Electrodeposition of aluminium and aluminium-copper alloys from a room temperature ionic liquid electrolyte containing aluminium chloride and triethylamine hydrochloride

Abstract

The electrodeposition of Al and Al-Cu binary alloys on to gold substrates from a room temperature ionic liquid electrolyte containing AlCl₃-Et₃NHCl was studied. The electrochemical behavior of the electrolyte and the mechanism of deposition were investigated through cyclic voltammetry (CV), and the properties of deposits obtained were assessed by scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM-EDS) and X-ray diffraction (XRD). Al of 70 μm in thickness and an Al-Cu alloy of 30 μm in thickness with 8at% copper were deposited from the electrolyte. SEM images of the deposits indicate that the Al deposit was smooth and uniform, whereas the Al-Cu deposit was nodular. The average crystalline size, as determined by XRD patterns, was found to be (30 ± 5) and (29 ± 5) nm, respectively, for Al and Al-Cu alloys. Potentiodynamic polarization (Tafel plots) and electrochemical impedance spectroscopic (EIS) measurements showed that Al-Cu alloys are more corrosion resistant than Al.

Keywords

electrodeposition / aluminium copper alloys / ionic liquids / triethylamine hydrochloride / copper acetylacetonate

References

[1] Lequeu P, Smith KP, Daniélou A. Aluminumcopper-lithium alloy 2050 developed for medium to thick plate. J. Mater. Eng. Perform., 2010, 19(6): 841.

[2] Kundar H, Krishna Srinivasan K. Impact toughness of ternary Al-Zn-Mg alloys in as cast and homogenized condition measured in the temperature range 263–673 K. Bull. Mater. Sci., 2000, 23(1): 35.

[3] El Abedin SZ, Moustafa E M, Hempelmann R, Natter H, Endres F. Additive free electrodeposition of nanocrystalline aluminium in a water and air stable ionic liquid. Electrochem. Commun., 2005, 7(11): 1111.

[4] Dubourg L, Pelletier H, Vaissiere D, Hlawka F, Cornet A. Mechanical characterisation of laser surface alloyed aluminium-copper systems. Wear, 2002, 253(9-10): 1077.

[5] Zhao Y, VanderNoot TJ. Electrodeposition of aluminium from nonaqueous organic electrolytic systems and room temperature molten salts. Electrochim. Acta, 1997, 42(1): 3.

[6] Badawy WA, Sabrah B A, Hilal N H Y. A new bath for the electrodeposition of aluminium: I. Conductivity measurements. J. Appl. Electrochem., 1986, 16(5): 707.

[7] Legrand L, Tranchant A, Messina R. Aluminium behaviour and stability in AlCl₃/DMSO₂ electrolyte. Electrochim. Acta, 1996, 41(17): 2715.

[8] Legrand L, Heintz M, Tranchant A, Messina R. Sulfone-based electrolytes for aluminum electrodeposition. Electrochim. Acta, 1995, 40(11): 1711.

[9] Jiang T, Brym M J C, Lasia G D A, Brisard G M. Electrodeposition of aluminium from ionic liquids: Part II. Studies on the electrodeposition of aluminum from aluminum chloride (AICl3)-trimethylphenylammonium chloride (TMPAC) ionic liquids. Surf. Coat. Technol., 2006, 201(1–2): 10.

[10] Gao LX, Wang LN, Qi T, Li YP, Chu JL, Qu JK. Electrodeposition of aluminum from AlCl3/Et3NHCl ionic liquids. Acta Phys. Chim. Sin., 2008, 24(6): 939.

[11] Freyland W, Zell CA, Abedin SZE, Endres F. Nanoscale electrodeposition of metals and semiconductors from ionic liquids. Electrochim. Acta, 2003, 48(20–22): 3053.

[12] Mann O, Pan GB, Freyland W. Nanoscale electrodeposition of metals and compound semiconductors from ionic liquids. Electrochim. Acta, 2009, 54(9): 2487.

[13] El Abedin SZ, Moustafa EM, Hempelmann R, Natter H, Endres F. Electrodeposition of nano-and microcrystalline aluminium in three different air and water stable ionic liquids. ChemPhysChem, 2006, 7(7): 1535.

[14] Perre E, Nyholm L, Gustafsson T, Taberna PL, Simon P, Edström K. Direct electrodeposition of aluminium nano-rods. Electrochem. Commun., 2008, 10(10): 1467.

[15] Jones SD, Blomgren GE. Low-temperature molten salt electrolytes based on aralkyl quaternary or ternary onium salts. J. Electrochem. Soc., 1989, 136(2): 424.

