Stress corrosion cracking of X80 pipeline steel exposed to high pH solutions with different concentrations of bicarbonate

Abstract

Susceptibilities to stress corrosion cracking (SCC) of X80 pipeline steel in high pH solutions with various concentrations of HCO₃ ⁻ at a passive potential of −0.2 V vs. SCE were investigated by slow strain rate tensile (SSRT) test. The SCC mechanism and the effect of HCO₃ ⁻ were discussed with the aid of electrochemical techniques. It is indicated that X80 steel shows enhanced susceptibility to SCC with the concentration of HCO₃ ⁻ increasing from 0.15 to 1.00 mol/L, and the susceptibility can be evaluated in terms of current density at −0.2 V vs. SCE. The SCC behavior is controlled by the dissolution-based mechanism in these circumstances. Increasing the concentration of HCO₃ ⁻ not only increases the risk of rupture of passive films but also promotes the anodic dissolution of crack tips. Besides, little susceptibility to SCC is found in dilute solution containing 0.05 mol/L HCO₃ ⁻ for X80 steel. This can be attributed to the inhibited repassivation of passive films, manifesting as a more intensive dissolution in the non-crack tip areas than at the crack tips.

Keywords

pipeline steel / stress corrosion cracking / bicarbonate t]passive films

References

[1] Zhang L, Li XG, Du CW, Huang YZ. Effect of applied potentials on stress corrosion cracking of X70 pipeline steel in alkali solution. Mater. Des., 2009, 30(6): 2259.

[2] Dong CF, Xiao K, Liu ZY, Yang WJ, Li XG. Hydrogen induced cracking of X80 pipeline steel. Int. J. Miner. Metall. Mater., 2010, 17(5): 579.

[3] Van Boven G, Chen W, Rogge R. The role of residual stress in neutral pH stress corrosion cracking of pipeline steels: Part I. Pitting and cracking occurrence. Acta Mater., 2007, 55(1): 29.

[4] Lu BT, Song F, Gao M, Elboujdaini M. Crack growth model for pipelines exposed to concentrated carbonate-bicarbonate solution with high pH. Corros. Sci., 2010, 52(12): 4064.

[5] Zhang GA, Cheng YF. Micro-electrochemical characterization and Mott-Schottky analysis of corrosion of welded X70 pipeline steel in carbonate/bicarbonate solution. Electrochim. Acta, 2009, 55(1): 316.

[6] Li T, Yang YJ, Gao KW, Lu MX. Mechanism of protective film formation during CO₂ corrosion of X65 pipeline steel. J. Univ. Sci. Technol. Beijing, 2008, 15(6): 702.

[7] Xu LN, Qin HM, Chang W, Zhang L, Lu MX, Li SF. CO₂ corrosion behavior of X70 pipeline steel in wet gas environment. J. Univ. Sci. Technol. Beijing, 2011, 33(12): 1478.

[8] Fu AQ, Cheng YF. Electrochemical polarization behavior of X70 steel in thin carbonate/bicarbonate solution layers trapped under a disbonded coating and its implication on pipeline SCC. Corros. Sci., 2010, 52(7): 2511.

[9] Liang P, Du CW, Li XG, Chen X, Zhang L. Effect of hydrogen on the stress corrosion cracking behavior of X80 pipeline steel in Ku’erle soil simulated solution. Int. J. Miner. Metall. Mater., 2009, 16(4): 407.

[10] Liang P, Li XG, Du CW, Chen X, Zhang L. Influence of chloride ions on the corrosion resistance of X80 pipeline steel in NaHCO₃ solution. J. Univ. Sci. Technol. Beijing, 2008, 30(7): 735.

[11] Eslami A, Kania R, Worthingham B, Boven GV, Eadie R, Chen W. Effect of CO₂ and R-ratio on nearneutral pH stress corrosion cracking initiation under a disbonded coating of pipeline steel. Corros. Sci., 2011, 53(6): 2318.

[12] Parkins RN, Zhou S. The stress corrosion cracking of C-Mn steel in CO₂-HCO₃ ⁻-CO₃ ²⁻ solutions: II. Electrochemical and other data. Corros. Sci., 1997, 39(1): 175.

[13] Fan L, Li XG, Du CW, Liu ZY. Electrochemical behavior of passive films formed on X80 pipeline steel in various concentrated NaHCO₃ solutions. J. Chin. Soc. Corros. Prot., 2012, 32(4): 322.

[14] Zhou JL, Li XG, Du CW, Pan Y, Li T, Liu Q. Passivation process of X80 pipeline steel in bicarbonate solutions. Int. J. Miner. Metall. Mater., 2011, 18(2): 178.

[15] Liu ZY, Li XG, Du CW, Zhai GL, Cheng YF. Stress corrosion cracking behavior of X70 pipe steel in an acidic soil environment. Corros. Sci., 2008, 50(8): 2251.

[16] Parkins RN. Predictive approaches to stress corrosion cracking failure. Corros. Sci., 1980, 20(2): 147.

[17] Parkins RN. Mechanistic aspects of intergranular stress corrosion cracking of ferritic steels. Corrosion, 1996, 52(5): 363.

[18] Liu ZY, Li XG, Zhang YR, Du CW, Zhai GL. Relationship between electrochemical characteristics and SCC of X70 pipeline steel in an acidic soil simulated solution. Acta Metall. Sin. Engl. Lett., 2009, 22(1): 58.

[19] Li D, Meng FY, Ma XQ, Qiao LJ, Chu WY. Molecular dynamics simulation of porous layer-induced stress in Fe single crystal. Comput. Mater. Sci., 2010, 49(3): 641.

[20] Parkins RN, Blanchard WK Jr. Delanty BS. Transgranular stress corrosion cracking of high-pressure pipelines in contact with solutions of near neutral pH. Corrosion, 1994, 50(5): 394.

[21] Davies DH, Burstein GT. The effects of bicarbonate on the corrosion and passivation of iron. Corrosion, 1980, 36(8): 416.

[22] Meng GZ, Zhang C, Cheng YF. Effects of corrosion product deposit on the subsequent cathodic and anodic reactions of X-70 steel in near-neutral pH solution. Corros. Sci., 2008, 50(11): 3116.

[23] Liang P, Li XG, Du CW, Chen X. Stress corrosion cracking of X80 pipeline steel in simulated alkaline soil solution. Mater. Des., 2009, 30(5): 1712.

[24] Wang JQ, Atrens A. SCC initiation for X65 pipeline steel in the “high” pH carbonate/bicarbonate solution. Corros. Sci., 2003, 45(10): 2199.