Leaching of lead from zinc leach residue in acidic calcium chloride aqueous solution

Abstract

A process with potentially reduced environmental impacts and occupational hazards of lead-bearing zinc plant residue was studied to achieve a higher recovery of lead via a cost-effective and environmentally friendly process. This paper describes an optimization study on the leaching of lead from zinc leach residue using acidic calcium chloride aqueous solution. Six main process conditions, i.e., the solution pH value, stirring rate, concentration of CaCl₂ aqueous solution, liquid-to-solid (L/S) ratio, leaching temperature, and leaching time, were investigated. The microstructure and components of the residue and tailing were characterized using scanning electron microscopy (SEM) and X-ray diffraction (XRD). On the basis of experimental results, the optimum reaction conditions were determined to be a solution pH value of 1, a stirring rate of 500 r·min⁻¹, a CaCl₂ aqueous solution concentration of 400 g·L⁻¹, a liquid-to-solid mass ratio of 7:1, a leaching temperature of 80°C, and a leaching time of 45 min. The leaching rate of lead under these conditions reached 93.79%, with an iron dissolution rate of 19.28%. Silica did not take part in the chemical reaction during the leaching process and was accumulated in the residue.

Keywords

lead metallurgy / hydrometallurgy / leach residue / zinc / calcium chloride / leaching rate

References

[1] Rusen A., Sunkar A.S., Topkaya Y.A. Zinc and lead extraction from Çinkur leach residues by using hydrometallurgical method. Hydrometallurgy, 2008, 93(1–2): 45.

[2] Jha M.K., Kumar V., Singh R.J. Review of hydrometallurgical recovery of zinc from industrial wastes. Resour. Conserv. Recycl., 2001, 33(1): 1.

[3] Zhu X.F., Li L., Sun X.J., Yang D.N., Gao L.X., Liu J.W., Kumar R.V., Yang J.K. Preparation of basic lead oxide from spent lead acid battery paste via chemical conversion. Hydrometallurgy, 2012, 117–118, 24.

[4] Zhu X.F., He X., Yang J.K., Gao L.X., Liu J.W., Yang D., Sun X.J., Zhang W., Wang Q., Kumar R.V. Leaching of spent lead acid battery paste components by sodium citrate and acetic acid. J. Hazard. Mater., 2013, 250–251, 387.

[5] Zárate-Gutiérrez R., Lapidus G.T. Anglesite (PbSO₄) leaching in citrate solutions. Hydrometallurgy, 2014, 144–145, 124.

[6] Jiang K.Q., Guo Z.H., Xiao X.Y., Zhang L. Extraction of metals from a zinc smelting slag using two-step procedure combining acid and ethylene diaminetetraacetic acid disodium. J. Cent. South Univ., 2012, 19(7): 1808.

[7] Wu Z.H., Dreisinger D.B., Urch H., Fassbender S. Fundamental study of lead recovery from cerussite concentrate with methanesulfonic acid (MSA). Hydrometallurgy, 2014, 142, 23.

[8] Zárate-Gutiérrez R., Lapidus G.T., Morales R.D. Pressure leaching of a lead-zinc-silver concentrate with nitric acid at moderate temperatures between 130 and 170°C. Hydrometallurgy, 2010, 104(1): 8.

[9] Jha M.K., Kumari A., Choubey P.K., Lee J.C., Kumar V., Jeong J.K. Leaching of lead from solder material of waste printed circuit boards (PCBs). Hydrometallurgy, 2012, 121–124, 28.

[10] Pashkov G.L., Mikhlina E.V., Kholmogorov A.G., Mikhlin Y.L. Effect of potential and ferric ions on lead sulfide dissolution in nitric acid. Hydrometallurgy, 2002, 63(2): 171.

[11] Halikia I., Zoumpoulakis L., Christodoulou E. Lead sulphide leaching kinetics in nitric acid solutions. Erzmetall, 2002, 55(3): 166.

[12] Aydogan S., Erdemoglu M., Uçar G., Aras A. Kinetics of galena dissolution in nitric acid solutions with hydrogen peroxide. Hydrometallurgy, 2007, 88(1–4): 52.

[13] Kholmogorov A.G., Pashkov G.L., Mikhlina E.V., Shashina L.V., Zhizhaev A.M. Activation of hydrometallurgical treatment of PbS in nitric solutions. Chem. Sustain. Dev., 2003, 11, 879.

[14] Taylor P.R., Choi Y., Vidal E.E. Fluosilicic acid leaching of galena. Proceedings of the TMS Fall Extraction and Processing Conference, 2003 461.

[15] Zhang Y.L., Yu X.J., Li X.B. Kinetics of simultaneous leaching of Ag and Pb from hydrometallurgical zinc residues by chloride. Rare Met., 2012, 31(4): 402.

[16] Farahmand F., Moradkhani D., Safarzadeh M.S., Rashchi F. Brine leaching of lead-bearing zinc plant residues: process optimization using orthogonal array design methodology. Hydrometallurgy, 2009, 95(3–4): 316.

[17] Guo Z.H., Pan F.K., Xiao X.Y., Zhang L., Jiang K.Q. Optimization of brine leaching of metals from hydrometallurgical residue. Trans. Nonferrous Met. Soc. China, 2010, 20(10): 2000.

[18] Behnajady B., Moghaddam J., Behnajady M.A., Rashchi F. Determination of the optimum conditions for the leaching of lead from zinc plant residues in NaCl–H₂SO₄–Ca(OH)₂ media by the Taguchi method. Ind. Eng. Chem. Res., 2012, 51(10): 3887.

[19] Baba A.A., Adekola F.A., Ghosh M.K., Salubi Y.A., Oyedotun M.O., Rout P.O., Sheik A.R., Pradhan S.R. Leaching of lead from spent motorcycle battery in hydrochloric acid: Part II. Solvent extraction studies. Acta Metall. Slov., 2013, 19(1): 73.

[20] Turan M.D., Altundogan H.S., Tümen F. Recovery of zinc and lead from zinc plant residue. Hydrometallurgy, 2004, 75(1–4): 169.

[21] Sinadinovic D., Kamberovic Šutic A. Leaching kinetics of lead from lead (II) sulphate in aqueous calcium chloride and magnesium chloride solutions. Hydrometallurgy, 1997, 47(1): 137.

[22] Dutrizac J.E., Chen T.T. Mineralogical characterization of leach residues of a pyritic Zn–Pb–Cu–Ag concentrate. Can. Metall. Q., 1987, 26(3): 189.