Orientation variation along growth direction of millimeter free-standing CVD diamond thinned by mechanical grinding

Abstract

A free-standing diamond film with millimeter thickness prepared by DC arc plasma jet was thinned successively by mechanical grinding. The orientation and quality of the diamond films with different thicknesses were characterized by X-ray diffraction and Raman spectroscopy, respectively. The results show a random grain-orientation distribution during the initial growth stage. As the film thickness increases, the preferred orientation of the diamond film changes from (111) to (220), due to the competitive growth mechanism. Twinning generated during the nucleation stage appears to stabilize the preferential growth along the 〈110〉 direction. The interplanar spacing of the (220) plane is enlarged as the film thickness increases, which is caused by the increase of non-diamond-phase carbon and impurities under the cyclic gas. In addition, the quality of the diamond film is barely degraded during the growth process. Furthermore, the peak shift demonstrates a significant inhomogeneity of stress along the film growth direction, which results from competitive growth.

Keywords

diamond films / chemical vapor deposition / grinding / orientation / growth mechanisms / quality

References

[1] Malshe AP, Park BS, Brown WD, Naseem HA. A review of techniques for polishing and planarizing chemically vapor-deposited (CVD) diamond films and substrates. Diamond Relat. Mater., 1999, 8, 1198.

[2] Schwander M, Partes K. A review of diamond synthesis by CVD processes. Diamond Relat. Mater., 2011, 20, 1287.

[3] Wei JJ, Zhu XP, Lü FX, Ni JR. Comparative study of oxidation ability between boron-doped diamond (BDD) and lead oxide (PbO₂) electrodes. Int. J. Miner. Metall. Mater., 2011, 18(5): 589.

[4] Liu JL, Li CM, Zhu RH, Chen LX, Wang JJ, Feng ZH. Ohmic contact properties of p-type surface conductive layer on H-terminated diamond films prepared by DC arc jet CVD. Int. J. Miner. Metall. Mater., 2013, 20(8): 802.

[5] Ding GF, Mao HP, Cai YL, Zhang YH, Yao X, Zhao XL. Micromachining of CVD diamond by RIE for MEMS applications. Diamond Relat. Mater., 2005, 14, 1543.

[6] Lamara T, Belmahi M, Elmazria O, Le Brizoual L, Bougdira J, Rémy M, Alnot P. Freestanding CVD diamond elaborated by pulsed-microwave-plasma for ZnO/diamond SAW devices. Diamond Relat. Mater., 2004, 13, 581.

[7] Manfredotti C. CVD diamond detectors for nuclear and dosimetric applications. Diamond Relat. Mater., 2005, 14, 531.

[8] Chen H, Jia CC, Li SJ, Jia X, Yang X. Selective interfacial bonding and thermal conductivity of diamond/Cu-alloy composites prepared by HPHT technique. Int. J. Miner. Metall. Mater., 2012, 19(4): 364.

[9] Ali M, Ürgen M. Surface morphology, growth rate and quality of diamond films synthesized in hot filament CVD system under various methane concentrations. Appl. Surf. Sci., 2011, 257, 8420.

[10] Yang JX, Zhang HD, Li CM, Chen GC, Lu FX, Tang WZ, Tong YM. Effects of nitrogen addition on morphology and mechanical property of DC arc plasma jet CVD diamond films. Diamond Relat. Mater., 2004, 13, 139.

[11] Weng J, Wang JH, Dai SY, Xiong LW, Man WD, Liu F. Preparation of diamond films with controllable surface morphology, orientation and quality in an overmoded microwave plasma CVD chamber. Appl. Surf. Sci., 2013, 276, 529.

[12] Lu FX, Tang WZ, Huang TB, Liu JM, Song JH, Yu WX, Tong YM. Large area high quality diamond film deposition by high power DC arc plasma jet operating at gas recycling mode. Diamond Relat. Mater., 2001, 10, 1551.

[13] Lu FX, Tang WZ, Zhong GF, Huang TB, Liu JM, Li GH, Lo TL, Zhang YG, Sun ZL, Du SM, He QY, Wang SI. Economical deposition of a large area of high quality diamond film by a high power DC arc plasma jet operating in a gas recycling mode. Diamond Relat. Mater., 2000, 9, 1655.

[14] Li CM, Wang LM, Chen LX, Liu Z, Hei LF, Lu FX. Free-standing diamond films deposited by DC arc plasma jet on graphite substrates with a destroyable Ti interlayer. Diamond Relat. Mater., 2009, 18, 1348.

[15] Wild C, Herres N, Koidl P. Texture formation in polycrystalline diamond films. J. Appl. Phys., 1990, 68, 973.

[16] Li ZD, Wang L, Suzuki T, Argoitia A, Pirouz P, Angus JC. Orientation relationship between chemical vapor deposited diamond and graphite substrates. J. Appl. Phys., 1993, 73, 711.

[17] Frenklach M, Wang H. Detailed surface and gas-phase chemical kinetics of diamond deposition. Phys. Rev. B, 1991, 43(2): 1520.

[18] Sails SR, Gardiner DJ, Bowden M, Savage J, Rodway D. Monitoring the quality of diamond films using Raman spectra excited at 514.5 nm and 633 nm. Diamond Relat. Mater., 1996, 5, 589.

[19] van Bouwelen FM, van Enckevort WJP. A simple model to describe the anisotropy of diamond polishing. Diamond Relat. Mater., 1999, 8, 840.