Influence of Ce and Mn addition on α-Fe morphology in recycled Al-Si alloy ingots

Abstract

The influence of Ce or Ce and Mn combined additions on the morphology of α-Fe phases in recycled Al-Si alloys was experimentally investigated by microstructure observation and room temperature tensile testing. It is found that Ce modifies the morphology of α-Fe phase from the large Chinese script-like into the individual and fine nodular shape. A combined addition of Ce and Mn results in the promotion of primary α-Fe formation, and their size increases considerably with the increase in Ce content. The mechanism of the above morphological changes was discussed in accordance with the nucleation and growth of α-Fe phase during solidification.

Keywords

aluminum-silicon alloys / cerium / manganese / modification / morphology

References

[1] Yang X R, Mao WM, Gao C. Semisolid A356 alloy feedstock poured through a serpentine channel. Int. J. Miner. Metall. Mater., 2009, 16(5): 603.

[2] Bai YL, Xu J, Zhang ZF, Mao WM, Xu H. Numerical simulation on the rheo-diecasting of the semi-solid A356 aluminum alloy. Int. J. Miner. Metall. Mater., 2009, 16(4): 422.

[3] Khalifa W, Samuel FH, Gruzleski JE. Iron intermetallic phases in the Al corner of the Al-Si-Fe system. Metall. Mater. Trans. A, 2003, 34(13): 807.

[4] Ashtari P, Tezuka H, Sato T. Influence of Sr and Mn additions on intermetallic compound morphologies in Al-Si-Cu-Fe cast alloys. Mater. Trans., 2003, 44(12): 2611.

[5] Flores-V A, Sukiennik M, Castillejos-E AH, Acosta-G FA, Escobedo-B JC. A kinetic study on the nucleation and growth of the Al₈FeMnSi₂ intermetallic compound for aluminum scrap purification. Intermetallics, 1998, 6(3): 217.

[6] Shabestari SG. The effect of iron and manganese on the formation of intermetallic compounds in aluminum-silicon alloys. Mater. Sci. Eng. A, 2004, 383(2): 289

[7] Zhou HR, Li XG, Dong CF, Xiao K, Li T. Corrosion behavior of aluminum alloys in Na₂SO₄ solution using the scanning electrochemical microscopy technique. Int. J. Miner. Metall. Mater., 2009, 16(1): 84.

[8] Lu L, Dahle AK. Iron-rich intermetallic phases and their role in casting defect formation in hypoeutectic Al-Si alloys. Metall. Mater. Trans. A, 2005, 36(3): 819.

[9] Couture A. Iron in aluminum casting alloys: a literature survey. AFS Int. Cast Met. J., 1981 9

[10] Fu GS, Sun FS, Ren LM, Chen WZ, Qian KW. Modification behavior of trace rare earth on impurity phases in commercial purity aluminum. J. Rare Earths, 2002, 20(1): 61

[11] Cao X, Campbell J. Precipitation of primary intermetallic compounds in liquid Al 11.5 Si 0.4 Mg alloy. Int. J. Cast Met. Res., 2000, 13(3): 175

[12] Cao X, Campbell J. The nucleation of Fe-rich phases on oxide films in Al-11.5Si-0.4Mg cast alloys. Metall. Mater. Trans. A, 2003, 34(7): 1409.

[13] Dinnis CM, Taylor JA, Dahle AK. As-cast morphology of iron-intermetallics in Al-Si foundry alloys. Scripta Mater., 2005, 53(8): 955.

[14] Cao X, Campbell J. The solidification characteristics of Fe-rich intermetallics in Al-11.5Si-0.4Mg cast alloys. Metall. Mater. Trans. A, 2004, 35(5): 1425.

[15] Pucella G, Samuel AM, Samuel FH, Doty HW, Valtierra S. Sludge formation in Sr-modified Al-11.5wt%Si diecasting alloys. AFS Trans., 1999, 24, 117