Influence of acid leaching and calcination on iron removal of coal kaolin

Abstract

Calcination and acid leaching of coal kaolin were studied to determine an effective and economical preparation method of calcined kaolin. Thermogravimetric-differential thermal analysis (TG-DTA) and X-ray diffraction (XRD) demonstrated that 900°C was the suitable temperature for the calcination. Leaching tests showed that hydrochloric acid was more effective for iron dissolution from raw coal kaolin (RCK), whereas oxalic acid was more effective on iron dissolution from calcined coal kaolin (CCK). The iron dissolution from CCK was 28.78wt%, which is far less effective than the 54.86wt% of RCK under their respective optimal conditions. Through analysis by using Mössbauer spectroscopy, it is detected that nearly all of the structural ferrous ions in RCK were removed by hydrochloric acid. However, iron sites in CCK changed slightly by oxalic acid leaching because nearly all ferrous ions were transformed into ferric species after firing at 900°C. It can be concluded that it is difficult to remove the structural ferric ions and ferric oxides evolved from the structural ferrous ions. Thus, iron removal by acids should be conducted prior to calcination.

Keywords

kaolin / iron removal / calcination / acid leaching / extraction / Mössbauer spectroscopy

References

[1] Wu ZG, Shi SL, Liu QF. Preparation of micro-porous calcium silicate with coal series kaolin. Met. Mine, 2011 162

[2] Liu HB, Liu ZL. Recycling utilization patterns of coal mining waste in China. Resour. Conserv. Recycl., 2010, 54(12): 1331.

[3] Bian ZF, Dong JH, Lei SG, Leng HL, Mu SG, Wang H. The impact of disposal and treatment of coal mining wastes on environment and farmland. Environ. Geol., 2009, 58(3): 625.

[4] Pone JDN, Hein KAA, Stracher GB, Annegarn HJ, Finkleman RB, Blake DR, McCormack JK, Schroeder P. The spontaneous combustion of coal and its by-products in the Witbank and Sasolburg coalfields of South Africa. Int. J. Coal. Geol., 2007, 72(2): 124.

[5] Stracher GB, Taylor TP. Coal fires burning out of control around the world: thermodynamic recipe for environmental catastrophe. Int. J. Coal. Geol., 2004, 59(1–2): 7.

[6] Barbieri L, Lancellotti I, Manfredini T, Pellacani GC, Rincòn JM, Romero M. Nucleation and crystallization of new glasses from fly ash originating from thermal power plants. J. Am. Ceram. Soc., 2001, 84(8): 1851.

[7] Chugh YP, Patwardhan A. Mine-mouth power and process steam generation using fine coal waste fuel. Resour. Conserv. Recycl., 2004, 40(3): 225.

[8] Zuo PF. Comprehensive utilization of coal gangue. Coal Technol., 2009, 28(1): 186

[9] Yan YX, Wang XF, Wang XQ. Environmental effect and comprehensive utilization of coalmine waste from Huaibei and Huainan coalfield. J. Anhui. Univ. Sci. Technol. Nat. Sci., 2006, 26(2): 9

[10] Deng DH, Cen WL. Environmental effect of coal gangue stack area. China Min. Magaz., 1999 87

[11] Pan F, Lu XC, Wang TZ, Wang Y, Zhang ZM, Yan Y, Yang SP. Synthesis of large-mesoporous γ-Al₂O₃ from coal-series kaolin at room temperature. Mater. Lett., 2013, 91, 136.

[12] Wang BK, Ding H, Deng YX. Characterization of calcined kaolin/TiO₂ composite particle material prepared by mechano-chemical method. J. Wuhan. Univ. Technol. Mater. Sci. Ed., 2010, 25(5): 765.

[13] Wen Y, Li N, Han BQ. Preparation and characterization of porous ceramics prepared by kaolinite gangue and Al(OH)₃ with double addition of MgCO₃ and CaCO₃. Int. J. Miner. Metall. Mater., 2011, 18(4): 450.

[14] Murray HH. Applied Clay Mineralogy: Occurrences, Processing, and Application of Kaolins, Bentonites, Palygorskite-sepiolite, and Common Clays, 2007

[15] Cheng HF, Liu QF, Yang J, Frost RL. Thermogravimetric analysis of selected coal-bearing strata kaolinite. Thermochim. Acta, 2010, 507–508, 84.

