Microstructural and mechanical characteristics of Al-alloyed ductile iron upon casting and annealing

Abstract

Ductile iron containing 6.16wt% Al was developed to investigate the effects of aluminum on both its microstructure and hardness. It was found that aluminum not only increases the nodule count and pearlite content but also improves the hardness in both sand mold and metal mold castings. Annealing treatments were conducted to attain a homogenous microstructure and improve high-temperature serviceability. A ferrite/carbide or ferritic matrix was gained depending on the annealing temperature. It is also discovered that annealing has inverse influences on the hardness of the bulk alloy and the ferrite phase. Although it causes a small decrease in the bulk hardness of the specimens, it leads to an increase in the microhardness of the ferrite. Micro-segregation of the alloying elements was also investigated by means of electron probe micro-analysis for the specimens with different annealing durations and the as-cast specimen as well. An optimum annealing time was proposed to result in the least amount of micro-segregation of aluminum and silicon between graphite nodules.

Keywords

cast iron / casting / annealing / microstructure / hardness

References

[1] J.R. Davis, ASM Specialty Handbook: Cast Irons, ASM International, 1996.

[2] Kiani-Rashid A.R. The Influence of Aluminum and Heat Treatment Conditions on Austempered Ductile Irons, 2000, Leeds, University of Leeds

[3] Erfanian-Naziftoosi H.R., Haghdadi N., Kiani-Rashid A.R. The effect of isothermal heat treatment time on the microstructure and properties of 2.11%Al austemperecl ductile iron. J. Mater. Eng. Perform., 2012, 21, 1785

[4] Kiani-Rashid A.R., Edmonds D.V. Microstructural characteristics of Al-alloyed austempered ductile irons. J. Alloys Compd., 2009, 477, 391

[5] Abedi H.R., Fareghi A., Saghafian H., Kheirandish S.H. Sliding wear behavior of a ferritic-pearlitic ductile cast iron with different nodule count. Wear, 2010, 268, 622

[6] W.J. Keep, The influence of aluminum upon cast iron, [in] Annual Meeting of the American Association for the Advancement of Science, Detroit, 1888.

[7] Kiani Rashid A.R., Edmonds D.V. Oxidation behaviour of Al-alloyed ductile cast irons at elevated temperature. Surf. Interface Anal., 2004, 36, 1011

[8] Haque M.M. Investigation on properties and microstructures of spheroidal graphite Fe-C-2Si and Fe-C-2Al cast irons. J. Mater. Process. Technol., 2007, 191, 360

[9] Pedersen K.M., Tiedje N.S. Graphite nodule count and size distribution in thin walled ductile cast iron. Mater. Charact., 2008, 59, 1111

[10] Reynauld A., Roberge J.L. Application of high temperature spheroidal graphite cast irons in exhaust manifolds. Fonderie Fondeur d’Aujourd’hui, 1999, 182, 37.

[11] D.M. Stefanescu, ASM Metals Handbook Volume 15: Casting, ASM International, 1988.

[12] Nili-Ahmadabadi M., Mosallaiee-Pour M. Homogenization of ductile iron using partial melting aided by modeling. Mater. Sci. Eng. A, 2004, 373, 309

[13] Lacaze J. Solidification of spheroidal graphite cast irons: III. Microsegregation related Effects. Acta Mater., 1999, 47, 3779

[14] B. Black, G. Burger, R. Logan, R. Perrin, and R. Gundlach, Microstructure and dimensional stability in Si-Mo ductile irons for elevated temperature applications, [in] International Body Engineering Conference Exhibition and Automotive Transportation Technology Congress, SAE International, No.10, 2002, p.363.

[15] Kiani-Rashid A.R. Influence of austenitising conditions and aluminum content on microstructure and properties of ductile irons. J. Alloys Compd., 2009, 470, 323

[16] Kiani-Rashid A.R. The influence of Al content on the Fe-C-Al-Si equilibrium phase diagrams. J. Metall. Mater. Eng., 2009, 21, 89.

[17] Kiani-Rashid A.R., Edmonds D.V. Phase transformation study of aluminum-containing ductile cast irons by dilatometry. Mater. Sci. Eng. A, 2008, 481–482, 752.

[18] J.R. Brown, Foseco Ferrous Foundryman’s Handbook, Butterworth-Heinemann, 2000, p.70.

[19] Shayesteh-Zeraati A., Naser-Zoshki H., Kiani-Rashid A.R. Microstructural and mechanical properties (hardness) investigations of Al-alloyed ductile cast iron. J. Alloys Compd., 2010, 500, 129

[20] Petitbon E.U., Wallace J.F. Aluminum alloyed gray iron: Properties at room and elevated temperatures. AFS Cast Met. Res. J., 1973, 9, 127.

[21] Kiani-Rashid A.R., Golozar M.A. Microscopic segregation pattern of Al and Si in matrix microstructure of cast irons with spherical graphite. Esteghlal J., 2003, 2, 177.

[22] Hsu C.H., Chen M.L., Hu C.J. Microstructure and mechanical properties of 4% cobalt and nickel alloyed ductile irons. Mater. Sci. Eng. A, 2007, 444, 339

[23] Kumruoglu L.C. Mechanical and microstructure properties of chilled cast iron camshaft: Experimental and computer aided evaluation. Mater. Des., 2009, 30, 927

[24] Bayati H., Elliott R. Relationship between structure and mechanical properties in high manganese alloyed ductile iron. Mater. Sci. Technol., 1995, 11, 284.

[25] Krawvzjyk J., Bala P., Pacyna J. The effect of carbide precipitate morphology on fracture toughness in low-tempered steels containing Ni. J. Microsc., 2010, 237, 411