Synthesis of Mg₂B₂O₅ whiskers via coprecipitation and sintering process

Abstract

Mg₂B₂O₅ whiskers with high aspect ratio were synthesized by coprecipitation and sintering process using MgCl₂·6H₂O, H₃BO₃, and NaOH as raw materials and KCl as a flux. Their formation process was investigated by thermogravimetry and differential scanning calorimetry (TG-DSC), X-ray diffraction (XRD), and scanning electron microcopy (SEM). It is found that the products synthesized at 832°C are monoclinic Mg₂B₂O₅ whiskers with a diameter of 200–400 nm and a length of 50–80 μm. Transmission electron microscopy (TEM) and selected area electron diffraction (SAED) analyses show that the whiskers obtained at 832°C are single crystalline and grow along with the [010] direction. The growth mechanism of Mg₂B₂O₅ whiskers was also presented.

Keywords

magnesium borate / coprecipitation / sintering / crystal whiskers / crystal growth / microstructure

References

[1] Teshima K., Yubuta K., Shimodaira T., Suzuki T., Endo M., Shishido T., Oishi S. Environmentally friendly growth of highly crystalline photocatalytic Na₂Ti₆O₁₃ whiskers from a NaCl flux. Cryst. Growth Des., 2008, 8(2): 465

[2] Cao B., Yao W.J., Wang C.S., Ma X., Feng X., Lu X. Simple fabrication of rutile titanium dioxide whiskers. Mater. Lett., 2010, 64(16): 1819

[3] Pan J.S., Cao R.X., Yuan Y.W. A new approach to the mass production of titanium carbide, nitride and carbonitride whiskers by spouted bed chemical vapor deposition. Mater. Lett., 2006, 60(5): 626

[4] Wu P.L., Tian Z., Wang L.D., Fei W.D. Effect of changing rate of residual stress on thermal expansion behavior of magnesium borate whisker-reinforced aluminum composite. Thermochim. Acta, 2007, 455(1–2): 7

[5] Duan Y., Lu G.M., Song X.F., Sun S.Y., Yu J.G. Preparation and growth mechanism of magnesium borate whiskers with high aspect ratio. J. Inorg. Mater., 2011, 26(5): 364.

[6] Kitamura T., Sakane K., Wada H. Formation of needle crystals of magnesium pyroborate. J. Mater. Sci. Lett., 1988, 7(5): 467

[7] Xu B.S., Li T.B., Zhang Y., Zhang Z.X., Liu X.G., Zhao J.F. New synthetic route and characterization of magnesium borate nanorods. Cryst. Growth Des., 2008, 8(4): 1218

[8] Zhu W.C., Xiang L., He T.B., Zhu S. Hydrothermal synthesis and characterization of magnesium borate hydroxide nanowhiskers. Chem. Lett., 2006, 35(10): 1158

[9] Üçyildiz A., Girgin I. Controlled synthesis, characterization and thermal properties of Mg₂B₂O₅. Cent. Eur. J. Chem., 2010, 8(4): 758

[10] Li S., Fang X., Leng J., Shen H., Fan Y., Xu D. A new route for the synthesis of Mg₂B₂O₅ nanorods by mechano-chemical and sintering process. Mater. Lett., 2010, 64(2): 151

[11] Li Y., Fan Z.Y., Lu J.G., Chang R.P.H. Synthesis of magnesium borate (Mg₂B₂O₅) nanowires by chemical vapor deposition method. Chem. Mater., 2004, 16(13): 2512

[12] Xiao G.Q., Duan F., Zhang G., Fan Q.C. Dissolution-precipitation mechanism of self-propagating high-temperature synthesis of TiC-Cu cermets. J. Univ. Sci. Technol. Beijing, 2007, 14(6): 568

[13] Elssfah E.M., Elsanousi A., Zhang J., Song H.S., Tang C. Synthesis of magnesium borate nanorods. Mater. Lett., 2007, 61(22): 4358

[14] Xia Y.N., Yang P.D., Sun Y.G., Wu Y., Mayers B., Gates B., Yin Y., Kim F., Yan H. One-dimensional nanostructures: Synthesis, characterization, and applications. Adv. Mater., 2003, 15(5): 353

[15] Readey M.J. Formation and sintering characteristics of aluminum borate whiskers. J. Am. Ceram. Soc., 1992, 75(12): 3452