Production and characterization of ZnO nanoparticles and porous particles by ultrasonic spray pyrolysis using a zinc nitrate precursor

Abstract

ZnO nanoparticles and porous particles were produced by an ultrasonic spray pyrolysis method using a zinc nitrate precursor at various temperatures under air atmosphere. The effects of reaction temperature on the size and morphology of ZnO particles were investigated. The samples were characterized by energy dispersive spectroscopy, X-ray diffraction, transmission electron microscopy, and scanning electron microscopy. ZnO particles were obtained in a hexagonal crystal structure and the crystallite shapes changed from spherical to hexagonal by elevating the reaction temperature. The crystallite size grew by increasing the temperature, in spite of reducing the residence time in the heated zone. ZnO nanoparticles were obtained at the lowest reaction temperature and ZnO porous particles, formed by aggregation of ZnO nanoparticles due to effective sintering, were prepared at higher temperatures. The results showed that the properties of ZnO particles can be controlled by changing the reaction temperature in the ultrasonic spray pyrolysis method.

Keywords

zinc oxide / nanoparticles / nanocrystallites / porous materials / ultrasonic applications / spray pyrolysis

References

[1] Wang C., Li Q., Mao B., Wang E., Tian C. A different chemical route to synthesize ZnO nanoparticles. Mater. Lett., 2008, 62, 1339

[2] Xu W.G., Liu S.F., Lu S.X., Kang S.Y., Zhou Y., Zhang H.F. Photocatalytic degradation in aqueous solution using quantum-sized ZnO particles supported on sepiolite. J. Colloid Interface Sci., 2010, 351, 210

[3] Xie J., Li Y., Zhao W., Bian L., Wei Y. Simple fabrication and photocatalytic activity of ZnO particles with different morphologies. Powder Technol., 2011, 207, 140

[4] Shojaee S.A., Shahraki M.M., Sani M.A.F., Nemati A., Yousefi A. Microstructural and electrical properties of varistors prepared from coated ZnO nanopwders. J. Mater. Sci. Mater. Electron., 2010, 21, 571

[5] Ho G.W., Wong A.S.W. One step solution synthesis towards ultra-thin and uniform single-crystalline ZnO nanowires. Appl. Phys. A, 2007, 86, 457

[6] Breedon M., Rahmani M.B., Keshmiri S.H., Wlodarski W., Kalantar-zadeh K. Aqueous synthesis of interconnected ZnO nanowires using spray pyrolysis deposited seed layers. Mater. Lett., 2010, 64, 291

[7] Musić S., Dragčević D., Popović S., Ivanda M. Precipitation of ZnO particles and their properties. Mater. Lett., 2005, 59, 2388

[8] Jing L., Xu Z., Shang J., Sun X., Cai W., Guo H. The preparation and characterization of ZnO ultrafine particles. Mater. Sci. Eng. A., 2002, 332, 356

[9] Ada K., Gökgöz M., Önal M., Sarikaya Y. Preparation and characterization of a ZnO powder with hexagonal plate particles. Powder Technol., 2008, 181, 285

[10] Tsai S.C., Song Y.L., Tsai C.S., Yang C.C., Chiu W.Y., Lin H.M. Ultrasonic spray pyrolysis for nanoparticles synthesis. J. Mater. Sci., 2004, 39, 3647

[11] Okuyama K., Lenggoro W.I. Preparation of nanoparticles via spray route. Chem. Eng. Sci., 2003, 58, 537

[12] Gurmen S., Guven A., Ebin B., Stopić S., Friedrich B. Synthesis of nano-crystalline spherical cobalt-iron (Co-Fe) alloy particles by ultrasonic spray pyrolysis and hydrogen reduction. J. Alloys Compd., 2009, 481, 600

[13] Gurmen S., Ebin B., Stopić S., Friedrich B. Nanocrystalline spherical iron-nickel (Fe-Ni) alloy particles prepared by ultrasonic spray pyrolysis and hydrogen reduction (USP-HR). J. Alloys Compd., 2009, 480, 529

[14] Gurmen S., Ebin B. Production and characterization of the nanostructured hollow iron oxide spheres and nanoparticles by aerosol route. J. Alloys Compd., 2010, 492, 585

[15] S. Gurmen and B. Ebin, Synthesis of Ag/ZnO nanocomposite particles by ultrasonic spray pyrolysis method, [in] Supplemental Proceedings of TMS 2010 Annual Meeting & Exhibition Vol. 3, Seattle, 2010, p.829.

[16] B. Ebin, O. Gencer, and S. Gurmen, Aerosol route synthesis of copper oxide nanoparticles using copper nitrate solution, [in] Supplemental Proceedings of TMS 2010 Annual Meeting & Exhibition Vol. 3, Seattle, 2010, p.577.

[17] Taniguchi I. Powder properties of partially substituted LiM_xMn_2−xO₄ (M = Al, Cr, Fe and Co) synthesized by ultrasonic spray pyrolysis. Mater. Chem. Phys., 2005, 92, 172

[18] Milošević O., Jordović B., Uskoković D. Preparation of fine ZnO powders by an ultrasonic spray pyrolysis method. Mater. Lett., 1994, 19, 165

[19] Singh P., Kumar A., Deepak Kaur D. ZnO nanocrystalline powder synthesized by ultrasonic mist-chemical vapour deposition. Opt. Mater., 2008, 30, 1326

[20] Patil L.A., Bari A.R., Shinde M.D., Deo V., Kaushik M.P. Effect of aerosol carriers on ultrasonically prepared nanocrystalline ZnO powders. Adv. Powder Technol., 2011, 22, 722

[21] S. Gurmen, B. Ebin, and B. Ozkal, Preparation of zinc oxide nanostructures from zinc sulfate and zinc nitrate precursors, [in] Supplemental Proceedings of TMS 2009 Annual Meeting & Exhibition Vol. 3, San Francisco, 2009, p.607.

[22] Gürmen S., Stopić S., Friedrich B. Synthesis of nanosized spherical cobalt powder by ultrasonic spray pyrolysis. Mater. Res. Bull., 2006, 41, 1882

[23] Ebin B., Gürmen S. Aerosol synthesis of nano-crystalline iron particles from iron(II) chloride solution. Metall, 2011, 65, 151.