[16] Chandrasekhar S, Ramaswamy S. Influence of mineral impurities on the properties of kaolin and its thermally treated products. Appl. Clay Sci., 2002, 21(3–4): 133.

[17] Zhu CS, Luan JH, Zhang PH, Huang RA, Liu D, Xiang XJ, Li ZN. A study on calcinated whitening technology of kaolin in Benxi formation, Jiaozuo area. Coal Geol. China, 2008, 20(9): 14

[18] Gámiz E, Melgosa M, Sánchez-Marañón M, Martín-García JM, Delgado R. Relationships between chemico-mineralogical composition and color properties in selected natural and calcined Spanish kaolins. Appl. Clay Sci., 2005, 28(1–4): 269.

[19] Martínez-Luévanos A, Rodríguez-Delgado MG, Uribe-Salas A, Carrillo-Pedroza FR, Osuna-Alarcón JG. Leaching kinetics of iron from low grade kaolin by oxalic acid solutions. Appl. Clay Sci., 2011, 51(4): 473.

[20] Sidhu PS, Gilkes RJ, Cornell RM, Posner AM, Quirk JP. Dissolution of iron oxides and oxyhydroxides in hydrochloric and perchloric acids. Clays Clay Miner., 1981, 29(4): 269.

[21] Shabani MA, Irannajad M, Azadmehr AR. Investigation on leaching of malachite by citric acid. Int. J. Miner. Metall. Mater., 2012, 19(9): 782.

[22] Ambikadevi VR, Lalithambika M. Effect of organic acids on ferric iron removal from iron-stained kaolinite. Appl. Clay Sci., 2000, 16(3–4): 133.

[23] Larroyd F, Petter CO, Sampaio CH. Purification of north Brazilian kaolin by selective flocculation. Miner. Eng., 2002, 15(12): 1191.

[24] Chen LZ, Liao GP, Qian ZH, Chen J. Vibrating high gradient magnetic separation for purification of iron impurities under dry condition. Int. J. Miner. Process., 2012, 102–103, 136.

[25] Yavuz CT, Prakash A, Mayo JT, Colvin VL. Magnetic separations: from steel plants to biotechnology. Chem. Eng. Sci., 2009, 64(10): 2510.

[26] Cornell RM, Schwertmann U. The Iron Oxides: Structure, Properties, Reactions, Occurrences and Uses, 2003, New York, USA, VCH Publishers, 175.

[27] Künding W. A least square fit program. Nucl. Instrum. Methods, 1969, 75(2): 336.

[28] Huffman GP, Huggins FE. Mössbauer studies of coal and coke: quantitative phase identification and direct determination of pyritic and iron sulphide sulphur content. Fuel, 1978, 57(10): 592.

[29] Hinckley CC, Smith GV, Twardowska H, Saporoschenko M, Shiley RH, Griffen RA. Mössbauer studies of iron in Lurgi gasification ashes and power plant fly and bottom ash. Fuel, 1980, 59(3): 161.

[30] Taneja SP, Jones CHW. Mössbauer studies of iron-bearing minerals in coal and coal ash. Fuel, 1984, 63(5): 695.

[31] Ram LC, Tripathi PSM, Mishra SP. Mössbauer spectroscopic studies on the transformations of iron-bearing minerals during combustion of coals: Correlation with fouling and slagging. Fuel Process. Technol., 1995, 42(1): 47.

[32] Zhou CC, Liu GJ, Yan ZC, Fang T, Wang RW. Transformation behavior of mineral composition and trace elements during coal gangue combustion. Fuel, 2012, 97, 644.

[33] White CE, Provis JL, Proffen T, Riley DP, van Deventer JSJ. Combining density functional theory (DFT) and pair distribution function (PDF) analysis to solve the structure of metastable materials: the case of metakaolin. Phys. Chem. Chem. Phys., 2010, 12, 3239.

[34] Lee SO, Tran T, Park YY, Kim S J, Kim MJ. Study on the kinetics of iron oxide leaching by oxalic acid. Int. J. Miner. Process., 2006, 80(2–4): 144.

[35] Castelein O, Aldon L, Olivier-Fourcade J, Jumas JC, Bonnet JP, Blanchart P. ⁵⁷Fe Mössbauer study of iron distribution in a kaolin raw material: influence of the temperature and the heating rate. J. Eur. Ceram. Soc., 2002, 22(11): 1767.