Top slag refining for inclusion composition transform control in tire cord steel

Abstract

Controlling conditions for inclusion plasticization were calculated by FactSage, and the steel/slag reaction equilibration time was determined by pre-equilibrium experiments. Laboratory experiments with different top slags were carried out in 90 min, and industrial tests were performed based on the results of calculation and laboratory experiments. Scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS) were used to determine the morphology and composition of inclusions in tire cord steel. It is found that the shape of inclusions can be controlled well, and the composition of inclusions varies in the industrial test as the following transformation route: MnO-Al₂O₃-SiO₂→CaO-Al₂O₃-SiO₂→MnO-Al₂O₃-SiO₂. Inclusion plasticization can be achieved by controlling the binary basicity of top slag (CaO/SiO₂ by mass) around 1.0 and the (Al₂O₃) content in top slag below 10wt%. Under these controlling conditions in the industrial test, almost all of inclusions in the wire rods achieve plastic deformation.

Keywords

tire cords / ladle metallurgy / inclusions / plasticity / slags / refining

References

[1] Minamida T., Hiraga N., Shibata T. Developments in steel cord wire rods. R&D Kobe Steel Eng. Rep., 2000, 50(3): 31.

[2] Ujiie Y., Kimura H. Production technology for steel bars and wire rods. Nippon Steel Tech. Rep., 1999, 80, 1.

[3] Kimura M. Kobe Steel’s recent advancements in steel wire rod and bar products. R&D Kobe Steel Eng. Rep., 2006, 56(3): 1.

[4] Tashiro H., Tarui T., Sasaki S., Yoshie A., Nishida S., Ohashi S., Nakamura K., Demachi H. Ultra high tensile strength steel cord. Nippon Steel Tech. Rep., 1999, 80, 38.

[5] Liu Z.Z., Cai K.K. Purity steel production technology. Iron Steel, 2000, 35(2): 64.

[6] Zhang S.H. Alloy Steel, 1981, Beijing, Metallurgical Industry Press, 136.

[7] Gatellier C., Gaye H., Lehman J., Bellot J., Moncel M. Inclusions control in low aluminium steels. Rev. Metall. Cah. Inf. Tech., 1992, 89(4): 361.

[8] Bernard G., Ribound P.V., Urbain G. Investigation of the plasticity of oxide inclusions. Rev. Metall. Cah. Inf. Tech., 1981, 78(5): 421.

[9] Wang L.F., Zhang J.M., Wang X.H., Wang W.J. Experimental research of composition control of CaO-SiO₂-Al₂O₃-MgO inclusion by using low basic top slag for tire cord steel. J. Univ. Sci. Technol. Beijing, 2004, 26(1): 26.

[10] Suito H., Inoue R. Thermodynamics on control of inclusions composition in ultra-clean steels. ISIJ Int., 1996, 36(5): 528

[11] Kimura S., Mimura T., Hoshikawa I., Ibaraki N., Chouda T. Control techniques to reduce inclusions during the manufacture of steel for tire cords. R&D Kobe Steel Eng. Rep., 2004, 54(3): 25.

[12] Wang L.F., Zhang J.M., Wang X.H., Jin Q.F. Composition control of CaO-SiO-Al₂O₃-MgO inclusion by using low basic slag for tire cord steel in laboratory. J. Univ. Sci. Technol. Beijing, 2003, 25(6): 528.

[13] Cho S.W., Suito H. Assessment of aluminum-oxygen equilibrium in liquid iron and activities in CaO-Al₂O₃-SiO₂ slags. ISIJ Int., 1994, 34(2): 177

[14] Sigworth G.K., Elliott J.F. Thermodynamics of liquid dilute iron alloys. Met. Sci. J., 1974, 8(9): 298.

[15] Ohta H., Suito H. Activities in MnO-SiO₂-Al₂O₃ slags and deoxidation equilibria of Mn and Si. Metall. Mater. Trans. B, 1996, 27(2): 263

[16] Chen J.X. Common Charts and Data Book for Steel Making, 1984, Beijing, Metallurgical Industry Press, 548.

[17] Lupis C.H.P. Chemical Thermodynamics of Materials, 1983, New York, North-Holland, 289.

[18] Jiang M., Wang X.H., Chen B., Wang W.J. Laboratory study on evolution mechanisms of non-metallic inclusions in high strength alloyed steel refined by high basicity slag. ISIJ Int., 2010, 50(1): 95

[19] Jiang M., Wang X.H., Chen B., Wang W.J. Formation of MgO-Al₂O₃ inclusions in high strength alloyed structural steel refined by CaO-SiO₂-Al₂O₃-MgO slag. ISIJ Int., 2008, 48(7): 885