[16] Wilkes JS, Levisky JA, Wilson RA, Hussey CL. Dialkylimidazolium chloroaluminate melts: a new class of room-temperature ionic liquids for electrochemistry, spectroscopy and synthesis. Inorg. Chem., 1982, 21(3): 1263.

[17] Zhao Y, VanderNoot TJ. Electrodeposition of aluminium from room temperature AlCl₃-TMPAC molten salts. Electrochim. Acta, 1997, 42(11): 1639.

[18] Simanavčius L, Stakėnas A, Šarkis A. Codeposition of aluminum with some metals from AlBr₃-dimethylethylphenylammonium bromide solutions containing acetylacetonate of selected metal. Electrochim. Acta, 2000, 46(4): 499.

[19] Ali MR, Nishikata A, Tsuru T. Electrodeposition of aluminum-chromium alloys from AlCl₃-BPC melt and its corrosion and high temperature oxidation behaviors. Electrochim. Acta, 1997, 42(15): 2347.

[20] Simanavičius L, Stakėnas A, Šarkis A. The initial stages of aluminum and zinc electrodeposition from an aluminum electrolyte containing quaternary aralkylammonium compound. Electrochim. Acta, 1997, 42(10): 1581.

[21] Tsuda T, Hussey CL, Stafford GR, Bonevich JE. Electrochemistry of titanium and the electrodeposition of Al-Ti alloys in the lewis acidic aluminum chloride-1-Ethyl-3-methylimidazolium chloride melt. J. Electrochem. Soc., 2003, 150(4): C234.

[22] Li JC, Nan SH, Jiang Q. Study of the electrodeposition of Al-Mn amorphous alloys from molten salts. Surf. Coat. Technol., 1998, 106(2–3): 135.

[23] Tsuda T, Hussey CL, Stafford GR, Kongstein O. Electrodeposition of Al-Zr alloys from lewis acidic aluminum chloride-1-ethyl-3-methylimidazolium chloride melt. J. Electrochem. Soc., 2004, 151(7): C447.

[24] Zhu Q, Hussey CL, Stafford GR. Electrodeposition of silver-aluminum alloys from a room-temperature chloroaluminatemolten salt. J. Electrochem. Soc., 2001, 148(2): C88.

[25] Ali MR, Nishikata A, Tsuru T. Electrodeposition of Co-Al alloys of different composition from the AlCl₃-BPCCoCl₂ room temperature molten salt. Electrochim. Acta, 1997, 42(12): 1819.

[26] Tsuda T, Hussey CL, Stafford GR. Electrodeposition of Al-Mo alloys from the Lewis acidic aluminum chloride-1-ethyl-3-methylimidazolium chloride molten salt. J. Electrochem. Soc., 2004, 151(6): C379.

[27] Lisenkov A, Zheludkevich ML, Ferreira MGS. Active protective Al-Ce alloy coating electrodeposited from ionic liquid. Electrochem. Commun., 2010, 12(6): 729.

[28] Tsuda T, Hussey CL, Stafford GR. Electrodeposition of Al-Mo-Mn ternary alloys from the lewis acidic AlCl₃-EtMeImCl molten salt. J. Electrochem. Soc., 2005, 152(9): C620.

[29] Tsuda T, Arimoto S, Kuwabata S, Hussey CL. Electrodeposition of Al-Mo-Ti Ternary alloys in the Lewis acidic aluminum chloride-1-ethyl-3-methylimidazolium chloride room-temperature ionic liquid. J. Electrochem. Soc., 2008, 155(4): D256.

[30] Zhu Q, Hussey CL. Galvanostatic pulse plating of bulk Cu-Al alloys on nickel electrodes from roomtemperature chloroaluminate molten salts containing benzene. J. Electrochem. Soc., 2002, 149(5): C268.

[31] Tierney BJ, Pitner WR, Mitchell JA, Hussey CL, Stafford GR. Electrodeposition of copper and copperaluminum alloys from a room-temperature chloroaluminate molten salt. J. Electrochem. Soc., 1998, 145(9): 3110.

[32] Tang JW, Azumi K. Optimization of pulsed electrodeposition of aluminum from AlCl₃-1-ethyl-3-methylimidazolium chloride ionic liquid. Electrochim. Acta, 2011, 56(3): 1130.

[33] Ashour EA, Ateya BG. Electrochemical behaviour of a copper-aluminium alloy in concentrated alkaline solutions. Electrochim. Acta, 1997, 42(2): 243.

[34] Caporali S, Fossati A, Lavacchi A, Perissi I, Tolstogouzov A, Bardi U. Aluminium electroplated from ionic liquids as protective coating against steel corrosion. Corros. Sci., 2008, 50(2): 534.