Influence of cryogenic treatment on the wear characteristics of 100Cr6 bearing steel

Abstract

A series of reciprocating wear tests were performed on the deep cryogenically treated and conventionally heat-treated samples of 100Cr6 bearing steel to study the wear resistance. The worn surfaces as well as the wear debris were analyzed by scanning electron microscopy. The improvement in wear resistance of the deep cryogenically treated samples ranges from 49% to 52%. This significant improvement in wear resistance can be attributed to finer carbide precipitation in the tempered martensitic matrix and the transformation of retained austenite into martensite. X-ray diffraction analysis shows that the volume fraction of retained austenite in the conventionally heat-treated samples is 14% and that of the deep cryogenically treated samples is only 3%.

Keywords

bearing steel / cryogenic treatment / wear resistance / carbides / martensite

References

[1] Sergeev VZ, Fridman VB, Egorshina TV. Increasing the wear and corrosion resistance of fuel pump plunger pairs. Met. Sci. Heat Treat., 1988, 30(6): 401.

[2] Bensely A, Senthilkumar D, Mohan Lal D, Nagarajan G, Rajadurai A. Effect of cryogenic treatment on tensile behavior of case carburized steel-815M17. Mater. Charact., 2007, 58(5): 485.

[3] Yang HS, Wang J, Shen BL, Liu HH, Gao SJ, Huang SJ. Effect of cryogenic treatment on the matrix structure and abrasion resistance of white cast iron subjected to destabilization treatment. Wear, 2006, 261(10): 1150.

[4] Oppenkowski A, Weber S, Theisen W. Evaluation of factors influencing deep cryogenic treatment that affect the properties of tool steels. J. Mater. Process. Technol., 2010, 210(14): 1949.

[5] Kim HJ, Kim DE. Nano-scale friction: a review. Int. J. Precis. Eng. Manuf., 2009, 10(2): 141.

[6] Koneshlou M, Asl KM, Khomamizadeh F. Effect of cryogenic treatment on microstructure, mechanical and wear behaviors of AISI H13 hot work tool steel. Cryogenics, 2011, 51(1): 55.

[7] Jaswin MA, Shankar GS, Lal DM. Wear resistance enhancement in cryotreated En 52 and 21-4N valve steels. Int. J. Precis. Eng. Manuf., 2010, 11(1): 97.

[8] Firouzdor V, Nejati E, Khomamizadeh F. Effect of deep cryogenic treatment on wear resistance and tool life of M2 HSS drill. J. Mater. Process. Technol., 2008, 206(1-3): 467.

[9] Yun D, Lin XP, Xiao HS. Deep cryogenic treatment of high-speed steel and its mechanism. Heat Treat. Met., 1998, 25(3): 55

[10] Chi HX, Ma DS, Yong QL, Wu LZ, Zhang ZP, Wang YW. Effect of cryogenic treatment on properties of Cr8-type cold work die steel. J. Iron Steel Res., 2010, 17(6): 43.

[11] ASTM G 133-05. Standard Test Method for Linearly Reciprocating Ball-on-Flat Sliding Wear, 2006, West Conshohocken, Pennsylvania, Annual Book of Standards, ASTM International

[12] ASTM E 975-03. Standard Practice for X-ray Determination of Retained Austenite in Steel with Near Random Crystallographic Orientation, 2004, West Conshohocken, Pennsylvania, Annual Book of Standards, ASTM International

[13] ASTM E 3-11. Standard Guide for Preparation of Metallographic Specimens, 2004, West Conshohocken, Pennsylvania, Annual Book of Standards, ASTM International