Fabrication of an r-Al₂Ti intermetallic matrix composite reinforced with α-Al₂O₃ ceramic by discontinuous mechanical milling for thermite reaction

Abstract

In this study, a powder mixture with an Al/TiO₂ molar ratio of 10/3 was used to form an r-Al₂Ti intermetallic matrix composite (IMC) reinforced with α-Al₂O₃ ceramic by a novel milling technique, called discontinuous mechanical milling (DMM) instead of milling and ignition of the produced thermite. The results of energy dispersive X-ray spectroscopy (EDX) and X-ray diffraction (XRD) of samples with varying milling time indicate that this fabrication process requires considerable mechanical energy. It is shown that Al₂Ti-Al₂O₃ IMC with small grain size was produced by DMM after 15 h of ball milling. Peaks for γ-TiAl as well as Al₂Ti and Al₂O₃ are observed in XRD patterns after DMM followed by heat treatment. The microhardness of the DMM-treated composite produced after heat treatment was higher than Hv 700.

Keywords

composite materials / intermetallics / alumina / titanium aluminide / ball milling / thermite reaction process

References

[1] Yamaguchi M, Inui H, Ito K. High-temperature structural intermetallics. Acta Mater., 2000, 48, 307.

[2] Naplocha K, Granat K. Microwave activated combustion synthesis of porous Al-Ti structures for composite reinforcing. J. Alloys Compd., 2009, 486, 178.

[3] Hsu CW, Chao CC. Effect of heat treatments on in-situ Al₂O₃/TiAl₃ composites produced from squeeze casting of TiO₂/A356 composites. Metall. Mater. Trans. B, 2002, 33, 31.

[4] Ying DY, Zhang DL, Newby M. Solid-state reactions during heating mechanically milled Al/TiO₂ composite powders. Metall. Mater. Trans. A, 2004, 35, 2115.

[5] Welham NJ. Mechanical activation of the formation of an alumina-titanium trialuminide composite. Intermetallics, 1998, 6, 363.

[6] Welham NJ. Mechanical activation of the solid-state reaction between Al and TiO₂. Mater. Sci. Eng. A, 1998, 255, 81.

[7] Gheorghe I, Rack HJ. Reactive infiltration of 25 vol Pct TiO₂/Al composites. Metall. Mater. Trans. A, 2002, 33, 2155.

[8] Feng CF, Froyen L. Formation of Al₃Ti and Al₂O₃ from an Al-TiO₂ system for preparing in-situ aluminium matrix composites. Compos. Part A, 2000, 31, 385.

[9] Alamolhoda S, Heshmati-Manesh S, Ataie A. Role of intensive milling in mechano-thermal processing of TiAl/Al₂O₃ nano-composite. Adv. Powder Technol., 2012, 23(3): 343.

[10] Travitzky N, Gotman I, Claussen N. Alumina-Ti aluminide interpenetrating composites: microstructure and mechanical properties. Mater. Lett., 2003, 57, 3422.

[11] Yeh CL, Li RF. Formation of TiAl-Ti₅Si₃ and TiAl-Al₂O₃ in situ composites by combustion synthesis. Intermetallics, 2008, 16, 64.

[12] Horvitz D, Gotman I, Gutmanas EY, Claussen N. In situ processing of dense Al₂O₃-Ti aluminide interpenetrating phase composites. J. Eur. Ceram. Soc., 2002, 22, 947.

[13] Forouzanmehr N, Karimzadeh F, Enayati MH. Synthesis and characterization of TiAl/α-Al₂O₃ nanocomposite by mechanical alloying. J. Alloys Compd., 2009, 478, 257.

[14] Fan RH, Lü HL, Sun KN, Wang WX, Yi XB. Kinetics of thermite reaction in Al-Fe₂O₃ system. Thermochim. Acta, 2006, 440, 129.

[15] Fan RH, Liu B, Zhang JD, Bi JQ, Yin YS. Kinetic evaluation of combustion synthesis 3TiO₂ + 7Al → 3TiAl + 2Al₂O₃ using non-isothermal DSC method. Mater. Chem. Phys., 2005, 91, 140.

[16] Kamali AR, Nejad I B, Aboutalebi MR, Razavizadeh H. Effect of ball milling on reaction between TiO₂ and Al. Russ. J. Non Ferrous Met., 2009, 50(3): 246.

[17] Liu Z, Raynova S, Zhang D, Gabbitas B. Study on the self sustained reactions in an Al-TiO₂ composite powder produced by high-energy mechanical milling. Mater. Sci. Eng. A, 2007, 449–451, 1107.

[18] Palm M, Zhang LC, Stein F, Sauthoff G. Phases and phase equilibria in the Al-rich part of the Al-Ti system above 900°C. Intermetallics, 2002, 10, 523.

[19] Mousavian R T, Sharafi S, Shariat MH. Microwave-assisted combustion synthesis in a mechanically activated Al-TiO₂-H₃BO₃ system. Int. J. Refract. Met. Hard Mater., 2011, 29, 281.

[20] Mousavian R T, Sharafi S, Roshan MR, Shariat MH. Effect of mechanical activation of reagents’ mixture on the high-temperature synthesis of Al₂O₃-TiB₂ composite powder. J. Therm. Anal. Calorim., 2011, 104(3): 1063.