Additive effects on tin electrodepositing in acid sulfate electrolytes

Abstract

The effects of additives on the stannous reduction of an acid sulfate bath were investigated using cyclic and linear sweep voltammetry, electrochemical impedance spectroscopy (EIS), and microstructure analysis. In the absence of additives, tin coatings are rough, and the tin electrodepositing is a single-step reduction process accompanied by hydrogen gas evolution. The addition of tartaric acid produces a slight reduction in the peak current of stannous reduction and has an appreciably positive effect on the stability of the acidic tin bath. Both benzylidene acetone and polyoxyethylene octylphenol ether hinder the stannous reduction and greatly suppress the hydrogen gas evolution. Formaldehyde slightly decreases the peak current density of stannous reduction and serves as an auxiliary brightener in the acid sulfate bath. The presence of mixed additives greatly suppresses the stannous reduction and hydrogen gas evolution and consequently produces a significantly smoother and denser tin coating. The (112) crystal face is found to be the dominant and preferred orientation of tin deposits.

Keywords

electrodepositing / tin / additives / stannous reduction

References

[1] Illés B, Horváth B, Harsányi G. Effect of strongly oxidizing environment on whisker growth form tin coating. Surf. Coat. Technol., 2010, 205(7): 2262.

[2] Low CTJ, Walsh FC. Electrodeposition of tin, copper and tin-copper alloys from a methanesulfonic acid electrolyte containing a perfluorinated cationic surfactant. Surf. Coat. Technol., 2008, 202(8): 1339.

[3] Chen YH, Wang YY, Wan CC. Microstructural characteristics of immersion tin coatings on copper circuitries in circuit boards. Surf. Coat. Technol., 2007, 202(3): 417.

[4] Park YW, Sankara Narayanan TSN, Lee KY. Effect of temperature on the fretting corrosion of tin plated copper alloy contacts. Wear, 2007, 262(3–4): 320.

[5] Low CTJ, Walsh FC. The stability of an acidic tin methanesulfonate electrolyte in the presence of a hydroquinone antioxidant. Electrochim. Acta, 2008, 53(16): 5280.

[6] Low CTJ, Walsh FC. The influence of a perfluorinated cationic surfactant on the electrodeposition of tin from a methanesulfonic acid bath. J. Electroanal. Chem., 2008, 615(2): 91.

[7] Martyak NM, Seefeldt R. Additive-effects during plating in acid tin methanesulfonate electrolytes. Electrochim. Acta, 2004, 49(25): 4303.

[8] Suh MS, Park CJ, Kwon HS. Effects of plating parameters on alloy composition and microstructure of Sn-Bi electrodeposits from methane sulphonate bath. Surf. Coat. Technol., 2006, 200(11): 3527.

[9] García-Gabaldón M, Pérez-Herranz V, Sánchez E, Mestre S. Effect of tin concentration on the electrical properties of ceramic membranes used as separators in electrochemical reactors. J. Membr. Sci., 2008, 323(1): 213.

[10] Wu JW, Zhai GF, Chen Q, Wang JQ, Ren G. The interfacial structure of plated copper alloy resistance spot welded joint. Appl. Surf. Sci., 2008, 254(22): 7227.

[11] Tzeng GS, Lin SH, Wang YY, Wan CC. Effects of additives on the electrodeposition of tin from an acidic Sn(II) bath. J. Appl. Electrochem., 1996, 26(4): 419.

[12] Carlos IA, Bidoia ED, Pallone EMJA, Almeida MRH, Souza CAC. Effect of tartrate content on aging and deposition condition of copper-tin electrodeposits from a non-cyanide acid bath. Surf. Coat. Technol., 2002, 157(1): 14.

[13] Rockwell GP, Dahn JR. Sn-based roughness gradients for high-throughput screening. Thin Solid Films, 2008, 516(21): 7361.

[14] Xiao FX, Wei YJ, Li FF, Zhao XC, Liu T. Influence of formaldehyde and emulsifier OP on semi-bright tin plating of printed circuit board in acidic bath. Mater. Prot., 2011, 44(1): 1.

[15] Zhang LM, Fang JL, Yuan GW, Shen PD. Practical Electroplating Additives, 2007, Beijing, Chemical Industry Press, 468.

[16] Crosby Jeffrey N. Tin Plating, 2007

[17] Monk P MS. Fundamentals of Electro-Analytical Chemistry, 2008, New York, John Wiley & Sons, 234.

[18] Kruglikov S, Averin E, Simmov K, Kharlamov V. Bright tin plating baths. National Association for Surface Finishing Annual Technical Conference, Kentucky, 2009 351.

[19] Medvedev GI, Makrushin NA. Electrodeposition of tin from sulfate electrolyte in the presence of syntanol, formaldehyde, and allyl alcohol. Russ. J. Appl. Chem., 2004, 77(11): 1781.

[20] Fang JL. Theory and Application of Electroplating Additives, 2007, Beijing, Chemical Industry Press, 224.

[21] Xiao FX, Shen XN, Wei YJ, Li FF. Influence of gelatin and benzaldehyde on semi-bright tin coating electrodeposited in acidic bath. Mater. Prot., 2011, 44(5): 1.