Effect of equal channel angular extrusion on Al-6063 bending fatigue characteristics

Abstract

The purpose of this investigation was to refine the grains of annealed 6063 aluminum alloy and to improve its yield stress and ultimate strength. This was accomplished via the equal channel angular extrusion (ECAE) process at a temperature of 200°C using route A, with a constant ram speed of 30 mm/min through a die angle of 90° between the die channels for as many as 6 passes. The experiments were conducted on an Avery universal testing machine. The results showed that the grain diameter decreased from 45 μm to 2.8 μm after 6 extrusion passes. The results also indicated that the major improvement in fatigue resistance occurred after the first pass. The subsequent passes improved the fatigue life but at a considerably lower rate. A maximum increase of 1100% in the case of low applied stresses and an approximately 2200% increase in fatigue resistance in the case of high applied stresses were observed after 5 passes. The improvement of fatigue resistance is presumed to be due to (1) a reduction in the size and the number of Si crystals with increasing number of ECAE passes, (2) the aggregation of Cu during the ECAE process, (3) the formation and growth of CuAl2 grains, and (4) grain refinement of the Al-6063 alloy during the ECAE process.

Keywords

aluminum alloys / equal channel angular pressing / bending / fatigue life / grain size / microstructure

References

[1] Segal VM. Materials processing by simple shear. Mater. Sci. Eng. A, 1995, 197(2): 157.

[2] Valiev RZ, Langdon TG. Principles of equal-channel angular pressing as a processing tool for grain refinement. Prog. Mater. Sci., 2006, 51(7): 881.

[3] Skrotzki W, Scheerbaum N, Oertel CG, Arruffat-Massion R, Suwas S. Microstructure and texture gradient in copper deformed by equal channel angular pressing. Acta Mater., 2007, 55(6): 2013.

[4] Niendorf T, Canadinc D, Maier HJ, Karaman I, Yapici GG. Microstructure-mechanical property relationships in ultrafine-grained NbZr. Acta Mater., 2007, 55(19): 6596.

[5] Gabor P, Canadinc D, Maier HJ, Hellmig RJ, Zuberova Z, Estrin J. The Influence of zirconium on the low-cycle fatigue response of ultrafine-grained copper. Metall. Mater. Trans. A, 2007, 38(9): 1916.

[6] Mogucheva A, Kaibyshev R. Fatigue properties of an 1421 aluminum alloy processed by ECAE. J. Phys. Conf. Ser., 2010, 240(1): 012055.

[7] Chen YC, Huang YY, Chang CP, Kao PW. The effect of extrusion temperature on the development of deformation microstructures in 5052 aluminium alloy processed by equal channel angular extrusion. Acta Mater., 2003, 51(7): 2005.

[8] Serban N, Cojocaru VD, Butu M. Mechanical behavior and microstructural development of 6063-T1 aluminum alloy processed by equal-channel angular pressing (ECAP): pass number influence. JOM, 2012, 64(5): 607.

[9] Lapovok R, Loader C, Dalla Torre FH, Semiatin SL. Microstructure evolution and fatigue behavior of 2124 aluminum processed by ECAE with back pressure. Mater. Sci. Eng. A, 2006, 425(1–2): 36.

[10] Niendorf T, Dadda J, Canadinc D, Maier HJ, Karaman I. Monitoring the fatigue-induced damage evolution in ultrafine-grained interstitial-free steel utilizing digital image correlation. Mater. Sci. Eng. A, 2009, 517(1–2): 225.

[11] Chen YJ, Chai YC, Roven HJ, Gireesh SS, Yu YD, Hjelen J. Microstructure and mechanical properties of A_l−xMg alloys processed by room temperature ECAP. Mater. Sci. Eng. A, 2012, 545, 139.

[12] Vinogradov AY, Stolyarov VV, Hashimoto S, Valiev RZ. Cyclic behavior of ultrafine-grain titanium produced by severe plastic deformation. Mater. Sci. Eng. A, 2001, 318(1–2): 163.

[13] Niendorf T, Canadinc D, Maier HJ, Karaman I. On the microstructural stability of ultrafine-grained interstitial-free steel under cyclic loading. Metall. Mater. Trans. A, 2007, 38(9): 1946.

[14] Islamgaliev RK, Kulyasova OB, Mingler B, Zehetbauer MJ, Minkow A. Structure and fatigue properties of the Mg alloy AM60 processed by ECAP. Mater. Sci. Forum, 2008, 584–586, 803.

[15] Estrin Y, Vinogradov A. Fatigue behaviour of light alloys with ultrafine grain structure produced by severe plastic deformation: an overview. Int. J. Fatigue, 2010, 32(6): 898.

[16] Wong MK, Kao PW, Lui JT, Chang CP, Kao PW. Cyclic deformation of ultrafine-grained aluminum. Acta Mater, 2007, 55(2): 715.

[17] Niendorf T, Maier HJ, Canadinc D, Yapici GG, Karaman I. Improvement of the fatigue performance of an ultrafine-grained Nb-Zr alloy by nano-sized precipitates formed by internal oxidation. Scripta Mater, 2008, 58(7): 571.

[18] Zeng RC, Han EH, Ke W, Dietzel W, Kainer KU, Atrens A. Influence of microstructure on tensile properties and fatigue crack growth in extruded magnesium alloy AM60. Int. J. Fatigue, 2010, 32(2): 411.

[19] Hockauf M, Meyer LW, Halle T, Kuprin C, Hietschold M, Schulze S, Krüger L. Mechanical properties and microstructural changes of ultrafine-grained AA6063T6 during high-cycle fatigue. Int. J. Mater. Res., 2006, 97(10): 1392.

[20] Warmuzek M. Aluminum-Silicon Casting Alloys: An Atlas of Microfractographs, 2004 39.