Production of HfO₂ thin films using different methods: chemical bath deposition, SILAR and sol-gel process

Abstract

Hafnium oxide thin films (HOTFs) were successfully deposited onto amorphous glasses using chemical bath deposition, successive ionic layer absorption and reaction (SILAR), and sol-gel methods. The same reactive precursors were used for all of the methods, and all of the films were annealed at 300°C in an oven (ambient conditions). After this step, the optical and structural properties of the films produced by using the three different methods were compared. The structures of the films were analyzed by X-ray diffraction (XRD). The optical properties are investigated using the ultraviolet-visible (UV-VIS) spectroscopic technique. The film thickness was measured via atomic force microscopy (AFM) in the tapping mode. The surface properties and elemental ratios of the films were investigated and measured by scanning electron microscopy and energy-dispersive X-ray spectroscopy (EDX). The lowest transmittance and the highest reflectance values were observed for the films produced using the SILAR method. In addition, the most intense characteristic XRD peak was observed in the diffraction pattern of the film produced using the SILAR method, and the greatest thickness and average grain size were calculated for the film produced using the SILAR method. The films produced using SILAR method contained fewer cracks than those produced using the other methods. In conclusion, the SILAR method was observed to be the best method for the production of HOTFs.

Keywords

hafnium oxide / thin films / optical properties / structural properties / chemical deposition / absorption / sol-gel process

References

[1] Wilk GD, Wallace RM, Anthony JM. High-κ gate dielectrics: Current status and materials properties considerations. J. Appl. Phys., 2001, 89(10): 5243.

[2] Kingdom AI, Maria JP, Streiffer SK. Alternative dielectrics to silicon dioxide for memory and logic devices. Nature, 2000, 406, 1032.

[3] Batson PE. Conduction bandstructure in strained silicon by spatially resolved electron energy loss spectroscopy. Ultramicroscopy, 1995, 59(1–4): 63.

[4] M.P. Agustin, G. Bersuker, B. Foran, L.A. Boatner, and S. Stemmer, Scanning transmission electron microscopy investigations of interfacial layers in HfO₂ gate stacks, J. Appl. Phys., 100(2006), art. No. 024103.

[5] Muller DA, Sorsch T, Moccio S, Baumann FH, Evans-Lutterodt K, Timp G. The electronic structure at the atomic scale of ultrathin gate oxides. Nature, 1999, 399, 758.

[6] Martinez FL, Toledano-Luque M, Gandia JJ, Cárabe J, Bohne W, Röhrich J, Strub E, Mártil I. Optical properties and structure of HfO₂ thin films grown by high pressure reactive sputtering. J. Phys. D, 2007, 40, 5256.

[7] M.C. Cheynet, S. Pokrant, F.D. Tichelaar, and J.L. Rouvière, Crystal structure and band gap determination of HfO₂ thin films, J. Appl. Phys., 101(2007), art. No. 054101.

[8] Kozuka H. Handbook of Sol-Gel Science and Technology Processing, Characterization and Applications, 2005, New York, Kluwer Academic Publishers, 247

[9] N.V. Nguyen, A.V. Davydov, and D. Chandler-Horowitz, Sub-bandgap defect states in polycrystalline hafnium oxide and their suppression by admixture of silicon, Appl. Phys. Lett., 87(2005), art. No. 192903.

[10] He G, Zhu LQ, Liu M, Fang Q, Zhang LD. Optical and electrical properties of plasma-oxidation derived HfO₂ gate dielectric films. Appl. Surf. Sci., 2007, 253(7): 3413.

[11] Jiang K, Anderson JT, Hoshino K, Li D, Wager JF, Keszler DA. Low-energy path to dense HfO₂ thin films with aqueous precursor. Chem. Mater., 2011, 23(4): 945.

[12] Teren AR, Thomas R, He JQ, Ehrhart P. Comparison of precursors for pulsed metal-organic chemical vapor deposition of HfO₂ high-K dielectric thin films. Thin Solid Films, 2005, 478(1–2): 206.

[13] Chin. Phys. B, 2010, 19(8)

[14] H. Shimizu, D. Nemoto, M. Ikeda, and T. Nishide, Characteristics of sol-gel-derived and crystallized HfO₂ thin films dependent on sol solution, Jpn. J. Appl. Phys., 49(2010), art. No. 121502.

[15] Hu H, Zhu CX, Lu YF, Wu YH, Liew T, Li MF, Cho BJ, Choi WK, Yakolev N. Physical and electrical characterization of HfO₂ metal-insulator-metal capacitors for Si analog circuit applications. J. Appl. Phys., 2003, 94(1): 551.

[16] İ.A. Kariper and T. Özpozan, Cobalt xanthate thin film with chemical bath deposition, J. Nanomater., 2013(2013), art. No. 139864.

[17] Pathan HM, Lokhande CD. Deposition of metal chalcogenide thin films by successive ionic layer adsorption and reaction (SILAR) method. Bull. Mater. Sci., 2004, 27(2): 85.