W., Price D.A. Effect of cryogenic cooling on corrosion of friction stir welded AA7010-T7651. nti-Corros. Methods Mater, 2010, 57(2): 83.

[20] Padovani C., Davenport A.J., Connolly B.J., Williams S.W., Siggs E., Groso A., Stampanoni M. Corrosion protection of AA7449-T7951 friction stir welds by laser surface melting with an Excimer laser. Corros. Sci, 2011, 53(12): 3956.

[21] Kalita S.J. Microstructure and corrosion properties of diode laser melted friction stir weld of aluminum alloy 2024 T351. Appl. Surf. Sci, 2011, 257(9): 3985.

[22] Hatamleh O., Singh P.M., Garmestani H. Corrosion susceptibility of peened friction stir welded 7075 aluminum alloy joints. Corros. Sci, 2009, 51(1): 135.

[23] Prasad Rao K., Janaki Ram G.D., Stucker B.E. Improvement in corrosion resistance of friction stir welded aluminum alloys with micro arc oxidation coatings. Scripta Mater, 2008, 58(11): 998.

[24] Surekha K., Murty B.S., Prasad Rao K. Microstructural characterization and corrosion behavior of multipass friction stir processed AA2219 aluminium alloy. Surf. Coat. Technol, 2008, 202(17): 4057.

[25] Surekha K., Murty B.S., Prasad Rao K. Effect of processing parameters on the corrosion behaviour of friction stir processed AA 2219 aluminum alloy. Solid State Sci, 2009, 11(4): 907.

[26] Surekha K., Murty B.S., Prasad Rao K. Comparison of corrosion behaviour of friction stir processed and laser melted AA 2219 aluminium alloy. Mater. Des, 2011, 32(8-9): 4502.

[27] Liu Z., Chong P.H., Butt A.N., Skeldon P., Thompson G.E. Corrosion mechanism of laser-melted AA 2014 and AA 2024 alloys. Appl. Surf. Sci, 2005, 247(1-4): 294.

[28] Liao C.M., Wei R.P. Galvanic coupling of model alloys to aluminum: a foundation for understanding particle-induced pitting in aluminum alloys. Electrochim. Acta, 1999, 45(6): 881.

[29] Blanc C., Freulon A., Lafont M.C., Kihn Y., Mankowski G. Modelling the corrosion behaviour of Al2CuMg coarse particles in copper-rich aluminium alloys. Corros. Sci, 2006, 48(48): 3838.

[30] Shao M.H., Fu Y., Hu R.G., Lin C.J. A study on pitting corrosion of aluminum alloy 2024-T3 by scanning microreference electrode technique. Mater. Sci. Eng. A, 2003, 344(1-2): 323.

[31] Grilli R., Baker M.A., Castle J.E., Dunn B., Watts J.F. Localized corrosion of a 2219 aluminium alloy exposed to a 3.5% NaCl solution. Corros. Sci, 2010, 52(9): 2855.

[32] American Society for TestingMaterials, ASTM G34-01. Standard Test Method for Exfoliation Corrosion Susceptibility in 2XXX and 7XXX Series Aluminum Alloys, 2013

[33] Robinson M.J., Jackson N.C. The influence of grain structure and intergranular corrosion rate on exfoliation and stress corrosion cracking of high strength Al–Cu–Mg alloys. Corros. Sci, 1999, 41(5): 1013.

[34] Conde A., de Damborenea J. Evaluation of exfoliation susceptibility by means of the electrochemical impedance spectroscopy. Corros. Sci, 2000, 42, 1363.

[35] Luo C., Zhou X., Thompson G.E., Hughes A.E. Observations of intergranular corrosion in AA2024-T351: the influence of grain stored energy. Corros. Sci, 2012, 61, 35.

[36] Gabrielli C., Keddam M., Stupnišek-Lisac E., Takenouti H. Etude du comportement anodique de l'interface fer-acide nitrique a l'aide d'une regulation a resistance negative. Electrochim. Acta, 1976, 21(10): 757.