Effects of magnetic fields on Fe-Si composite electrodeposition

Abstract

Coatings containing Fe-Si particles were electrodeposited on 3.0wt% Si steel sheets under magnetic fields. The effects of magnetic flux density (MFD), electrode arrangement and current density on the surface morphology, the silicon content in the coatings and the cathode current efficiency were investigated. When a magnetic field was applied parallel to the current and when the MFD was less than 0.5 T, numerous needle-like structures appeared on the coating surface. With increasing MFD, the needle-like structures weakened and were transformed into dome-shaped structures. Meanwhile, compared to results obtained in the absence of a magnetic field, the silicon content in the coatings significantly increased as the MFD was increased for all of the samples obtained using a vertical electrode system. However, in the case of an aclinic electrode system, the silicon content decreased. Furthermore, the cathode current efficiency was considerably diminished when a magnetic field was applied. A possible mechanism for these phenomena was discussed.

Keywords

composite coatings / electrodeposition / silicon steel / magnetic field / surface morphology / silicon content / magnetohydrodynamics

References

[1] Park BH, Kang BS, Bu SD, Noh TW, Lee J, Jo W. Lanthanum-substituted bismuth titanate for use in non-volatile memories. Nature, 1999, 401(6754): 682.

[2] Ros T, Houbaert Y, Fischer O, Schneider J. Thermomechanical processing of high Si-steel (up to 6.3% Si). IEEE Trans. Magn., 2001, 37(4): 2321.

[3] Fiorillo F. Advances in Fe-Si properties and their interpretation. J. Magn. Magn. Mater., 1996, 157–158, 428.

[4] Fu HD, Zhang ZH, Pan HJ, Mo YK, Xie JX. Warm/cold rolling processes for producing Fe-6.5wt% Si electrical steel with columnar grains. Int. J. Miner. Metall. Mater., 2013, 20, 535.

[5] Zhou PW, Zhong YB, Wang H, Long Q, Li F, Sun ZQ, Dong LC, Fan LJ. Effects of parallel magnetic field on electrocodeposition behavior of Fe/nano-Si particles composite electroplating. Appl. Surf. Sci., 2013, 282, 624.

[6] Pan YJ, Zhang H, Wu XJ. Study on composite electroplating technology of iron with powder of silicon or ferrosilicon. Plat. Finish., 2004, 26(6): 13

[7] Mohan S, Saravanan G, Bund A. Role of magnetic forces in pulse electrochemical deposition of Ni-nanoAl₂O₃ composites. Electrochim. Acta, 2012, 64, 94.

[8] Sci. Technol. Adv. Mater., 2008, 9(2art.024208)

[9] Tschulik K, Koza JA, Uhlemann M, Gebert A, Schultz L. Effects of well-defined magnetic field gradients on the electrodeposition of copper and bismuth. Electrochem. Commun., 2009, 11(11): 2241.

[10] Tschulik K, Sueptitz R, Koza J, Uhlemann M, Mutschke G, Weier T, Gebert A, Schultz L. Studies on the patterning effect of copper deposits in magnetic gradient fields. Electrochim. Acta, 2010, 56(1): 297.

[11] Wang C, Zhong YB, Wang J, Wang ZQ, Ren WL, Lei ZS, Ren ZM. Effect of magnetic field on electroplating Ni/nano-Al₂O₃ composite coating. J. Electroanal. Chem., 2009, 630, 42.

[12] Feng QY, Li TJ, Zhang ZT, Zhang J, Liu M, Jin JZ. Preparation of nanostructured Ni/Al₂O₃ composite coatings in high magnetic field. Surf. Coat. Technol., 2007, 201(14): 6247.

[13] Hu F, Chan KC, Qu NS. Effect of magnetic field on electrocodeposition behavior of Ni-SiC composites. J. Solid State Electrochem., 2007, 11(2): 267.

[14] Yamada T, Asai S. Distribution control of dispersed particles in a film fabricated by composite plating method using a high magnetic field. J. Jpn. Inst. Met., 2005, 69(2): 257.

[15] Yamada T, Asai S. Development of a new composite plating method orienting dispersed materials by use of a high magnetic field. J. Jpn. Inst. Met., 2001, 65(10): 910

[16] Jiao F, Qu NS, Zhu ZW, Li XL. Preparation of nano-barium ferrite/CoNi alloy magnetic coating by composite electrodeposition. Mater. Mech. Eng., 2009, 33(12): 5

[17] Hinds G, Coey JMD, Lyons MEG. Influence of magnetic forces on electrochemical mass transport. Electrochem. Commun., 2001, 3(5): 215.

[18] Peipmann R, Thomas J, Bund A. Electrocodeposition of nickel-alumina nanocomposite films under the influence of static magnetic fields. Electrochim. Acta, 2007, 52(19): 5808.

[19] Bund A, Koehler S, Kuehnlein HH, Plieth W. Magnetic field effects in electrochemical reactions. Electrochim. Acta, 2003, 49(1): 147.

[20] Zhou PW, Zhong YB, Wang H, Fan LJ, Dong LC, Li F, Long Q, Zheng TX. Behavior of Fe/nano-Si particles composite electrodeposition with a vertical electrode system in a static parallel magnetic field. Electrochim. Acta, 2013, 111, 126.

[21] Long Q, Zhong YB, Li F, Liu CM, Zhou JF, Fan LJ, Li MJ. Effect of static magnetic field on the morphology and Si content of Fe-Si composite coating. Acta Metall. Sin., 2013, 49(10): 1201

[22] Wang C, Zhong YB, Ren WL, Lei ZS, Ren ZM, Jia J, Jiang AR. Effects of parallel magnetic field on electrocodeposition behavior of Ni/nanoparticle composite electroplating. Appl. Surf. Sci., 2008, 254(18): 5649.

[23] Hovestad A, Janssen LJJ. Electrochemical codeposition of inert particles in a metallic matrix. J. Appl. Electrochem., 1995, 25(6): 519.

[24] Hilbert F, Miyoshi Y, Eichkorn G, Lorenz WJ. Correlations between the kinetics of electrolytic dissolution and deposition of iron. J. Electrochem. Soc., 1971, 118(12): 1927.

[25] Matsushima H, Nohira T, Mogi I, Ito Y. Effects of magnetic fields on iron electrodeposition. Surf. Coat. Technol., 2004, 179(2–3): 245.