Effect of scanning speed during PTA remelting treatment on the microstructure and wear resistance of nodular cast iron

Abstract

The surface of nodular cast iron (NCI) with a ferrite substrate was rapidly remelted and solidified by plasma transferred arc (PTA) to induce a chilled structure with high hardness and favorable wear resistance. The effect of scanning speed on the microstructure, microhardness distribution, and wear properties of PTA-remelted specimens was systematically investigated. Microstructural characterization indicated that the PTA remelting treatment could dissolve most graphite nodules and that the crystallized primary austenite dendrites were transformed into cementite, martensite, an interdendritic network of ledeburite eutectic, and certain residual austenite during rapid solidification. The dimensions of the remelted zone and its dendrites increase with decreased scanning speed. The microhardness of the remelted zone varied in the range of 650 HV_0.2 to 820 HV_0.2, which is approximately 2.3–3.1 times higher than the hardness of the substrate. The wear resistance of NCI was also significantly improved after the PTA remelting treatment.

Keywords

nodular cast iron / surface treatment / plasma arc remelting / scanning speed / microhardness / wear resistance

References

[1] Alabeedi KF, Abboud JH, Benyounis KY. Microstructure and erosion resistance enhancement of nodular cast iron by laser melting. Wear, 2009, 266(9–10): 925.

[2] Abboud JH. Microstructure and erosion characteristic of nodular cast iron surface modified by tungsten inert^gas. Mater. Des., 2012, 35, 677.

[3] Benyounis KY, Fakron OMA, Abboud JH, Olabi AG, Hashmi MJS. Surface melting of nodular cast iron by Nd-YAG laser and TIG. J. Mater. Process. Technol., 2005, 170(1–2): 127.

[4] Dai WS, Chen LH, Lui TS. SiO₂ particle erosion of spheroidal graphite cast iron after surface remelting by the plasma transferred arc process. Wear, 2001, 248(1–2): 201.

[5] Amirsadeghi A, Heydarzadeh Sohi M. Comparison of the influence of molybdenum and chromium TIG surface alloying on the microstructure, hardness and wear resistance of ADI. J. Mater. Process. Technol., 2008, 201(1–3): 673.

[6] Grum J, Šturm R. Microstructure analysis of nodular iron 400–12 after laser surface melt hardening. Mater. Charact., 1996, 37(2–3): 81.

[7] Shi KY, Hu SB, Xu W, Huang QW. Surface treatment of 45 steels by plasma beam alloying and plasma surface quenching. Adv. Mater. Res., 2010, 129–131, 1109.

[8] Yan M, Zhu WZ. Surface treatment of 45 steel by plasma-arc melting. Surf. Coat. Technol., 1997, 91(3): 183.

[9] Bourithis L, Papadimitriou GD. The effect of microstructure and wear conditions on the wear resistance of steel metal matrix composites fabricated with PTA alloying technique. Wear, 2009, 266(11–12): 1155.

[10] Huang QW, Hu SB, Wang AH. Research development of plasma beam surface strengthening technology. Heat. Treat. Met., 2011, 36(8): 1

[11] Roy A, Manna I. Laser surface engineering to improve wear resistance of austempered ductile iron. Mater. Sci. Eng. A, 2001, 297(1–2): 85.

[12] Heydarzadeh Sohi M, Karshenas G, Boutorabi SMA. Electron beam surface melting of as cast and austempered ductile irons. J. Mater. Process. Technol., 2004, 153–154, 199.

[13] Yan M, Zhu WZ, Luo W, Zhang XB, Zhou BC, Zhao XB. Effect of plasma-arc scanning on the wear resistance of gray iron. Mater. Lett., 2002, 56(1–2): 14.

[14] Tong X, Zhou H, Ren LQ, Zhang ZH, Cui RD, Zhang W. Thermal fatigue characteristics of gray cast iron with non-smooth surface treated by laser alloying of Cr powder. Surf. Coat. Technol., 2008, 202(12): 2527.

[15] Karamış MB, Yıldızlı K. Surface modification of nodular cast iron: A comparative study on graphite elimination. Mater. Sci. Eng. A, 2010, 527(20): 5225.

[16] Heydarzadeh Sohi M, Ebrahimi M, Ghasemi HM, Shahripour A. Microstructural study of surface melted and chromium surface alloyed ductile iron. Appl. Surf. Sci., 2012, 258(19): 7348.

[17] Grum J, Šturm R. Comparison of measured and calculated thickness of martensite and ledeburite shells around graphite nodules in the hardened layer of nodular iron after laser surface remelting. Appl. Surf. Sci., 2002, 187(1–2): 116.

[18] Wang JS, Meng HM, Yu HY, Fan ZS, Sun DB. Characterization and wear behavior of WC-0.8Co coating on cast steel rolls by electro-spark deposition. Int. J. Miner. Metall. Mater., 2009, 16(6): 707

[19] Sun GF, Zhou R, Li P, Feng AX, Zhang YK. Laser surface alloying of C-B-W-Cr powders on nodular cast iron rolls. Surf. Coat. Technol., 2011, 205(8–9): 2747.

[20] Sahin Y, Kilicli V, Ozer M, Erdogan M. Comparison of abrasive wear behavior of ductile iron with different dual matrix structures. Wear, 2010, 268(1–2): 153.