Bonding characteristics of the Al₂O₃-metal composite coating fabricated onto carbon steel by combustion synthesis

Abstract

The fabrication of an alumina-metal composite coating onto a carbon steel substrate by using a self-propagating high-temperature synthesis technique was demonstrated. The effects of the type and thickness of the pre-coated layer on the binding structure and surface quality of the coating were systematically investigated. The macrostructure, phase composition, and bonding interface between the coating and the substrate were investigated by scanning electronic microscopy (SEM), X-ray diffraction (XRD), and energy-dispersive X-ray spectrometry (EDS). The diffraction patterns indicated that the coating essentially consisted of α-Al₂O₃, Fe(Cr), and FeO·Al₂O₃. With an increase in the thickness of the pre-coated working layer, the coating became more smooth and compact. The transition layer played an important role in enhancing the binding between the coating and the substrate. When the pre-coated working layer was 10 mm and the pre-coated transition layer was 1 mm, a compact structure and metallurgical bonding with the substrate were obtained. Thermal shock test results indicated that the ceramic coating exhibited good thermal shock resistance when the sample was rapidly quenched from 800°C to room temperature by plunging into water.

Keywords

carbon steel / combustion synthesis / composite coatings / phase composition / morphology / thermal shock resistance

References

[1] Merzhanov AG. History and recent developments in SHS. Ceram. Int., 1995, 21(5): 371.

[2] Merzhanov AG. Fundamentals, achievements, and perspectives for development of solid-flame combustion. Russ. Chem. Bull., 1997, 46(1): 1.

[3] Varma A, Mukasyan AS. Combustion synthesis of advanced materials: fundamentals and applications. Korean J. Chem. Eng., 2004, 21(2): 527.

[4] Mukasyan AS, White JDE. Combustion joining of refractory materials. Int. J. Self Propag. High Temp. Synth., 2007, 16(3): 154.

[5] Morsi K. The diversity of combustion synthesis processing: a review. J. Mater. Sci., 2012, 47(1): 68.

[6] La PQ, Bai MW, Xue QJ, Liu WM. A study of Ni₃Al coating on carbon steel surface via the SHS casting route. Surf. Coat. Technol., 1999, 113(1–2): 44.

[7] Wei MX, Wang SQ, Wang F, Cui XH. A thermal explosion process to fabricate an intermetallic matrix composite coating on a steel. Mater. Des., 2009, 30(8): 3041.

[8] Wang G, Jiang SQ, Wang ZH, Cai D, Yi Y, Zhou ZH. Self-propagating high-temperature synthesis of Al₂O₃-TiB2 coatings by aluminothermic reactions. Rare Met. Mater. Eng., 2012, 41, 215

[9] Wang CH, Wang ZH, Zhou ZH, Jiang SQ, Xue XF, Yao JJ. Fabrication and characterization of Al₂O₃-metal composite coating on steel plate with nonpressure combustion synthesis. Rare Met., 2013, 32(4): 390.

[10] Odawara O. Ceramic lined pipes produced by a centrifugal-thermit process. Trans. Jpn. Inst. Met., 1985, 26(8): 578.

[11] Odawara O, Ikeuchi J. Alumina and zirconia ceramic lined pipes produced by a centrifugal-thermit process. Trans. Jpn. Inst. Met., 1986, 27(9): 702.

[12] Odawara O. Long ceramic-lined pipes produced by a centrifugal-thermit process. J. Am. Ceram. Soc., 1990, 73(3): 629.

[13] Sun SG, Zhu Y, Ni HJ, Huang MY. Research progress in ceramic-lined pipe prepared by self-propagating high temperature synthesis. Hot Work. Technol., 2009, 38(24): 48

[14] Mahmoodian R, Rahbari RG, Hamdi M, Hassan MA, Sparham M. The effects of an unexpected ceramic coating phase at the head of a pipe on joining and postprocessing of a ceramic-lined composite pipe. JOM, 2013, 65(1): 80.

[15] Zhang JJ, Wang ZH, Lin PH, Yuan HB, Zhou ZH, Jiang SQ. Effect of vacuum annealing on the characteristics of plasma sprayed Al₂O₃-13wt.% TiO₂ coatings. J. Therm. Spray Technol., 2012, 21(5): 782.

[16] Liu AG, Guo MH, Gao JS, Zhao MH. Influence of bond coat on shear adhesion strength of erosion and thermal resistant coating for carbon fiber reinforced thermosetting polyimide. Surf. Coat. Technol., 2006, 201(6): 2696.

[17] Technical Committee on Non-Ferrous Metals, JIS H8304-2007. Ceramic Sprayed Coatings, 2007, Japan, JP-JISC

[18] Li WG, Zhou HP, Zhao YL, Li Y. An experimental study on combustion synthesizing of plane ceramic coating. Key. Eng. Mater., 2002, 224–226, 609.

[19] Merzhanov AG. Theory and practice of SHS: worldwide state of the art and the newest results. Int. J. SHS, 1993, 2(2): 113

[20] An ZJ. Synthesis Mechanism and Preparation of Electric Field-activated FGM, 2005, Shanxi, Taiyuan University of Technology, 6

[21] Sierra C, Vázquez AJ. NiAl coating on carbon steel with an intermediate Ni gradient layer. Surf. Coat. Technol., 2006, 200(14–15): 4383.

[22] Wang DQ. Effects of additives on combustion synthesis of Al₂O₃-TiB2 ceramic composite. J. Eur. Ceram. Soc., 2009, 29(8): 1485.

[23] Jiao AY, Wang FH, Yang SQ. Study on making ceramic composite steel plate by SHS process. Adv. Mater. Res., 2011, 299–300, 806.

[24] Du ZZ, Fu HG, Fu HF, Xiao Q. A study of ceramic-lined compound copper pipe produced by SHS-centrifugal casting. Mater. Lett., 2005, 59(14–15): 1853.

[25] Aksaf IA, Pask JA. Stable and metastable equilibria in the system SiO₂-Al₂O₃. J. Am. Ceram. Soc., 1975, 58(11–12): 507.

[26] Wang Y, Tian W, Yang Y. Thermal shock behavior of nanostructured and conventional Al₂O₃/13wt% TiO₂ coatings fabricated by plasma spraying. Surf. Coat. Technol., 2007, 201(18): 7746.