Effect of aluminum oxide on the compressive strength of pellets

Abstract

Analytical-reagent-grade Al₂O₃ was added to magnetite ore during the process of pelletizing, and the methods of mercury intrusion, scanning electron microscopy, and image processing were used to investigate the effect of Al₂O₃ on the compressive strength of the pellets. The results showed that, as the Al₂O₃ content increased, the compressive strength of the pellets increased slightly and then decreased gradually. When a small amount of Al₂O₃ was added to the pellets, the Al₂O₃ combined with fayalite (2FeO·SiO₂) and the aluminosilicate (2FeO·2Al₂O₃·5SiO₂) was generated, which releases some iron oxide and reduces the inhibition of fayalite to the solid phase of consolidation. When Al₂O₃ increased sequentially, high melting point of Al₂O₃ particles hinder the oxidation of Fe₃O₄ and the recrystallization of Fe₂O₃, making the internal porosity of the pellets increase, which leads to the decrease in compressive strength of the pellets.

Keywords

magnetite / ore pellets / alumina / compressive strength / porosity / microanalysis

References

[1] Li ZY, Yu QY. BF slag structure adjustment for high Al₂O₃ slag smelting. Baosteel Technol., 2012 1

[2] Long F. The Effection on Ironmaking Raw Materials and Metallurgical Process by High Content of Al₂O₃ Iron Ore, 2006, Wuhan, Wuhan University of Technology, 1

[3] Fu JY, Tao J, Zhu DQ. Sintering and Pelleting, 1996, Changsha, Center South University of Technology Press, 281

[4] Ye KW. Heavily push forward the pelletizing production in our country. Sintering Pelleting, 2007, 32(5): 1

[5] Zhang YP, Fu JY, Jiang T, Yang YB. The influence of the gangue contents on properties of pellet. Sintering Pelletizing, 2002, 27(4): 11

[6] Das B, Mishra BK, Prakash S, Das SK, Reddy PSR, Angadi SI. Magnetic and flotation studies of banded hematite quartzite (BHQ) ore for the production of pellet grade concentrate. Int. J. Miner. Metall. Mater., 2010, 17(6): 675.

[7] Zhang YM. Pellets Production Technology, 1998, Beijing, Metallurgical Industry Press, 66

[8] Huang ZC, Yi LY, Peng H, Jiang T. Effects of roast temperature on properties of oxide pellets and its gas-based direct reduction. J. Cent. South Univ. Sci. Technol., 2012, 43(8): 2889

[9] Feng JX, Zhang Y, Zheng HW, Xie XY, Zhang C. Drying and preheating processes of iron ore pellets in a traveling grate. Int. J. Miner. Metall. Mater., 2010, 17(5): 535.

[10] Zhang YK. Exploration and practice of low temperature induration process of V-Ti pellets. Sintering Pelletizing, 2010, 35(6): 17

[11] Gao QJ, Wei G, He YB, Shen FM. Effect of MgO on compressive strength of pellet. J. Northeast. Univ. Nat. Sci., 2013, 34(1): 103

[12] Huang ZC, Zhang YB, Chen YM, Zhuang JM. Microstructure of oxidized pellets mainly made from hematite with magnetite. J. Cent. South Univ. Sci. Technol., 2003, 34(6): 606

[13] Wang XL. The Ferrous Metallurgy (Part of Iron), 2009, Beijing, Metallurgical Industry Press, 64

[14] Xiao Q. Theory and Practice of Pelletizing, 1991, Changsha, Central South University of Technology Press, 93

[15] Chen YM, Li J. Crystal rule of Fe₂O₃ in oxidized pellets. J. Cent. South Univ. Sci. Technol., 2007, 38(1): 70